Abstract
Steelmaking slag and residues from granite cuttings are industrial wastes with considerable production, however limited applications. This work studied an inertization and recovery process of such wastes as raw materials into production of rock wool (i.e. a thermo-acoustic insulator with growing market). Several batches were produced aiming the chemical proprieties of a currently marketed rock wool. Mixtures were casted at temperatures of 1400-1500 °C, then quenched in water and also poured into a Herty Viscosimeter. Produced materials with thickness smaller than 500µm were characterized by chemical analyses, XRD, SEM, EDS and DTA. ThermoCalc software was used to simulate the cooling curves of rock wools. Results showed that incorporation of wastes does not affect the main qualities of rock wool, the thermal insulation and prevention of fire spread. Raw material batches of rock wools may assimilate up to 66% of granite waste, or 53% steelmaking slag, or 70% combining both materials.
steelmaking slag; granite waste; rock wool; thermal insulator
1 Introduction
Recycling of solid wastes has been growing steadily in recent years, along with
rising industrial production. The waste generation increase presents a serious
problem of environment and costly disposal. Recovery of industrial wastes into
useful subproducts might be economically viable, and it is desirable since the
disposal involves expensive transportation, as well as the monitoring of deposit
areas11. Zhuo C, Alves JO, Tenório JAS and Levendis YA. Synthesis of
carbon nanomaterials through up-cycling agricultural and municipal solid wastes.
Industrial & Engineering Chemistry Research. 2012; 51(7):2922-2930.
http://dx.doi.org/10.1021/ie202711h.
http://dx.doi.org/10.1021/ie202711h...
,22. Alves JO, Zhuo C, Levendis YA and Tenório JAS. Microstructural
Analysis of Carbon Nanomaterials Produced from Pyrolysis/Combustion of
Styrene-Butadiene-Rubber (SBR). Materials Research. 2011; 14(4):499-504.
http://dx.doi.org/10.1590/S1516-14392011005000078.
http://dx.doi.org/10.1590/S1516-14392011...
. Vitrification process has been
widely used as final destination for hazardous materials due to the inertization
capability of organic toxics, heavy metals, fly ashes and nuclear wastes33. Chou I-C, Kuo Y-M, Lin C, Wang J-W, Wang C-T and Chang-Chien G-P.
Electroplating sludge metal recovering with vitrification using mineral powder
additive. Resources, Conservation and Recycling. 2012; 58:45-49.
http://dx.doi.org/10.1016/j.resconrec.2011.10.006.
http://dx.doi.org/10.1016/j.resconrec.20...
4. Cimdins R, Rozenstrauha I, Berzina L, Bossert J and Bücker M.
Glassceramics obtained from industrial waste. Resources, Conservation and
Recycling. 2000; 29(4):285-290.
http://dx.doi.org/10.1016/S0921-3449(00)00053-7.
http://dx.doi.org/10.1016/S0921-3449(00)...
-55. Quijorna N, Coz A, Andres A and Cheeseman C. Recycling of Waelz
slag and waste foundry sand in red clay bricks. Resources, Conservation and
Recycling. 2012; 65:1-10.
http://dx.doi.org/10.1016/j.resconrec.2012.05.004.
http://dx.doi.org/10.1016/j.resconrec.20...
.
The world production of crude steel in 2010 reached about 1.4 billion tons,
registering a new record of production. Considering that for each ton of steel
produced are generated 150 kg of steelmaking slag, approximately 210 million tons of
such waste were produced in 201066. World Steel Association. Crude steel statistics. 2010. Available
from: <http://www.worldsteel.org>. Access in: 25/05/2011.,77. Wang Q, Yan P and Feng J. A discussion on improving hydration
activity of steel slag by altering its mineral compositions. Journal of
Hazardous Materials. 2011; 186(2-3):1070-1075.
http://dx.doi.org/10.1016/j.jhazmat.2010.11.109. PMid:21168967
http://dx.doi.org/10.1016/j.jhazmat.2010...
. The production of steel from electric arc furnaces has
expanded due to the higher availability of steel scrap, which is the main component
of the production charge88. Sebag MG, Korzenowski C, Bernardes AM and Vilela AC. Evaluation
of environmental compatibility of EAFD using different leaching standards.
Journal of Hazardous Materials. 2009; 166(2-3):670-675.
http://dx.doi.org/10.1016/j.jhazmat.2008.11.125. PMid:19223119
http://dx.doi.org/10.1016/j.jhazmat.2008...
.
Steelmaking slag is the result of an aggregation of several elements which the
presence is not important on steel making process. Among different wastes from the
steel process, steelmaking slag represents one of most hazardous since it may
contains heavy metals such as chromium, manganese and iron99. Motz H and Geiseler J. Products of steel slags an opportunity to
save natural resources. Waste Management. 2001; 21(3):285-293.
http://dx.doi.org/10.1016/S0956-053X(00)00102-1. PMid:11280521
http://dx.doi.org/10.1016/S0956-053X(00)...
