Mechanical and optical properties of conventional restorative glass-ionomer cements - a systematic review

Abstract

Objectives

To perform a systematic review of test methodologies on conventional restorative glass-ionomer cement (GIC) materials for mechanical and optical properties to compare the results between different GICs.

Material and Methods

Screening of titles and abstracts, data extraction, and quality assessments of full-texts were conducted in search for in vitro studies on conventional GICs that follow the relevant specifications of ISO standards regarding the following mechanical and optical properties: compressive strength, flexural strength, color, opacity and radiopacity.

Sources

The Latin American and Caribbean Health Sciences (LILACS), Brazilian Bibliography of Dentistry (BBO) databases from Latin-American and Caribbean System on Health Sciences Information (BIREME) and PubMed/Medline (US National Library of Medicine - National Institutes of Health) databases were searched regardless of language. Altogether, 1146 in vitro studies were selected. Two reviewers independently selected and assessed the articles according to pre-established inclusion/exclusion criteria. Among all the properties investigated, only one study was classified as being of fair quality that tested compressive strength and was included. It was observed that many authors had not strictly followed ISO recommendations and that, for some properties (diametral tensile strength and microhardness), there are no guidelines provided.

Conclusions

It was not possible to compare the results for the mechanical and optical properties of conventional restorative GICs due to the lack of standardization of studies.

Glass-ionomer cement; Mechanical properties; Optical properties; Restoration

Introduction

Since the 1950s, when the deleterious effects of mercury on humans became known, a worldwide movement to control and reduce its use in a variety of products, processes, and industries was observed11 - Azevedo FA, Nascimento ES, Chasin AM. In: Azevedo FA, Chasin AA, orgs. Metais: gerenciamento da toxicidade. São Paulo (SP): Atheneu; 2003. p. 299-352.. These actions culminated, with the signing of the Treaty of Minamata by 128 countries in October 2013, with the aim of reducing the atmospheric emissions of the mercury through environmental practices and the best available techniques for new enterprises22 - United Nations Environment Programme (UNEP). Minamata Convention on Mercury. Text and Annexes. Oct. 2013. [cited 2017 Aug. 03]. Available from: http://www.mercuryconvention.org/Portals/11/documents/Booklets/COP1%20version/Minamata-Convention-booklet-eng-full.pdf
http://www.mercuryconvention.org/Portals...
.

Currently, the two main direct dental materials available in oral health as alternatives to amalgam restorations are resinous materials and polyalkenoate-based materials, among which the most biomimetic material is the glass-ionomer cement33 - Srinivasan K, Chitra S. Emerging trends in oral health profession: the biomimetic - a review. Arch Dent Med Res. 2015;1(3):40-7..

The main advantages of composite resins are their excellent mechanical properties, good aesthetics and handling, which contribute to a reduced operative time44 - Ferracane JL. Resin composite - state of the art. Dent Mater. 2011;27(1):29-38.. On the other hand, the two most critical problems associated with such aesthetic restorations are the absence of therapeutic remineralization of the carious dentin and the low durability/integrity of the resin-dentin interface over time55 - De Munck J, van Landuyt K, Peumans M, Poitevin A, Lambrechts P, Braem M, et al. A critical review of the durability of adhesion to tooth tissue: methods and results. J Dent Res. 2005;84(2):118-32..

In contrast, glass-ionomer cements (GICs) have interesting properties such as biocompatibility, bioactivity, fluoride release, excellent coefficient of linear thermal expansion/contraction and modulus of elasticity, as well as being the only restorative material capable of chemically bonding to the tooth structure66 - Sidhu SK, Nicholson JW. A review of glass-ionomer cements for clinical dentistry. J Funct Biomater. 2016;7(3). pii: E16..

However, the first restorative GICs had insufficient mechanical properties to be indicated as definitive posterior and anterior restorations in permanent teeth77 - Peutzfeldt A, García-Godoy F, Asmussen E. Surface hardness and wear of glass ionomers and compomers. Am J Dent. 1997;10(1):15-7.,88 - Zafar MS, Ahmed N. Effects of wear on hardness and stiffness of restorative dental materials. Life Sci J. 2014;11:11-8.. In order to overcome their poor mechanical properties, various modifications have been added into the cement powder and liquid, such as bioactive apatite, zirconia, zinc, strontium oxide, fibers, stainless steel, silica, nanocrystals, among others99 - Lohbauer U, Walker J, Nikolaenko S, Werner J, Clare A, Petschelt A, et al. Reactive fibre reinforced glass ionomer cements. Biomaterials. 2003;24(17):2901-7.

