Alumina ceramics obtained by chemical synthesis using conventional and microwave sintering

Cerâmicas de alumina obtidas por síntese química e sinterizadas em forno convencional e por microondas

Abstracts

It is well known that the heating mechanism and powder precursor define the microstructural characteristics of ceramics. Especially abnormal grain growth of pure alumina ceramics developed during conventional sintering method suggests that this material is a potential candidate to be treated in microwave sintering process. Alumina ceramics produced with commercial (A1K) and chemically synthesized powders were sintered in conventional and microwave furnaces. Two methods were employed to prepare the chemically synthesized nanosized powders: Pechini method and emulsification with oleic acid. The microwave sintered samples were characterized by apparent density and scanning electron microscopy and compared with the samples sintered in a conventional furnace. Alumina ceramics sintered in the microwave furnace had fine grained microstructure, not related with the starting powders. This characteristic was achieved in a sintering time shorter than those produced in the conventional furnace. However, satisfactory densification was observed only to A1K ceramics (3.95 g/cm³) sintered during one hour in microwave furnace.

synthesis; sintering; microwave; alumina

É conhecido que os mecanismos de aquecimento e os pós precursores definem as características microestruturais das cerâmicas. Especialmente, o crescimento anormal de cerâmicas de alumina pura desenvolvidos durante o método de sinterização convencional sugere que esse material é um candidato potencial para ser tratado no processo de sinterização em microondas. Cerâmicas de alumina produzidas com pós comercial (A1K) e quimicamente sintetizado foram sinterizados em fornos convencional e por microondas. Dois métodos foram empregados para preparar quimicamente os pós nanométricos: método de Pechini e por emulsificação em ácido oleico. As cerâmicas sinterizadas em microondas foram caracterizadas por densidade aparente e por microscopia eletrônica de varredura, e comparados com as amostras sinterizadas em forno convencional. Aluminas sinterizadas em microondas apresentaram uma granulometria fina, não relacionada com os pós precursores. Essa característica foi obtida para um tempo de queima menor do que o obtido em fornos resistivos. Contudo, uma alta densificação foi observada apenas em cerâmicas A1K (3,95 g/cm³) sinterizadas durante uma hora em microondas.

síntese; sinterização; microondas; alumina

Alumina ceramics obtained by chemical synthesis using conventional and microwave sintering

Cerâmicas de alumina obtidas por síntese química e sinterizadas em forno convencional e por microondas

D. Thomazini^I; M. V. Gelfuso^I; A. S. A. Chinelatto^II; A. L. Chinelatto^II; F. K. Sanson^II; F. Teixeira Neto^III

^IItajubá Federal University, Av. BPS 1303, Itajubá, MG, Brazil. [e-mail], [e-mail]

^IIPonta Grossa State University, Av. General Carlos Cavalcanti 4748, Ponta Grossa, PR, Brazil. [e-mail], [e-mail]

^IIIFortaleza University, Av. Washington Soares 1321, Fortaleza, CE, Brazil. [e-mail]

ABSTRACT

It is well known that the heating mechanism and powder precursor define the microstructural characteristics of ceramics. Especially abnormal grain growth of pure alumina ceramics developed during conventional sintering method suggests that this material is a potential candidate to be treated in microwave sintering process. Alumina ceramics produced with commercial (A1K) and chemically synthesized powders were sintered in conventional and microwave furnaces. Two methods were employed to prepare the chemically synthesized nanosized powders: Pechini method and emulsification with oleic acid. The microwave sintered samples were characterized by apparent density and scanning electron microscopy and compared with the samples sintered in a conventional furnace. Alumina ceramics sintered in the microwave furnace had fine grained microstructure, not related with the starting powders. This characteristic was achieved in a sintering time shorter than those produced in the conventional furnace. However, satisfactory densification was observed only to A1K ceramics (3.95 g/cm³) sintered during one hour in microwave furnace.

Keywords: synthesis, sintering, microwave, alumina.