. About 20% of the world’s production of
steelmaking slag is not reused due the characteristics of this waste, mainly the
expansibility problem. A large portion of industrial parks are occupied for this
waste, which raises the disposal costs. Therefore, recycling and reusing slag is a
technical, economic and environmental solution for steel companies77. Wang Q, Yan P and Feng J. A discussion on improving hydration
activity of steel slag by altering its mineral compositions. Journal of
Hazardous Materials. 2011; 186(2-3):1070-1075.
http://dx.doi.org/10.1016/j.jhazmat.2010.11.109. PMid:21168967
http://dx.doi.org/10.1016/j.jhazmat.2010...
,1010. Pioro LS and Pioro IL. Reprocessing of metallurgical slag into
materials for the building industry. Waste Management. 2004; 24(4):371-379.
http://dx.doi.org/10.1016/S0956-053X(03)00071-0. PMid:15081065
http://dx.doi.org/10.1016/S0956-053X(03)...
.
Another industrial sector with high production of waste is the industry of granite
cutting. Approximately 30% of powdered wastes are generated during the granite
extraction process, specifically on the rock cutting. Such values represents that a
single company may produce up to 35 tons of this residue per month. The granite
waste need be appropriately managed, since the discharge in rivers, lakes or
watersheds can cause siltation. Also, this residue may cause serious human health
problems, such as silicosis. Currently, the granite waste is mainly used in civil
construction to produce materials in the form of mortar, bricks and tiles1111. Moreira JMS, Freire MN and Holanda JNF. Utilization of granite
sawing waste from Espírito Santo state in red ceramic. Cerâmica. 2004;
49(312):262-267.,1212. Silva MA, Paes HR Jr and Holanda JNF. Reuse of ornamental
rock-cutting waste in aluminous porcelain. Journal of Environmental Management.
2011; 92(3):936-940. http://dx.doi.org/10.1016/j.jenvman.2010.10.060.
PMid:21074931
http://dx.doi.org/10.1016/j.jenvman.2010...
. However, new applications for this waste are
necessary due to the high produced volumes and the average growth of world
production estimated at 6% per year1313. Rodrigues GF, Alves JO, Tenório JAS and Espinosa DCR. Study of
wastes from ornamental rocks for production of vitreous materials. Tecnologica
em Metalurgia, Materiais e Mineração. 2011; 8(3):203-207.
http://dx.doi.org/10.4322/tmm.2011.032.
http://dx.doi.org/10.4322/tmm.2011.032...
,1414. Menezes RR, Ferreira HS, Neves GA and Ferreira HC. The use of
granite wastes as ceramic raw materials. Cerâmica. 2002;
48(306):92-101..
Rock wools are man-made mineral fibers (MMMF) fabricated with the melting of basalt
or other natural rocks at temperatures above 1400 °C1515. Trdič F, Sirok B, Bullen PR and Philpott DR. Monitoring mineral
wool production using real-time machine vision. J. Real-Time Imaging. 1999;
5(2):125-140. http://dx.doi.org/10.1016/S1077-2014(99)80010-2.
http://dx.doi.org/10.1016/S1077-2014(99)...
,1616. Thermal Insulation Manufacturers’ Association - TIMA. Man-made
vitreous fibers: nomenclature, chemical and physical properties. Stamford:
Owens-Corning Fiberglass; 1991. IPCS-WHO.. The thermo-acoustic characteristics of fire
resistance, and not rendering toxic smoke ensure to rock wools a broad consumer
market in the industries of construction, automotive, and electric-electronics,
among others. Rock wools are usually produced with melting spinning process, in
which a thin stream of material is dripped onto a wheel internally cooled with water
or liquid nitrogen that causes a fast solidification1717. Ueda M, Murase F, Takahashi F and Matsumoto T. An optical system
for measuring the eccentricity of glass wool pipe - for industrial use. Optics
and Lasers in Engineering. 1999; 31(6):493-501.
http://dx.doi.org/10.1016/S0143-8166(99)00030-5.
http://dx.doi.org/10.1016/S0143-8166(99)...
,1818. Marabini AM, Plescia P, Maccari D, Burragato F and Pelino M New
materials from industrial and mining wastes: glass-ceramics and glass- and
rock-wool fibre. International Journal of Mineral Processing. 1998;
53(1-2):121-134.
http://dx.doi.org/10.1016/S0301-7516(97)00062-8.
http://dx.doi.org/10.1016/S0301-7516(97)...
. This study aims to recovery steelmaking slag and
granite cutting waste as feedstock of rock wools by the replacement of traditional
raw materials, reducing the costs and impact of disposal of such residues. In
addition, the use of recycled materials decreases extraction of non-renewable
resources necessary to produce the rock wool.