10 - Gu YW, Yap AU, Cheang P, Khor KA. Zirconia-glass ionomer cement-A potential substitute for miracle mix. Scr Mater. 2005;52(2):113-6.

11 - Gu YW, Yap AU, Cheang P, Khor KA. Effects of incorporation of HA/ZrO2 into glass ionomer cement (GIC). Biomaterials. 2005;26(7):713-20.

12 - Zoergiebel J, Ilie N. Evaluation of a conventional glass ionomer cement with new zinc formulation: effect of coating, aging and storage agents. Clin Oral Investig. 2013;17:619-26.

13 - Boyd D, Towler MR. The processing, mechanical properties and bioactivity of zinc based glass ionomer cements. J Mater Sci Mater Med. 2005;16(9):843-50.

14 - Deb S, Nicholson JW. The effect of strontium oxide in glass-ionomer cements. J Mater Sci Mater Med. 1999;10(8):471-4.

15 - Kerby RE, Bleiholder RF. Physical properties of stainless-steel and silver-reinforced glass-ionomer cements. J Dent Res. 1991;70(10):1358-61.

16 - Tjandrawinata R, Irie M, Yoshida Y, Suzuki K. Effect of adding spherical silica filler on physico-mechanical properties of resin modified glass-ionomer cement. Dent Mater J. 2004;23(2):146-54.
-1717 - Silva RM, Pereira FV, Mota FA, Watanabe E, Soares SM, Santos MH. Dental glass ionomer cement reinforced by cellulose microfibers and cellulose nanocrystals. Mater Sci Eng C Mater Biol Appl. 2016;58(1):389-95.. As a result of these improvements, glass-ionomer cement may now be indicated for posterior and anterior restorations of deciduous and permanent teeth66 - Sidhu SK, Nicholson JW. A review of glass-ionomer cements for clinical dentistry. J Funct Biomater. 2016;7(3). pii: E16.,1818 - Gurgan S, Kutuk ZB, Ergin E, Oztas SS, Cakir FY. Clinical performance of a glass ionomer restorative system: a 6-year evaluation. Clin Oral Investig. 2017;21(7):2335-43..

Due to the wide variety of dental products that are constantly being launched in the world market, selecting the ideal restorative material becomes a difficult task for the clinician. Prior to clinical trials, laboratory tests are of fundamental importance in guiding professionals regarding the choice of material for their daily practice, as they test the effects of material composition changes or the evolution of their properties and can predict their clinical performance1919 - Frankenberger R, Krämer N, Lohbauer U, Nikolaenko SA, Reich SM. Marginal integrity: is this clinical performance of bonded restorations predictable in vitro? J Adhes Dent. 2007;9(Suppl 1):107-16..

The International Organization for Standardization (ISO) was established in 1947 with the aim of approving international standards in all technical fields, including dentistry. The ISO provides quality assurance for dental materials through regulation and standardization of tests that evaluate materials, ensuring their reproducibility in different centers2020 - Marsden A, Shahtout A. International Organization for Standardization. In: Garcia LS, editor. Clinical laboratory management. 2nd ed. Washington: ASM Press; 2014. p. 447-50..

It has been observed that many studies which have previously evaluated the properties of GICs did not follow a standardized protocol, such as environment temperature of specimen storage, duration of storage, size of the specimens and the load applied in the tests. All these factors are associated with variation in the manipulation technique in different centers and the lack of standardization on reporting in vitro studies and the powder/liquid ratio of the cements make it impossible to compare and discuss the results in literature2121 - Baig MS, Fleming GJ. Conventional glass-ionomer materials: a review of the developments in glass powder, polyacid liquid and the strategies of reinforcement. J Dent. 2015;43(8):897-912.

22 - Krithikadatta J, Gopikrishna V, Datta M. CRIS Guidelines (Checklist for Reporting In-vitro Studies): a concept note on the need for standardized guidelines for improving quality and transparency in reporting in-vitro studies in experimental dental research. J Conserv Dent. 2014;17(4):301-4.
-2323 - Dowling AH, Fleming GJ, McGinley EL, Addison O. Improving the standard of the standard for glass ionomers: an alternative to the compressive fracture strength test for consideration? J Dent. 2012;40(3):189-201..

Hence, a systematic review of literature is necessary in order to verify the standardization in laboratory tests performed with these materials.

Therefore, the objectives of this review were (1) to systematically analyze the conventional restorative GIC test methodologies for the following properties: compressive strength, flexural strength, color, opacity and radiopacity; and (2) to compare the above-mentioned properties of different GICs.

Material and methods

Protocol and registration

The protocol of this systematic review is registered at the Prospective International Registration of Systematic Reviews (PROSPERO) (https://www.crd.york.ac.uk/PROSPERO/) with reference number CRD42017050061. It aims to answer the following PICO question: Is it possible to compare the results of mechanical and optical properties of conventional restorative GICs obtained from laboratory studies?

