THE POWDER OF Co₆₄Nb₃₀B₆ OBTAINED BY MECHANICAL ALLOYING

This work aims to synthesize the alloy Co₆₄Nb₃₀B₆ through mechanical alloying using a planetary ball mill. A disc rotation per minute and a ball/powder weight ratio of 300 rpm and 10:1 were used, with a milled time of 10 h, respectively. The characterization of the Co₆₄Nb₃₀B₆ alloy was performed by X-ray diffraction (XRD), examined by scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDS), thermoanalytical techniques (TGA/DTA), vibrating sample magnetometer (VSM) and confirmed by Braunauer, Emmet e Teller (BET) method type IV isotherms with a hysteresis loop for mesoporous materials. The results indicated that the evolution of the amorphous phase in the Co₆₄Nb₃₀B₆ composition through the mechanical alloying process exhibited good soft magnetic properties with the addition of the metalloid element B and its excellent unique ferromagnetic properties. Through thermoanalytical analysis (TGA/DTA), it was shown that at higher temperatures, Co and Nb ions are oxidized by the environment and, therefore, the mass can be slightly increased to 14.9% and a probable contribution of boron in evolution stability thermal and magnetic in the amorphous phase, respectively. This suggests that the newly developed high-performance amorphous alloy Co₆₄Nb₃₀B₆ has great application potential.

Keywords:
amorphous alloy Co₆₄Nb₃₀B₆; mechanical alloying; characterization