2 Experimental Methods
2.1 Materials
The raw materials used in this study were steelmaking slag from an Electric Arc Furnace (EAF), granite cutting residue from an industry on Espírito Santo State - Brazil, and chemical reagents (i.e. silica, alumina, magnesium oxide, iron oxide, calcium carbonate, and borax). Steelmaking slag was received in blocks, thus the material was cracked into pieces smaller than 4.76 mm. Granite waste was received in a fine powder form, thus these were dried at 90 °C for 24 hours before use.
2.2 Sample preparation
Several mixtures were prepared using the residues and chemical additives. The batches were based on the chemical composition of a currently marketed rock wool provided by a thermo-acoustic company, and the range of composition recommended in the literature. Three cases were prepared: a) using only granite waste; b) using only steelmaking slag; and c) using both residues. The mixtures were homogenized during 10 minutes in a laboratory scale agitator.
The main objective of the work was maximize the amount of residues in the batches, however some tests presented melting points above the furnace capacity or insufficient fluidity to allow pouring, thus these materials were discarded from the investigation. In this aspect, the characterization work was performed in the materials from batches with efficient and superior incorporation of the residues. The mixing compositions of such batches were:
-
a
Using only granite waste - 66% granite waste and 34% chemical reagents (22.7% calcium carbonate, 6.6% magnesium oxide and 4.7% iron oxide);
-
b
Using only steelmaking slag - 53% steelmaking slag and 47% chemical reagents (30.3% silica, 6.1% alumina, 6.1% magnesium oxide and 4.5% Borax);
-
c
Using both residues: 46% granite waste, 23% steelmaking slag and 31% chemical reagents (21.9% calcium carbonate, 6.4% magnesium oxide and 2.7% iron oxide).
The batches were heated in a laboratory-scale electric furnace with no controlled
gas atmosphere during 50 min. The equipment operates open, the system pressure
is constant, and a variation on oxygen pressure does not affect the equilibrium
of phases. Melted samples were quenched in a water bath at room temperature in
order to rapidly cool the materials, which is essential to produce vitreous
materials. Three temperatures were used to cast the materials: 1400, 1450 and
1500 ºC, such range was based on the method of rock wool production cited in the
literature1515. Trdič F, Sirok B, Bullen PR and Philpott DR. Monitoring mineral
wool production using real-time machine vision. J. Real-Time Imaging. 1999;
5(2):125-140. http://dx.doi.org/10.1016/S1077-2014(99)80010-2.
http://dx.doi.org/10.1016/S1077-2014(99)...
,1616. Thermal Insulation Manufacturers’ Association - TIMA. Man-made
vitreous fibers: nomenclature, chemical and physical properties. Stamford:
Owens-Corning Fiberglass; 1991. IPCS-WHO.. Temperatures of materials during the process were
measured using an optical pyrometer. After the cooling process, samples of
materials were collected and dried in an oven at 90 °C for 24 hours.
2.3 Sample characterization
Samples of produced materials in fiber forms and thickness smaller than 500µm were applied in the characterization processes. The nominal variation on the temperature not significantly affected the results of the produced materials, therefore only the characterization results of samples poured at 1450 °C were selected to present in this work.
Produced materials were characterized by chemical analysis, X-ray diffraction (XRD) and Differential Thermal Analysis (DTA). Scanning Electronic Microscopy (SEM) was used to verify formation of secondary phases in the produced materials, and Energy Dispersive Spectroscopy (EDS) was applied to establish the phase compositions. XRD analysis was carried out using a Philips MPD 1880 40 mA Diffractometer adjusted with copper Kα radiation (λ = 1.5418 Å) and voltage of 40 kV. The DTA was performed in a Netzsch 409C equipment with alumina crucibles, air atmosphere, and heating rate of 15 °C/min. SEM/EDS analyses were conducted with a Philips XL-30 instrument using 3 kV voltage and working distance of 8.2 mm.
The Herty Viscosity Test is frequently used in industry to provide quick and
approximate values for comparative purposes. A Herty viscometer is composed of
two steel blocks with a groove in the middle interface in which the melted
material is poured. Thus, the distance travelled by the material before
solidification is measured, and an approximation of viscosity value is
obtained1919. Brooks RF, Dinsdale AT and Quested PN. The measurement of
viscosity of alloys -a review of methods, data and models. Measurement Science
& Technology. 2005; 16(2):354-362.
http://dx.doi.org/10.1088/0957-0233/16/2/005.
http://dx.doi.org/10.1088/0957-0233/16/2...
,2020. Keene BJ. Slag atlas. 2nd ed. Düsseldorf: Verlag Stahleisen
GmbH; 1995.. A laboratory-scale Herty viscosimeter was applied
in this work to measure variations on viscosity according to different batches
compositions and casting temperatures.