Eligibility criteria

Inclusion criteria

In vitro studies published from 1990 onwards which reported on mechanical and optical properties (compressive strength, flexural strength, color, opacity, radiopacity) of conventional glass-ionomer cements were considered eligible. There was no language restriction.

Exclusion criteria

Studies were excluded if: 1) the number of specimens per group was less than five; 2) there was incorrect or missing statistical analysis; 3) the use of resin-modified glass-ionomer cement was reported; 4) it did not follow the recommendations of the ISO standards 9917-1 for compressive strength, color, opacity and radiopacity and 9917-2 and 4049 for flexural strength2424 - International Organization of Standardization. ISO 9917-1:2007 - Dental-water-based cements. Part 1: Powder/liquid acid-base cements. Geneva: ISO; 2016.

25 - International Organization for Standardization. ISO 9917-2:2017 –Dentistry - Water based cements. Part 2: Resin-modified cements. Geneva: ISO; 2017.
-2626 - International Organization for Standardization. ISO 4049:2009 - Dentistry - Water sorption and water solubility of resin cements. Geneva: ISO; 2009.. Whenever ISO established a range for the tests, the value considered was the mean value. For example, for the compressive strength test, it is established that the mechanical tester should be operated at a cross-head speed of (0.75±0.30) mm/min, the value considered was 0.75 mm/min.

Databases and search strategies

The literature search was conducted on the Latin American and Caribbean Health Sciences (LILACS) and Brazilian Bibliography of Dentistry (BBO) databases from the Latin-American and Caribbean System on Health Sciences Information (BIREME) on February 28th, 2018, as well as PubMed/Medline (US National Library of Medicine - National Institutes of Health) on March 1st, 2018. On the basis of the properties of conventional glass-ionomers assessed in this review — compressive strength, flexural strength, color, opacity and radiopacity — the search strategies were conducted using controlled vocabulary (MeSH terms/DeCS) and free keywords in English (PubMed, LILACS, BBO), Portuguese and Spanish (LILACS, BBO) as shown in Figures 1 and 2.

Figure 1
Search Strategy used for LILACS and BBO (Latin-American and Caribbean System on Health Sciences Information)

Figure 2
Search strategy used for PubMed/Medline (US National Library of Medicine - National Institutes of Health)

Selection of studies and calibration of investigators

Initially, the abstracts and titles of the studies identified by the search strategy were screened by two independent investigators in order to select the studies that would be fully read. The studies selected were then independently analyzed by the same two investigators in order to check their eligibility according to the inclusion and exclusion criteria. In case of disagreement between the investigators, a consensus was reached through discussion with external consultation.

Risk of bias and quality of evidence

Data extraction and quality assessment of the included studies were critically evaluated by two independent investigators. For quality assessment, the following variables were analyzed according to the CRIS guidelines2222 - Krithikadatta J, Gopikrishna V, Datta M. CRIS Guidelines (Checklist for Reporting In-vitro Studies): a concept note on the need for standardized guidelines for improving quality and transparency in reporting in-vitro studies in experimental dental research. J Conserv Dent. 2014;17(4):301-4. for in vitro studies: 1) sample preparation and handling; 2) allocation sequence and randomization process; 3) whether the evaluators were blinded; and 4) statistical analysis. Studies with information about all variables were deemed to be of good quality; if 2- 3 variables were present, they were deemed of fair quality; and lastly, they were classified as being of poor quality when none or just one aspect was covered.

Results

Search and included studies

Initially, 1146 studies were found, but only 367 articles were selected after screening the titles and abstracts. From these, 152 duplicated articles were excluded. Eventually, 215 articles were fully read, from which 118 were excluded due to the main exclusion criteria and 97 were excluded by not following the ISO Protocols. The number of articles excluded according to the ISO recommendation are shown in Table 1. Considering the distribution of studies according to the properties tested, it was observed that only one article about compressive strength was included, while none on flexural strength, color, opacity and radiopacity were according to our criteria (Figure 3).

Table 1
Number* of studies excluded according to the ISO recommendations by property

Figure 3
Flowchart showing the inclusion process of the studies that composed in the review

The characteristics of the study included are shown in Figure 4. Comparisons among studies were thus not possible.

Figure 4
Characteristics of the study included in the review according to the property tested

With respect to the quality assessment, the only study included was considered of fair quality, as the authors did not inform whether evaluators were blinded to the type of procedure or material that the sample was subjected to and how the samples were allocated to the different groups studied.