RESUMO

É conhecido que os mecanismos de aquecimento e os pós precursores definem as características microestruturais das cerâmicas. Especialmente, o crescimento anormal de cerâmicas de alumina pura desenvolvidos durante o método de sinterização convencional sugere que esse material é um candidato potencial para ser tratado no processo de sinterização em microondas. Cerâmicas de alumina produzidas com pós comercial (A1K) e quimicamente sintetizado foram sinterizados em fornos convencional e por microondas. Dois métodos foram empregados para preparar quimicamente os pós nanométricos: método de Pechini e por emulsificação em ácido oleico. As cerâmicas sinterizadas em microondas foram caracterizadas por densidade aparente e por microscopia eletrônica de varredura, e comparados com as amostras sinterizadas em forno convencional. Aluminas sinterizadas em microondas apresentaram uma granulometria fina, não relacionada com os pós precursores. Essa característica foi obtida para um tempo de queima menor do que o obtido em fornos resistivos. Contudo, uma alta densificação foi observada apenas em cerâmicas A1K (3,95 g/cm³) sinterizadas durante uma hora em microondas.

Palavras-chave: síntese, sinterização, microondas, alumina.

INTRODUCTION

Microwave sintering (µS) is usually described as a process that can promote densification in ceramics at a very high heating rate of about 400 ºC/min [1, 2], at a lower temperature than that employed in the conventional sintering process (cS) [3-6]. High density materials can be obtained by microwave and conventional heating methods [7-9], presenting significant differences in physical properties such as density, mechanical strength and grain size distribution.

Three essential mechanisms of heat transport can act during the conventional heating process: radiation, convection and conduction. In the case of microwave heating, the energy of the electromagnetic radiation is converted directly into thermal energy by reorientation of dipoles in the material. The dielectric loss or loss tangent (tanδ = ε"/ε') indicates the tendency of the material to convert absorbed energy into heat. This type of heating is more efficient, since, unlike heat transport by convection or conduction, it involves no losses. The direct interaction between microwave irradiation and the material causes volumetric heating of the sample, thus eliminating the problem of thermal gradients inherent in conventional firing [3, 10].

The structural state of both grain boundaries and surfaces of ultrafine ceramic powders is close to the amorphous state [11]. If the influence of reactivity or specific surface area of the materials in a microwave field can be experimentally verified, the effect of grain boundary on the microwave sintering enhancement would be confirmed. Studies involving powders obtained by chemical routes could be very interesting to analyze this propose.

Moreover, the chemical synthesis routes play a crucial role in preparing the final product and are better than traditional methods for the production of fine-grained mixed oxide powders, having good physical properties. Fine powders prepared involve shorter diffusion distances study the sintering behavior of a commercial alumina and alumina chemically synthesized by the Pechini method and 2400 by emulsification in oleic acid, using the conventional and microwave sintering processes. The sample densities and microstructures were then compared and analyzed.

EXPERIMENTAL PROCEDURE

Preparation of alumina powders by chemical synthesis

Aluminum nitrate salt (Al(NO₃)₃.9H₂O) was used for the chemical synthesis of the alumina powders. In the Pechini method (PM), the salt was dissolved in an aqueous solution of citric acid in the proportion of 3:1, under constant agitation and heating. Ethylene glycol was then added in a 40:60 (citric acid: ethylene glycol) ratio, resulting in a PM solution.

For the synthesis with emulsification in oleic acid (OA), aluminum hydroxide was precipitated from the PM solution, using ammonium hydroxide. After filtering the precipitate, oleic acid was added in a ratio of 40:60 to the dry mass of aluminum hydroxide. The precipitate and oleic acid were mixed for 30 min in a rotary mixer, at a rotation of 800 to 1000 rpm, resulting in the OA solution.

The resins obtained by the two methods were calcined at 500 ºC for 1.5 h and then at temperatures ranging from 900 to 1200 ºC. In both cases, the transformation to α-Al₂O₃ occurred in the powder treated at 1100 ºC during 120 min, as indicated by the X-ray diffraction (XRD) analysis presented in Figs. 1a and 1b, respectively for OA and PM powders. Fig. 1 shows some spurious peaks related the presence of θ-alumina phase, considered a transition phase, which turns into α-Al₂O₃ with increasing calcination temperature. The mean particles sizes, measured by half-width peak in the XRD of the OA and PM calcined powders were 31±4 nm and 38±6 nm, respectively.

The powder density values measured by helium picnometry were 3.68 and 3.96 g/cm³ for OA and PM powders, respectively. The lower density value for OA powder indicates the presence of θ-Al₂O₃, in agreement with the XRD analysis.

Ceramics processing and characterization

The samples were uniaxially pressed under 40 MPa into cylindrical compacts (9.5 mm diameter and 3 mm thickness), after which they were isostatically cold pressed under 150 MPa.