ThermoCalc software version “n” running SLAG3 databases was used to perform thermodynamic and phase diagram calculations for multi-component systems of practical importance. In this work, the numerical code was used to simulate the cooling curves of an industrial rock wool and of the produced materials in order to compare the primary solid phases. Chemical compositions of the materials, previously determined, were used for the ThermoCalc simulations.
3 Results and Discussion
3.1 Chemical analysis of wastes
Results of the chemical analysis of steelmaking slag (see Table 1) shown that the main component of this residue is
calcium oxide (46.9 wt. %). The recovery of steelmaking slag has restricted
applications due to the volume instability, in which the main cause is the
phenomenon of hydration of free lime, although hydration of free magnesia may
also contribute77. Wang Q, Yan P and Feng J. A discussion on improving hydration
activity of steel slag by altering its mineral compositions. Journal of
Hazardous Materials. 2011; 186(2-3):1070-1075.
http://dx.doi.org/10.1016/j.jhazmat.2010.11.109. PMid:21168967
http://dx.doi.org/10.1016/j.jhazmat.2010...
,2121. Wang G, Wang Y and Gao Z. Use of steel slag as a granular
material: volume expansion prediction and usability criteria. Journal of
Hazardous Materials. 2010; 184(1-3):555-560.
http://dx.doi.org/10.1016/j.jhazmat.2010.08.071. PMid:20843599
http://dx.doi.org/10.1016/j.jhazmat.2010...
. The volume instability can be solved by
submitting the steelmaking slag to a vitrification process2222. Juckes LM. The volume stability of modern steelmaking slags.
Mineral Processing and Extractive Metallurgy. 2003; 112(3):177-197.
http://dx.doi.org/10.1179/037195503225003708.
http://dx.doi.org/10.1179/03719550322500...
.
Table 1 also provides the chemical analysis of the waste from granite cuttings. The main components of this residue are silica and alumina, together such oxides are responsible for almost 86% of the chemical composition. Therefore, granite waste was used as a source of these components in the production of vitreous materials.
3.2 Physical characteristics of formed materials
Produced materials showed proprieties similar to glass: translucent, fragile and brittle at room temperature. The materials displayed a green color, which is reasonably due to the content of Fe2O3 (7.6-11.1% by wt.). Different sizes and formats of materials were produced: pieces about 10 mm, fibres with thickness about 500 µm, and thin powder.
3.3 Chemical analysis of formed materials
Table 2 provides the results of the
chemical analyses of the rock wools produced in this study, sorted by each
residue. This table also shows the chemical analyses of an industrial rock wool
and the chemical composition range of rock wools cited in the literature1616. Thermal Insulation Manufacturers’ Association - TIMA. Man-made
vitreous fibers: nomenclature, chemical and physical properties. Stamford:
Owens-Corning Fiberglass; 1991. IPCS-WHO.,2323. Buck RL. Man-made vitreous fibers. Norfolk: U.S. Navy
Environmental Health Center; 1997. Technical Manual NEHC-TM6290.91-1, Rev.
A.
24. Liddell D and Miller K. Mineral fibers and health. Boca Raton:
CRC Publishers; 1991.-2525. Luoto K, Holopainen M, Kangas J, Kalliokoski P and Savolainen K.
Dissolution of short and long rockwool and glasswool fibers by macrophages in
flowthrough cell culture. Environmental Research. 1998; 78(1):25-37.
http://dx.doi.org/10.1006/enrs.1997.3825. PMid:9630442
http://dx.doi.org/10.1006/enrs.1997.3825...
.
Comparison of chemical compositions of rock wool samples: Industrial wool, literature range and produced materials sorted by each applied residue (in wt. %).
Produced materials showed high silica content (43.2-47.7% by wt.), which is the most common glass forming oxide. Responsible for about 30% of the chemical composition of produced materials, CaO, MgO, Na2O, K2O are usual glass modifiers that have the function of increase the fluidity and reduce the melting temperature. Alumina, Fe2O3, MnO2 and TiO2 are intermediary components that provide specific characteristics in rock wools, such as thermal resistance and chemical stability1616. Thermal Insulation Manufacturers’ Association - TIMA. Man-made vitreous fibers: nomenclature, chemical and physical properties. Stamford: Owens-Corning Fiberglass; 1991. IPCS-WHO.,2626. Bansal NP and Doremus RH. Handbook of glass properties. London: Academic Press; 1986..
A comparison of the values described in Table 2 shown that materials produced using only steelmaking slag or with both wastes are composed of similar major elements that industrial rock wool, and also in accordance with the chemical composition range of rock wools mentioned in the literature. Material produced only with the granite waste contains the major elements according to the reference values, with the exception of a small discrepancy in alumina content (14.2 wt. %), which is difficult to control due to the high value found in the granite waste composition (19.3 wt. %).