Discussion

In the field of dental materials, when a new product is finally tested in clinical trials, a series of laboratory tests would have already been carried out in order to verify its microstructure, properties and handling characteristics2828 - van Noort R. Clinical relevance of laboratory studies on dental materials: strength determination - a personal view. J. Dent. Suppl. 1994;22:S4-S8.. However, as no dental material currently available in the market has ideal properties for any dental application2929 - McCabe JF, Walls A. Applied dental materials. Hoboken: John Wiley & Sons; 2013.,3030 - Powers JM, Wataha JC. Dental materials: properties and manipulation. St. Louis: Elsevier Health Sciences; 2014., the industry/researchers are constantly searching for improvements. This requires, among other aspects, comparisons of laboratory test results of products from different generations, which is only possible if such tests follow standardized protocols. Therefore, this systematic review aimed to assess how some important characteristics and properties of conventional glass-ionomers were carried out according to the standards established by the ISO.

The selection of glass-ionomer is justified by the importance that the material gained since it was first proposed by Wilson and Kent more than 40 years ago3131 - Wilson AD, Kent BE. The glass-ionomer cement, a new translucent dental filling material. J Appl Chem Biotechnol. 1971;21:313-8.. With the advent of the Atraumatic Restorative Treatment (ART) 3232 - Frencken JE, Pilot T, Songpaisan Y, Phantumvanit P. Atraumatic restorative treatment (ART): rationale, technique, and development. J Public Health Dent. 1996;56(3 Spec No):135-40., a procedure in which the cavity is cleaned only with hand instruments and restored with glass-ionomer cement, the restorative version of GIC became popular and a variety of GIC brands became available. Currently, the properties of glass-ionomer cements have become even more relevant because this material has been considered as a possible alternative to dental amalgams. Thus, although the mechanical properties of a product do not necessarily entirely indicate its clinical performance2828 - van Noort R. Clinical relevance of laboratory studies on dental materials: strength determination - a personal view. J. Dent. Suppl. 1994;22:S4-S8., it is of paramount importance that a GIC has minimum standards set by recognized regulatory agencies before it can be considered appropriate for clinical use.

The results of this review show that, depending on the property studied, none or only one laboratory study universally followed valid standardized protocols proposed to test different GIC properties. Some authors stated that they followed the specifications, but they modified the dimensions of the test specimens, the storage times, and the speed of load application, therefore making it impossible to make direct comparisons with other studies2121 - Baig MS, Fleming GJ. Conventional glass-ionomer materials: a review of the developments in glass powder, polyacid liquid and the strategies of reinforcement. J Dent. 2015;43(8):897-912.. For the compressive strength test, the test machine can be regulated at a cross-head speed of 0.75 mm/min and, provided the established parameters have been followed, the observed values can be compared. The test machine should always be calibrated to ensure reliable results. In this study, the speed of 0.75 mm/min was fixed and the interval of ±0.30 was not considered, since, if they were, any publication that had used speed between 0.45 and 1.05 mm/min would have been included. However, the data from these publications would not be comparable, due to lack of standardization, similar to studies with test specimens of different sizes. Therefore, the ISO should be asked to modify this important specification detail. Another important aspect that should be mentioned refers to how in vitro studies are reported. It was observed that the only study included in this review did not inform on whether sample randomization was performed or whether the evaluators were blinded to the procedures that each sample was submitted to, since it is not a requirement of the ISO specifications. However, as in randomized clinical trials, the randomization process in an in vitro experiment reduces the chances of bias and guarantees that the difference in outcome between groups is by chance. In addition, the inclusion of independent observers promotes transparency of the results2222 - Krithikadatta J, Gopikrishna V, Datta M. CRIS Guidelines (Checklist for Reporting In-vitro Studies): a concept note on the need for standardized guidelines for improving quality and transparency in reporting in-vitro studies in experimental dental research. J Conserv Dent. 2014;17(4):301-4.. This is quite relevant, and a checklist for reporting studies has already been proposed to improve the quality and transparency in reporting in vitro studies in experimental dental research2222 - Krithikadatta J, Gopikrishna V, Datta M. CRIS Guidelines (Checklist for Reporting In-vitro Studies): a concept note on the need for standardized guidelines for improving quality and transparency in reporting in-vitro studies in experimental dental research. J Conserv Dent. 2014;17(4):301-4..