The samples obtained by the conventional sintering process, cS ceramics, were sintered in an electrical furnace at 1650 ºC for 5, 30, 60 min, at 5 ºC/min; on the other hand the µS ceramics were sintered at 1650 ºC at 400 ºC/min for different times. The microwave furnace used in this work was modified from a domestic model, with a nominal power of 1450 W and 2.45 GHz operating frequency, SiC as microwave susceptor and a chamber size of about 8000 cm³. The high-grade Al₂O₃ (99.85% purity, Alcoa® A1000SG), consisting of fine particles averaging 1.05±0.15 µm diameter, were used to produced commercial alumina samples (A1K) which were compared with chemical powder ceramics. The particle size of the powder was measured in a particle size distribution equipment (Horiba Capa-700).

The density of the ceramics was determined after sintering, based on their mass and geometric dimensions. The microwave effect on densification of alumina was evaluated by the enhancement in the sintered density achieved by microwave and conventional processes.

The fracture surfaces were examined by scanning electron microscopy (SEM, Shimadzu SSX-550) to analyze the grain shape, size distribution and porosity. The grain size of the ceramic bodies was measured with a CAD software.

RESULTS AND DISCUSSION

Fig. 2 presents the density of A1K, PM and OA ceramics produced by cS method as a function of soaking time. Note that after 2 h at 1650 ºC the density of the A1K samples was about 99.2%TD. However, the PM and OA samples did not reach density values higher than 76%TD, probably due to the formation of aggregates, which is very common occurrence in chemically produced powders.

Fig. 3 shows the effect of soaking time on the densification of the samples of commercial alumina A1000 (A1K), Pechini method and emulsification in oleic acid in the µS process. As can be seen, the densification of the commercial alumina samples in the microwave field was higher at the same temperature than that obtained by conventional process. A1K samples presented high densification in 60 min (3.95 g/cm³), while the PM and OA ceramics presented no significant densification. However, their density values were slightly lower than in PM and OA cS samples, suggesting that the densification process is favored in microwave heating. Previous studies [14] showed that ceramics produced with these powders did not present density values exceeding 76%TD, despite being composed of nanometric particles. These nanometric particles produce aggregates that hinder compaction under pressure and create high porosity. However, an interesting finding is that the densities of the PM (3.0 g/cm³) and OA (2.6 g/cm³) ceramics obtained by the µS and cS processes were almost the same, although the µS process took less time. In fact, the coupling efficiency of microwaves directly to the material is the primary advantage of microwave processing as compared to traditional routes. The volumetric heating ability of microwaves allows for more rapid and uniform heating, resulting in decreased processing time.

Fig. 4 presents the fracture SEM micrographs of the A1K, PM and OA ceramics produced by the cS and µS methods fired at 120 min. Note the more fine-grained microstructure of the µS samples compared to that of the cS samples, resulting from the faster heating rate applied in microwave sintering, which favors boundary diffusion and grain growth [15]. The grains of the sintered compacts in conventional treatment grow discontinuously, and the grains of the microwave sintered compacts homogeneously.

The lower green density of the µS samples, 32.6% of TD for the OA ceramics and 43.6% of TD for the PM ceramics in comparison with A1K ceramics (∼50% of TD) illustrates the difficulty involved in the conformation of these materials. The low powder compaction can be attributed to the use of nanosized powder (particle size ∼ 30 nm) and correspondingly smaller pore size in the green body. Critical pore size is achieved at a lower density than in the case of the A1K powder with higher particle sizes; thus, the higher values for the green compacts density of A1K previously indicate the higher sintered density for those ceramics.

Cheng et al. [16] found the same dificult when they tryied to densify nanometric alumina particles, achieving green bodies with ∼ 52% T.D. when sintering nanometric alumina ceramics using microwave energy. The alumina powders were doped with 0.05wt.% of MgO and fired in H₂ atmosphere. These authors demonstrated that the addition of MgO was fundamental in improving the sintering process of nanometric powders. In addition, Agrawal [10]] observed that ceramics with a green density higher than 45%TD is more favorable for µS sintering than for cS.