3.4 Cooling curves of materials
The cooling curve is an important factor on studies of vitreous materials since the cooling condition directly affects the structure of formed material. Simulation results using ThermoCalc software are shown in Figure 1, in which the curves express number of moles of a phase present in the system (NP) by the temperature.
Cooling curves of rock wools fabricated using only granite waste (a), only steelmaking slag (b), both residues (c), and from a industrial sample (d).
Cooling curve based on the chemical composition of industrial rock wool is shown in Figure 1d. The first solid phase displayed is the spinel (MgAl2O4) formed approximately at 1220 °C, and the second solid phase is the calcium silicate CaO⋅SiO2 formed around at 1210 °C.
Simulations using chemical compositions of the formed materials are shown in Figures 1a, 1b and 1c. The produced rock wools showed behaviour similar to the industrial rock wool, in which all samples presented spinel as the first phase and calcium silicate as the second phase. Spinel phases were formed at 1210-1290 °C, and calcium silicate phases were formed at 1190-1220 °C.
Phase’s diagrams of rock wools also showed the formation of the phases CaO-MgO-SiO2, Fe2O3, MgO-SiO2 and SiO2-Al2O3 on a temperature range of 1140-1180 °C. Such phases were not highlighted in Figure 1 in order to emphasise the temperatures of primary phases, which are directly related with the formation of vitreous materials.
ThermoCalc simulations also indicated that raw materials based on wastes (Figures 1a, 1b and 1c) and the traditional raw materials (Figure 1d) have approximate melting points, around 1200 °C. Therefore, the use of steelmaking slag and granite waste as raw material should not affect the energy efficiency of the rock wool industrial process.
3.5 X-ray diffraction analysis of materials
The X-ray diffraction spectra of the produced materials are shown in Figure 2. Rock wool is an amorphous material, therefore it should present a homogeneous curve without notable crystalline peaks. The X-ray diffraction spectra of a current marketed rock wool is shown in Figure 2d, which confirms the homogeneous curve and serves as reference to compare with the produced materials.
X-ray diffraction spectra of rock wools fabricated using only granite waste (a), only steelmaking slag (b), both residues (c), and from a industrial sample (d).
The material obtained using only granite waste presented a spectrum with some crystalline peaks (see Figure 2a). Such peaks are characteristic of spinel, the first solid phase formed during the cooling, which is in accordance with the thermodynamic computational simulation of rock wools (Figure 1). The spinel formation indicates that the fast cooling process was not successfully performed, in other words, the process established enough time to form the first crystalline phase previously the occurrence of the vitrification.
Figures 2b and 2c respectively shown the X-ray diffraction spectra of
materials produced using only steelmaking slag and both residues. Absence of
notable crystalline peaks indicates that the materials are amorphous2727. Shi C and Zheng K. A review on the use of waste glasses in the
production of cement and concrete. Resources, Conservation and Recycling. 2007;
52(2):234-247.
http://dx.doi.org/10.1016/j.resconrec.2007.01.013.
http://dx.doi.org/10.1016/j.resconrec.20...
. Therefore, the fast cooling
processes were successfully performed.
3.6 Scanning Electronic Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) analyses of materials
Images obtained by SEM analysis of the formed materials are shown in Figure 3. The image of a current marketed rock wool is shown in Figure 3d. The homogeneous appearance of such image serves as reference to compare with the produced materials.
SEM images of rock wools fabricated using only granite waste (a), only steelmaking slag (b), both residues (c), and from a industrial sample (d).
The image of rock wools produced using only granite waste is shown in Figure 3a, in which the formation of a secondary phase was presented. Thus, EDS analysis was used to identify this region, the obtained spectrum is shown on Figure 4. The result is characteristic of the spinel phase, such fact is consistent with the spinel peaks shown in the XRD image of this material (Figure 2a).
The homogeneous appearances shown in Figures 3b and 3c indicate that secondary phases were not formed on materials produced using only steelmaking slag or both residues. Such results are in accordance with the amorphous curves in the XRD spectra obtained for these materials (Figures 2b and 2c).
3.7 Differential Thermal Analysis (DTA)
Figure 5 shows the results of DTA testing, where the graphics express the thermal behavior of the produced materials. Exothermic peaks correspond to the crystallization temperatures of the materials, while endothermic peaks represent the melting temperatures.
Differential thermal analysis of rock wools fabricated using only granite waste (a), only steelmaking slag (b), both residues (c), and from a industrial sample (d).