Unexpectedly, no studies regarding flexural strength, opacity, color and radiopacity survived the systematic review process and only one article for compressive strength could be included. This is of great concern as these properties are extremely important, since they are references for the indication of GICs for different clinical situations. Moreover, organizations such as the ISO seek to establish parameters to be observed before the introduction of new materials on the market. The Compressive Strength Test in particular is advocated by the ISO because most mastication forces are compressive in nature. The Compressive Fracture Strength (CFS) test is the only mechanical test established in ISO 9917 Part 1: Powder/liquid acid-base cements for hand-mixed GICs or conventional cements2424 - International Organization of Standardization. ISO 9917-1:2007 - Dental-water-based cements. Part 1: Powder/liquid acid-base cements. Geneva: ISO; 2016.. For resin-modified GICs, the ISO 9917 Part 2: Resin-modified cements2525 - International Organization for Standardization. ISO 9917-2:2017 –Dentistry - Water based cements. Part 2: Resin-modified cements. Geneva: ISO; 2017. do not recommend the CFS test, but the Flexural Strength (FS) test. Both tests can be considered satisfactory to evaluate the mechanical properties of restorative glass-ionomer cements and would represent stress-bearing in the clinical situation99 - Lohbauer U, Walker J, Nikolaenko S, Werner J, Clare A, Petschelt A, et al. Reactive fibre reinforced glass ionomer cements. Biomaterials. 2003;24(17):2901-7.. However, there is disagreement in the literature, considering that FS should be used rather than the CFS test, as GICs are brittle materials2323 - Dowling AH, Fleming GJ, McGinley EL, Addison O. Improving the standard of the standard for glass ionomers: an alternative to the compressive fracture strength test for consideration? J Dent. 2012;40(3):189-201.. According to Baig and Fleming2121 - Baig MS, Fleming GJ. Conventional glass-ionomer materials: a review of the developments in glass powder, polyacid liquid and the strategies of reinforcement. J Dent. 2015;43(8):897-912. (2015), the only mechanical test that represents a discriminatory performance indicator for hand-mixed GICs is the CFS test, compared to the Three-Point Flexure Strength, Biaxial Flexure Strength and Hertzian Indentation tests. As mechanical properties are not intrinsic properties of GICs, details are very important and can produce completely different results for the same material if the guidelines are different. For example, the method of material preparation, discrepancies in the powder:liquid ratio, size of the specimens, storage time and duration, the loading rate used to perform the test etc., all affect the results obtained. Currently, the ISO specifications established for compressive strength and flexural strength specify a crosshead speed range of 0.75±0.30 mm/min and 0.75±0.25 mm/min, respectively, which means that the range for CFS is of the order of 0.45-1.05 mm/min and for FS it is 0.5-1.0 mm/min. This allows investigators flexibility from the lowest to the highest speed and the impact of this is that their results cannot be compared. It is suggested that the ISO should replace range values with point values in the tests and that researchers should strictly follow the specifications, so that the results, even though in different laboratories, can be compared.

The only article included in this review was the study conducted by Nomoto and McCabe2727. Nomoto R, McCabe JF. Effect of mixing methods on the compressive strength of glass ionomer cements. J Dent. 2001;29(3):205-10. (2001). They evaluated the effect of mixing methods on the compressive strength and porosity of GICs. Among the materials tested was a conventional restorative GIC presented in two forms: Ketac Molar Hand-mix and Ketac Molar Aplicap (ESPE, Seefeld, Germany). Both had P/L ratio below 3.5 and the results exceeded the minimum value of compressive strength stipulated by the ISO. The authors concluded that manual manipulation and the P/L ratios seem not to be the main factors interfering with the results. Other factors, including the differences in composition, viscosity and the incorporation of porosity must be considered. They concluded that the compressive strength test was able to distinguish changes in the mechanical properties of GICs through changes in composition and extent of porosity. The authors also observed that the FS test was initially an alternative to CFS but was rejected due to the difficulties in obtaining reliable specimens for testing.

In this review, a systematic search of literature for two other mechanical properties considered important to be evaluated for GICs was carried out: Diametral Tensile Strength (DTS) and Microhardness. However, due to the lack of international regulation and standardization to evaluate such properties, they were eventually excluded from this review. By carefully analyzing the articles that evaluated DTS, we found that most of them refer to the American Dental Association specification number 27,3333 - American National Standards Institute. Specification No. 27, Resin-based Filling Materials. Chicago: American Dental Association; 1993. although this specification contraindicates this test. The ADA 27 specification relates to the ownership of “Tensile Strength (TS)”, which is very different from the property of “Diametral Tensile Strength (DTS)”.

The DTS test or “Tensile Strength by Diametral Compression” or “Brazilian Test” is the test adopted by the Brazilian Association of Technical Norms (ABNT) on the ABNT NBR 7222: 2011 registration3434 - Associação Brasileira de Normas Técnicas. NBR 7222:2011 - Concreto e argamassa - Determinação da resistência à tração por compressão diametral de corpos de prova cilíndricos. Rio de Janeiro: ABNT; 2011. for cylindrical specimens of concrete and not for dental cements. Therefore, there is an urgent need to: (1) come to a consensus about the relevance of testing GIC regarding DTS; and (2) to establish guidelines that can be applied globally with respect to the best way to test DTS.

