Investigation of the effect of indirect pulp capping materials on dentin mineral density

Aim

To evaluate the potential of inducing mineral density changes of indirect pulp capping materials applied to demineralized dentin.

Methods

A total of 50 cavities were prepared, 5 in each tooth, in extracted ten molars without caries, impacted or semi-embedded. The cavities were scanned by microcomputed tomography (µ-CT) after creating artificial caries by microcosm method (pre-treatment). Each cavity was subjected to one of 5 different experimental conditions: control (dental wax), conventional glass ionomer cement (Fuji IX GP Extra), resin-modified calcium silicate (TheraCal LC), resin-modified calcium hydroxide (Ultra-Blend Plus), MTA (MM-MTA) and the samples were kept under intrapulpal pressure using simulated body fluid for 45 days. Then, the second µ-CT scan was performed (post-treatment), and the change in dentin mineral density was calculated. Afterward, elemental mapping was performed on the dentinal surfaces adjacent to the pulp capping agents of 5 randomly selected samples using energy dispersive X-ray spectroscopy (EDS) apparatus attached to a scanning electron microscope (SEM). The Ca/P ratio by weight was calculated. Friedman test and Wilcoxon Signed Ranks test were used to analyze the data.

Results

There was a significant increase in mineral density values of demineralized dentin after treatment for all material groups (p<0.05). Resin-modified calcium silicate had similar efficacy to MTA and conventional glass ionomer cement, but was superior to resin-modified calcium hydroxide in increasing the mineral density values of demineralized dentin.

Conclusions

Demineralized dentin tissue that is still repairable can be effectively preserved using materials with remineralization capability.

Calcium hydroxide; Calcium compounds; Silicates; Spectrometry, X-ray emission; Glass ionomer cement; X-ray microtomography