Table I lists the values of the measured grain sizes in the sintered ceramics presented in Fig. 4. As can be seen, the µS values are lower than those of the cS samples. In addition, the fi nal grain size was similar for both ceramics, PM and OA. The control of grain size and grain growth is very important for producing advanced ceramics because abnormal grain growth and grain size infl uence the characteristics of the ceramic product [17]. Because direct heat transfer in microwave irradiation is more effi cient than in conventional irradiation heating, the microwave sintering process was found to occur mainly by grain boundary diffusion, as indicated by the low neck ratios [18], promoting densifi cation without grain growth. Chen and Wang [19] studied two-stage sintering of alumina with submicrometer grain size and reported the success for densification of a nanometer sized yttria powder without the final stage of grain growth. They postulated that at a certain temperature range (called "kinetic window") densification is already in operation, while the grain boundary motion is not yet activated. The cS samples probably reached this "kinectic window" while PM and OA ceramics did not due to the initial nanosized particle.

CONCLUSIONS

The samples obtained by microwave sintering presented a finer microstructure than those produced by conventional sintering. This may have resulted from the high heating rate, which favors the sintering process by boundary diffusion. The commercial alumina reaches densification (99.2%TD) in less time by the microwave sintering process than in the conventional one due to the direct transfer of microwave energy to the samples, which accelerated the densification process. The ceramics produced with chemically synthesized alumina powders did not densify but density values reached results slightly close the ones obtained in the conventional furnace, even being heated for less time. This is due to their low values of green density, which hindered the densification process.

(Rec. 17/03/2010, Rev. 05/04/2010, Ac. 08/05/2010)

• [1] D. Thomazini, M. V. Gelfuso, F. Teixeira Neto, Proc. 49ş Cong. Bras. Ceram., Águas de S. Pedro, SP, Brazil (2005).
• [2] M. V. Gelfuso, F. Teixeira Neto, D. Thomazini, Cerâmica 53, 327 (2007) 309.
• [3] D. D. Upadhyaya, J. Mater. Sci. 36 (2001) 4707.
• [4] W. H. Sutton, J. Am. Ceram. Soc. 68 (1989) 376.
• [5] D. E. Clarck, W. H. Sutton, Ann. Rev. Mater. Sci. 26 (1996) 299.
• [6] R. R. Menezes, P. M. Souto, R. H. G. A. Kiminami, Cerâmica 53, 327 (2007) 218.
• [7] C. Saltiel, Z. Fathi, W. H. Sutton, Mechanical Eng. 26 (1995) 102.
• [8] A. Birnboim, D. Gershon, J. Calame, A. Birman, Y. Carmel, J. Rodgers, B. Levush, Yu. V. Bykov, A. G. Eremeev, V. V. Holoptsev, V. E. Semenov, D. Dadon, P. L. Martin, M. Rosen, R. Hutcheon, J. Am. Ceram. Soc. 81 (1998) 1493.
• [9] M. V. Gelfuso, F. Teixeira Neto, D. Thomazini, Proc. 11^th Int. Meeting Ferroelectricity, Iguassu Falls, PR, Brazil (2005).
• [10] D. Agrawal, J. Cheng, R. Peelamedu, R. Roy, Current Adv. Mater. Processes 17 (2004) 670.
• [11] Y. Fang, J. Cheng, D. Agrawal, Mater. Lett. 58 (2004) 498.
• [12] P. Bowen, C. Carry, Powder Technol. 128 (2002) 248.
• [13] R. E. P. Salem, A. L. Chinelatto, A. S. A. Chinelatto, Mater. Sci. Forum 591 (2008) 649-653.
• [14] A. S. A. Chinelatto, Proc. 50ş Cong. Bras. Ceram., S. Paulo, SP, Brazil (2006).
• [15] D. Agrawal, Y. Fang, D. M. Roy, R. Roy, Microwave Proc. Mater. III 269 (1992) 231.
• [16] J. Cheng, D. Agrawal, Y. Zhang, R. Roy, Mater. Lett. 56 (2002) 587.
• [17] Y. Hotta, T. Banno, S. Sano, A. Tsuzuki, K. Oda, J. Ceram. Soc. Japan 108 (2000) 103.
• [18] M. F. Ashby, Acta Metal. 22 (1974) 275.
• [19] W. Chen, X. H. Wang, Nature 404 (2000) 168.

Publication Dates

• Publication in this collection
  10 May 2011
• Date of issue
  Mar 2011

History

• Received
  17 Mar 2010
• Reviewed
  05 Apr 2010
• Accepted
  08 May 2010