According to the ISO 9917 Part 12424 - International Organization of Standardization. ISO 9917-1:2007 - Dental-water-based cements. Part 1: Powder/liquid acid-base cements. Geneva: ISO; 2016., to evaluate the optical properties for polyalkenoate restorative cements, the specimens should be prepared using a mold 1 mm thick and with 10 mm of internal diameter. Before measurements, the specimens must be stored for 7 days at 37°C in water in accordance with ISO 3696:19873535 - International Organization for Standardization. ISO 3696:1987: Water for analytical laboratory use -- Specification and test methods. Geneva: ISO; 1987.. The different studies on optical properties (color and opacity) in literature were not rigorously conducted using the ISO standard, and therefore were not included in this review. Twelve studies3636 - Li Q, Yu H, Wang Y. Colour and surface analysis of carbamide peroxide bleaching effects on the dental restorative materials in situ. J Dent. 2009;37(5):348-56.

37 - Lopes JH, Guimarães MS, Coldebella CR, Zu AC. Evaluation of ultrasonic waves application on glass ionomer cements: superficial roughness and hardness. Rev Odontol Bras Central. 2010;18(48):42-7.

38 - Wang E, Huang B. Discolouration of glass-ionomer cement at different fluoride concentration levels. Oral Health Dent Manag. 2014;13(2):1-4.

39 - Yu H, Pan X, Lin Y, Li Q, Hussain M, Wang Y. Effects of carbamide peroxide on the staining susceptibility of tooth-colored restorative materials. Oper Dent. 2009;34(1):72-82.

40 - Iazzetti G, Burgess JO, Gardiner D, Ripps A. Color stability of fluoride-containing restorative materials. Oper Dent. 2000;25(6):520-5.

41 - Gürdal P, Akdeniz BG, Hakan Sen B. The effects of mouthrinses on microhardness and colour stability of aesthetic restorative materials. J Oral Rehabil. 2002;29(9):895-901.

42 - Bezgin T, Özer L, Tulga Öz F, Özkan P. Effect of toothbrushing on color changes of esthetic restorative materials. J Esthet Restor Dent. 2015;27(Suppl 1):S65-73.

43 - Barutcigil C, Harorli OT, Yildiz M, Ozcan E, Arslan H, Bayindir F. The color differences of direct esthetic restorative materials after setting and compared with a shade guide. J Am Dent Assoc. 2011;142(6):658-65.

44 - Ayaz EA, Bagis B, Turgut S. Effect of antiasthmatic medication on the surface roughness and color stability of dental restorative materials. Med Princ Pract. 2014;23(1):24-8.

45 - Ayad NM. Susceptibility of restorative materials to staining by common beverages: an in vitro study. Eur J Esthet Dent. 2007;2(2):236-47.

46 - Autio-Gold JT, Barrett AA. Effect of fluoride varnishes on color stability of esthetic restorative materials. Oper Dent. 2004;29(6):636-41.
-4747 - Ashcroft AT, Cox TF, Joiner A, Laucello M, Philpotts CJ, Spradbery PS, et al. Evaluation of a new silica whitening toothpaste containing blue covarine on the colour of anterior restoration materials in vitro. J Dent. 2008;36(Suppl 1):S26-31. were excluded because the authors did not wait for the seven days required for specimens to be stored before analysis and four4848 - Prabhakar A, Pattanshetti K, Sugandhan S. A comparative study of color stability and fluoride release from glass ionomer cements combined with chlorhexidine. Int J Clin Pediatr Dent. 2013;6(1):26-9.

49 - Prabhakar AR, Mahantesh T, Vishwas TD, Aparna Kabade. Effect of surface treatment with remineralizing on the color stability and roughness of esthetic restorative materials. Arch Oral Res. 2009;5(1):19-27.

50 - Wang E, Huang B. Discolouration of glass-ionomer cement at different fluoride concentration levels. Oral Health Dent Manag. 2014;13(2):1-4.
-5151 - Yu H, Pan X, Lin Y, Li Q, Hussain M, Wang Y. Effects of carbamide peroxide on the staining susceptibility of tooth-colored restorative materials. Oper Dent. 2009;34(2):246. studies did the color analysis in specimens of 2 mm thick, making it impossible to compare results.

