AISI 316 austenitic stainless steel samples have been nitrided by cathodic cage technique in same treatment conditions: pressure 250 Pa, temperature 500 ºC and nitriding mixtures 80%N2/H2. The variance is limited just to process duration, from 1 to 5 hours. In this work the objective is to observe the increase of nitrided layer. It has been seen that there was layer formation to all times of nitriding. They are confirmed through optical microscopy and microhardness analysis. The X-ray difratogram presents similar phases proving that is possible obtain nitrided layer using cathodic cage technique even to short during treatment.
plasma nitriding; austenitica stainless steel; phase S; cathodic cage