Differential thermal analysis of material produced using only granite waste is shown in Figure 5a. Results indicate a crystallization temperature of 780 °C and a melting temperature of approximately 1200 °C. Figure 5b shows that the material produced using only steelmaking slag presented a crystallization temperature of 840 °C and melting temperature of 1150 °C. The association of both residues generated a material with crystallization temperature of 850 °C and melting temperature of 1220 °C, as presented in Figure 5c. Images obtained by SEM analysis of the formed materials are shown in Figure 3. Results of all produced materials are in an accordance with the DTA obtained from a current marketed rock wool (Figure 5d), since the crystallization temperature of 830 °C and melting temperature of 1160 °C are close to the range obtained.
Rock wool is employed for the manufacture of products designed to prevent fire
spread. According to the Thermal Insulation Manufacturers’ Association, the
temperatures reached in a typical building fire are approximately 925 °C and
1030 °C after 1 and 2 hours, respectively1616. Thermal Insulation Manufacturers’ Association - TIMA. Man-made
vitreous fibers: nomenclature, chemical and physical properties. Stamford:
Owens-Corning Fiberglass; 1991. IPCS-WHO.. The rock wools present devitrification
temperatures of about 725-900 °C, then forming a polycrystalline material that
is thermally and essentially dimensionally stable, which is high enough to
contain a structural fire for several hours. The produced materials devitrified
at temperatures of 780, 840 and 850 °C, therefore these are within the
recommended devitrification temperature range. Gualtieri et al. investigated
several mineral wools and concluded that rock wool can be melted with a maximum
firing temperature of 1100 °C.2828. Gualtieri AF, Foresti E, Lesci IG, Roveri N, Gualtieri ML, Dondi
M, et al. The thermal transformation of Man Made Vitreous Fibers (MMVF) and safe
recycling as secondary raw materials (SRM). Journal of Hazardous Materials.
2009; 162(2-3):1494-1506. http://dx.doi.org/10.1016/j.jhazmat.2008.06.066.
PMid:18675512
http://dx.doi.org/10.1016/j.jhazmat.2008...
Produced materials in this work presented melting
temperatures in the range of 1150-1220 °C, complying with the standard
established for rock wools. Therefore, the above discussed thermal behavior of
produced materials qualifies them as appropriate for use as fire inhibitors.
3.8 Herty Viscosity Test
Results of the Herty viscosity test are shown in Table 3. The measures indicate the distance traveled by the materials prior to solidify, therefore the highest fluidity values correspond to the lowest viscosities.
The batch produced using only granite waste presented the highest viscosities,
while the material produced using only steelmaking slag showed lowest
viscosities for all casting temperatures. Glass viscosity is directly affected
by the function of oxides present in the chemical composition (glass former,
glass modifier, or intermediary). Alumina does not forms a glass under normal
conditions, however when added to an alkali-silicate glass it assumes a
tetrahedral coordination similar to silica, i.e. becomes a glass former2626. Bansal NP and Doremus RH. Handbook of glass properties. London:
Academic Press; 1986.,2929. Harper CA. Handbook of ceramics, glasses, and diamonds. New
York: McGraw-Hill Professional; 2001.. Considering the alumina as
a glass former, the material produced using only granite waste contains 62% of
glass forming elements and 30% of glass modifiers. Such proportions respectively
change to 54% / 33% using only steelmaking slag, and to 59% / 32% using both
residues. Differences on oxide contents capable of increase (glass formers) or
decrease (glass modifiers) viscosity explains the discrepancy of fluidity found
on produced materials2727. Shi C and Zheng K. A review on the use of waste glasses in the
production of cement and concrete. Resources, Conservation and Recycling. 2007;
52(2):234-247.
http://dx.doi.org/10.1016/j.resconrec.2007.01.013.
http://dx.doi.org/10.1016/j.resconrec.20...
.
Materials produced with only granite waste contains the highest proportion of
glass forming elements (62%) and presented the lowest fluidity range (40-70 mm).
Furthermore, materials produced with only steelmaking slag contains the lowest
proportion of glass forming (54%) and presented the highest fluidity range
(120-180 mm).
The viscosity decreased, i.e. fluidity increases, proportionally with growth of casting temperature for all the batches composition. Such phenomena is in accordance with the normal glass making behaviour, in which viscosity decreases logarithmically with the increase in temperature2626. Bansal NP and Doremus RH. Handbook of glass properties. London: Academic Press; 1986.,2929. Harper CA. Handbook of ceramics, glasses, and diamonds. New York: McGraw-Hill Professional; 2001.. The increase on casting temperature from 1400 °C to 1500 °C resulted on fluidity alterations of 30 mm (only granite waste), 60 mm (only steelmaking slag) and 50 mm (both residues).