Regarding radiopacity, six articles were pre-selected, but five5252 - Yasa B, Kucukyilmaz E, Yasa E, Ertas ET. Comparative study of radiopacity of resin-based and glass ionomer-based bulk-fill restoratives using digital radiography. J Oral Sci. 2015;57(2):79-85

53 - Fonseca RB, Branco CA, Quagliatto PS, Gonçalves LS, Soares CJ, Carlo HL, et al. Influence of powder/liquid ratio on the radiodensity and diametral tensile strength of glass ionomer cements. J Appl Oral Sci. 2010;18(6):577-84.

54 - Hara AT, Serra MC, Rodrigues Júnior AL. Radiopacity of glass-ionomer/composite resin hybrid materials. Braz Dent J. 2001;12(2):85-9.

55 - Hitij T, Fidler A. Radiopacity of dental restorative materials. Clin Oral Investig. 2013;17(4):1167-77.
-5656 - Prévost AP, Forest D, Tanguay R, DeGrandmont P. Radiopacity of glass ionomer dental materials. Oral Surg Oral Med Oral Pathol. 1990;70(2):231-5. were excluded because the dimensions of the specimens did not follow ISO recommendations. One of them did not use the standard aluminum bar during radiographic shots and instead made specimens of different thicknesses5757 - Castro RY, Brasileiro CB, Giovannini JF. Evaluation of the gray-scale values of glass ionomer cement in indirect digital imaging. Arq Odontol. 2012;48(2):62-7..

In summary, it was not possible to compare the results of mechanical and optical properties of conventional restorative GICs, because of a lack of standardization of the studies. It is very important that researchers adhere to the ISO specifications when planning and implementing laboratory experiments to allow comparisons to be made between different conventional restorative GICs.

Conclusion

The scientific evidence that emerged from this review on the conventional restorative GIC test methodologies for mechanical and optical properties, which were compared in different GICs indicates that:

Only one published article that tested GIC mechanical and optical properties followed the ISO standards;

The study included was considered of fair quality, as the authors did not specify whether evaluators were blinded to the type of procedure/material that the sample was subjected to, and how samples were allocated to the different groups studied;

There is a need for ISO to replace the loading rate range with a loading rate standard for the mechanical tests for conventional restorative glass-ionomer cements;

There is a need for authors to strictly follow ISO instructions in laboratory experiments so that the data observed in different laboratories are comparable.

