This work presents the results of a study on the incorporation of solid waste from siderurgical industry in the formulation of a clayey mass used in the production of red ceramics. The prepared masses contained the following amounts of siderurgy waste: 0, 0.5, 1.0, 1.5, 2.0, 2.5 and 3.0wt%. The results of X-ray diffraction, granulometry and Atterberg's limits are presented for the ceramic masses. Test specimens were conformed by vacuum extrusion and fired at temperatures of 850 ºC, 900 ºC, 950 ºC, 1000 ºC and 1050ºC. The physical-mechanical properties were determined as a function of firing temperature and content of siderurgy waste. The results indicate that the addition of siderurgy solid waste modify the physic-chemical characteristics of the clayey mass and the ceramic properties of the test specimens. The results suggest also that the ceramic masses containing siderurgy waste could be used in the production of red ceramic for civil construction.
siderurgy solid waste; recycling; red ceramic