4 Conclusions
Tests performed using only granite waste showed that a maximum amount of 66% of this residue may be used in substitution to traditional raw materials during the manufacture of rock wool. The use of higher amounts of granite waste increases the viscosity, which causes difficulties in the quenching process. The high content of silica and alumina present in the granite waste establishes this material as a potential substituent for the glass formers in rock wool production. Steelmaking slag may assume up to 53% of raw materials in rock wool production, mainly substituting the calcium carbonate and iron oxide. Batches with only steelmaking slag presented the higher fluidity and lower melting temperature. The use of steelmaking slag combined with granite waste as raw materials for rock wool production proved to be efficient, and provides a substitution rate up to around 70% of the total mixture, with a 1:2 slag/granite waste weight ratio. Thermal analysis also showed that steelmaking slag and granite waste may be used as partial substitutes of raw materials in rock wool production, since the addition of such wastes does not affect the overall quality of the material produced in terms of thermal insulation and prevention of fire spread.
The recovery of steelmaking slag from EAF and residue from granite cuttings as raw materials in the production of rock wool is recommended due to the reduction in extraction of non-renewable resources necessary to produce such material. Furthermore, the technique may also contribute to reduce the costs and hazard of waste storage by steelmaking and granite extraction companies, since these are residues with considerable production and limited applications.
References
-
1Zhuo C, Alves JO, Tenório JAS and Levendis YA. Synthesis of carbon nanomaterials through up-cycling agricultural and municipal solid wastes. Industrial & Engineering Chemistry Research. 2012; 51(7):2922-2930. http://dx.doi.org/10.1021/ie202711h.
» http://dx.doi.org/10.1021/ie202711h -
2Alves JO, Zhuo C, Levendis YA and Tenório JAS. Microstructural Analysis of Carbon Nanomaterials Produced from Pyrolysis/Combustion of Styrene-Butadiene-Rubber (SBR). Materials Research. 2011; 14(4):499-504. http://dx.doi.org/10.1590/S1516-14392011005000078.
» http://dx.doi.org/10.1590/S1516-14392011005000078 -
3Chou I-C, Kuo Y-M, Lin C, Wang J-W, Wang C-T and Chang-Chien G-P. Electroplating sludge metal recovering with vitrification using mineral powder additive. Resources, Conservation and Recycling. 2012; 58:45-49. http://dx.doi.org/10.1016/j.resconrec.2011.10.006.
» http://dx.doi.org/10.1016/j.resconrec.2011.10.006 -
4Cimdins R, Rozenstrauha I, Berzina L, Bossert J and Bücker M. Glassceramics obtained from industrial waste. Resources, Conservation and Recycling. 2000; 29(4):285-290. http://dx.doi.org/10.1016/S0921-3449(00)00053-7.
» http://dx.doi.org/10.1016/S0921-3449(00)00053-7 -
5Quijorna N, Coz A, Andres A and Cheeseman C. Recycling of Waelz slag and waste foundry sand in red clay bricks. Resources, Conservation and Recycling. 2012; 65:1-10. http://dx.doi.org/10.1016/j.resconrec.2012.05.004.
» http://dx.doi.org/10.1016/j.resconrec.2012.05.004 -
6World Steel Association. Crude steel statistics. 2010. Available from: <http://www.worldsteel.org>. Access in: 25/05/2011.
-
7Wang Q, Yan P and Feng J. A discussion on improving hydration activity of steel slag by altering its mineral compositions. Journal of Hazardous Materials. 2011; 186(2-3):1070-1075. http://dx.doi.org/10.1016/j.jhazmat.2010.11.109. PMid:21168967
» http://dx.doi.org/10.1016/j.jhazmat.2010.11.109 -
8Sebag MG, Korzenowski C, Bernardes AM and Vilela AC. Evaluation of environmental compatibility of EAFD using different leaching standards. Journal of Hazardous Materials. 2009; 166(2-3):670-675. http://dx.doi.org/10.1016/j.jhazmat.2008.11.125. PMid:19223119
» http://dx.doi.org/10.1016/j.jhazmat.2008.11.125 -
9Motz H and Geiseler J. Products of steel slags an opportunity to save natural resources. Waste Management. 2001; 21(3):285-293. http://dx.doi.org/10.1016/S0956-053X(00)00102-1. PMid:11280521
» http://dx.doi.org/10.1016/S0956-053X(00)00102-1 -
10Pioro LS and Pioro IL. Reprocessing of metallurgical slag into materials for the building industry. Waste Management. 2004; 24(4):371-379. http://dx.doi.org/10.1016/S0956-053X(03)00071-0. PMid:15081065
» http://dx.doi.org/10.1016/S0956-053X(03)00071-0 -
11Moreira JMS, Freire MN and Holanda JNF. Utilization of granite sawing waste from Espírito Santo state in red ceramic. Cerâmica. 2004; 49(312):262-267.
-
12Silva MA, Paes HR Jr and Holanda JNF. Reuse of ornamental rock-cutting waste in aluminous porcelain. Journal of Environmental Management. 2011; 92(3):936-940. http://dx.doi.org/10.1016/j.jenvman.2010.10.060. PMid:21074931
» http://dx.doi.org/10.1016/j.jenvman.2010.10.060 -
13Rodrigues GF, Alves JO, Tenório JAS and Espinosa DCR. Study of wastes from ornamental rocks for production of vitreous materials. Tecnologica em Metalurgia, Materiais e Mineração. 2011; 8(3):203-207. http://dx.doi.org/10.4322/tmm.2011.032.
» http://dx.doi.org/10.4322/tmm.2011.032 -
14Menezes RR, Ferreira HS, Neves GA and Ferreira HC. The use of granite wastes as ceramic raw materials. Cerâmica. 2002; 48(306):92-101.
-
15Trdič F, Sirok B, Bullen PR and Philpott DR. Monitoring mineral wool production using real-time machine vision. J. Real-Time Imaging. 1999; 5(2):125-140. http://dx.doi.org/10.1016/S1077-2014(99)80010-2.
» http://dx.doi.org/10.1016/S1077-2014(99)80010-2 -
16Thermal Insulation Manufacturers’ Association - TIMA. Man-made vitreous fibers: nomenclature, chemical and physical properties. Stamford: Owens-Corning Fiberglass; 1991. IPCS-WHO.
-
17Ueda M, Murase F, Takahashi F and Matsumoto T. An optical system for measuring the eccentricity of glass wool pipe - for industrial use. Optics and Lasers in Engineering. 1999; 31(6):493-501. http://dx.doi.org/10.1016/S0143-8166(99)00030-5.
» http://dx.doi.org/10.1016/S0143-8166(99)00030-5 -
18Marabini AM, Plescia P, Maccari D, Burragato F and Pelino M New materials from industrial and mining wastes: glass-ceramics and glass- and rock-wool fibre. International Journal of Mineral Processing. 1998; 53(1-2):121-134. http://dx.doi.org/10.1016/S0301-7516(97)00062-8.
» http://dx.doi.org/10.1016/S0301-7516(97)00062-8 -
19Brooks RF, Dinsdale AT and Quested PN. The measurement of viscosity of alloys -a review of methods, data and models. Measurement Science & Technology. 2005; 16(2):354-362. http://dx.doi.org/10.1088/0957-0233/16/2/005.
» http://dx.doi.org/10.1088/0957-0233/16/2/005 -
20Keene BJ. Slag atlas. 2nd ed. Düsseldorf: Verlag Stahleisen GmbH; 1995.
-
21Wang G, Wang Y and Gao Z. Use of steel slag as a granular material: volume expansion prediction and usability criteria. Journal of Hazardous Materials. 2010; 184(1-3):555-560. http://dx.doi.org/10.1016/j.jhazmat.2010.08.071. PMid:20843599
» http://dx.doi.org/10.1016/j.jhazmat.2010.08.071 -
22Juckes LM. The volume stability of modern steelmaking slags. Mineral Processing and Extractive Metallurgy. 2003; 112(3):177-197. http://dx.doi.org/10.1179/037195503225003708.
» http://dx.doi.org/10.1179/037195503225003708 -
23Buck RL. Man-made vitreous fibers. Norfolk: U.S. Navy Environmental Health Center; 1997. Technical Manual NEHC-TM6290.91-1, Rev. A.
-
24Liddell D and Miller K. Mineral fibers and health. Boca Raton: CRC Publishers; 1991.
-
25Luoto K, Holopainen M, Kangas J, Kalliokoski P and Savolainen K. Dissolution of short and long rockwool and glasswool fibers by macrophages in flowthrough cell culture. Environmental Research. 1998; 78(1):25-37. http://dx.doi.org/10.1006/enrs.1997.3825. PMid:9630442
» http://dx.doi.org/10.1006/enrs.1997.3825 -
26Bansal NP and Doremus RH. Handbook of glass properties. London: Academic Press; 1986.
-
27Shi C and Zheng K. A review on the use of waste glasses in the production of cement and concrete. Resources, Conservation and Recycling. 2007; 52(2):234-247. http://dx.doi.org/10.1016/j.resconrec.2007.01.013.
» http://dx.doi.org/10.1016/j.resconrec.2007.01.013 -
28Gualtieri AF, Foresti E, Lesci IG, Roveri N, Gualtieri ML, Dondi M, et al. The thermal transformation of Man Made Vitreous Fibers (MMVF) and safe recycling as secondary raw materials (SRM). Journal of Hazardous Materials. 2009; 162(2-3):1494-1506. http://dx.doi.org/10.1016/j.jhazmat.2008.06.066. PMid:18675512
» http://dx.doi.org/10.1016/j.jhazmat.2008.06.066 -
29Harper CA. Handbook of ceramics, glasses, and diamonds. New York: McGraw-Hill Professional; 2001.
Publication Dates
-
Publication in this collection
Jan-Feb 2015
History
-
Received
08 Sept 2014 -
Reviewed
12 Jan 2015