References

  • 1
    - Azevedo FA, Nascimento ES, Chasin AM. In: Azevedo FA, Chasin AA, orgs. Metais: gerenciamento da toxicidade. São Paulo (SP): Atheneu; 2003. p. 299-352.
  • 2
    - United Nations Environment Programme (UNEP). Minamata Convention on Mercury. Text and Annexes. Oct. 2013. [cited 2017 Aug. 03]. Available from: http://www.mercuryconvention.org/Portals/11/documents/Booklets/COP1%20version/Minamata-Convention-booklet-eng-full.pdf
    » http://www.mercuryconvention.org/Portals/11/documents/Booklets/COP1%20version/Minamata-Convention-booklet-eng-full.pdf
  • 3
    - Srinivasan K, Chitra S. Emerging trends in oral health profession: the biomimetic - a review. Arch Dent Med Res. 2015;1(3):40-7.
  • 4
    - Ferracane JL. Resin composite - state of the art. Dent Mater. 2011;27(1):29-38.
  • 5
    - De Munck J, van Landuyt K, Peumans M, Poitevin A, Lambrechts P, Braem M, et al. A critical review of the durability of adhesion to tooth tissue: methods and results. J Dent Res. 2005;84(2):118-32.
  • 6
    - Sidhu SK, Nicholson JW. A review of glass-ionomer cements for clinical dentistry. J Funct Biomater. 2016;7(3). pii: E16.
  • 7
    - Peutzfeldt A, García-Godoy F, Asmussen E. Surface hardness and wear of glass ionomers and compomers. Am J Dent. 1997;10(1):15-7.
  • 8
    - Zafar MS, Ahmed N. Effects of wear on hardness and stiffness of restorative dental materials. Life Sci J. 2014;11:11-8.
  • 9
    - Lohbauer U, Walker J, Nikolaenko S, Werner J, Clare A, Petschelt A, et al. Reactive fibre reinforced glass ionomer cements. Biomaterials. 2003;24(17):2901-7.
  • 10
    - Gu YW, Yap AU, Cheang P, Khor KA. Zirconia-glass ionomer cement-A potential substitute for miracle mix. Scr Mater. 2005;52(2):113-6.
  • 11
    - Gu YW, Yap AU, Cheang P, Khor KA. Effects of incorporation of HA/ZrO2 into glass ionomer cement (GIC). Biomaterials. 2005;26(7):713-20.
  • 12
    - Zoergiebel J, Ilie N. Evaluation of a conventional glass ionomer cement with new zinc formulation: effect of coating, aging and storage agents. Clin Oral Investig. 2013;17:619-26.
  • 13
    - Boyd D, Towler MR. The processing, mechanical properties and bioactivity of zinc based glass ionomer cements. J Mater Sci Mater Med. 2005;16(9):843-50.
  • 14
    - Deb S, Nicholson JW. The effect of strontium oxide in glass-ionomer cements. J Mater Sci Mater Med. 1999;10(8):471-4.
  • 15
    - Kerby RE, Bleiholder RF. Physical properties of stainless-steel and silver-reinforced glass-ionomer cements. J Dent Res. 1991;70(10):1358-61.
  • 16
    - Tjandrawinata R, Irie M, Yoshida Y, Suzuki K. Effect of adding spherical silica filler on physico-mechanical properties of resin modified glass-ionomer cement. Dent Mater J. 2004;23(2):146-54.
  • 17
    - Silva RM, Pereira FV, Mota FA, Watanabe E, Soares SM, Santos MH. Dental glass ionomer cement reinforced by cellulose microfibers and cellulose nanocrystals. Mater Sci Eng C Mater Biol Appl. 2016;58(1):389-95.
  • 18
    - Gurgan S, Kutuk ZB, Ergin E, Oztas SS, Cakir FY. Clinical performance of a glass ionomer restorative system: a 6-year evaluation. Clin Oral Investig. 2017;21(7):2335-43.
  • 19
    - Frankenberger R, Krämer N, Lohbauer U, Nikolaenko SA, Reich SM. Marginal integrity: is this clinical performance of bonded restorations predictable in vitro? J Adhes Dent. 2007;9(Suppl 1):107-16.
  • 20
    - Marsden A, Shahtout A. International Organization for Standardization. In: Garcia LS, editor. Clinical laboratory management. 2nd ed. Washington: ASM Press; 2014. p. 447-50.
  • 21
    - Baig MS, Fleming GJ. Conventional glass-ionomer materials: a review of the developments in glass powder, polyacid liquid and the strategies of reinforcement. J Dent. 2015;43(8):897-912.
  • 22
    - Krithikadatta J, Gopikrishna V, Datta M. CRIS Guidelines (Checklist for Reporting In-vitro Studies): a concept note on the need for standardized guidelines for improving quality and transparency in reporting in-vitro studies in experimental dental research. J Conserv Dent. 2014;17(4):301-4.
  • 23
    - Dowling AH, Fleming GJ, McGinley EL, Addison O. Improving the standard of the standard for glass ionomers: an alternative to the compressive fracture strength test for consideration? J Dent. 2012;40(3):189-201.
  • 24
    - International Organization of Standardization. ISO 9917-1:2007 - Dental-water-based cements. Part 1: Powder/liquid acid-base cements. Geneva: ISO; 2016.
  • 25
    - International Organization for Standardization. ISO 9917-2:2017 –Dentistry - Water based cements. Part 2: Resin-modified cements. Geneva: ISO; 2017.
  • 26
    - International Organization for Standardization. ISO 4049:2009 - Dentistry - Water sorption and water solubility of resin cements. Geneva: ISO; 2009.
  • 27
    Nomoto R, McCabe JF. Effect of mixing methods on the compressive strength of glass ionomer cements. J Dent. 2001;29(3):205-10.
  • 28
    - van Noort R. Clinical relevance of laboratory studies on dental materials: strength determination - a personal view. J. Dent. Suppl. 1994;22:S4-S8.
  • 29
    - McCabe JF, Walls A. Applied dental materials. Hoboken: John Wiley & Sons; 2013.
  • 30
    - Powers JM, Wataha JC. Dental materials: properties and manipulation. St. Louis: Elsevier Health Sciences; 2014.
  • 31
    - Wilson AD, Kent BE. The glass-ionomer cement, a new translucent dental filling material. J Appl Chem Biotechnol. 1971;21:313-8.
  • 32
    - Frencken JE, Pilot T, Songpaisan Y, Phantumvanit P. Atraumatic restorative treatment (ART): rationale, technique, and development. J Public Health Dent. 1996;56(3 Spec No):135-40.
  • 33
    - American National Standards Institute. Specification No. 27, Resin-based Filling Materials. Chicago: American Dental Association; 1993.
  • 34
    - Associação Brasileira de Normas Técnicas. NBR 7222:2011 - Concreto e argamassa - Determinação da resistência à tração por compressão diametral de corpos de prova cilíndricos. Rio de Janeiro: ABNT; 2011.
  • 35
    - International Organization for Standardization. ISO 3696:1987: Water for analytical laboratory use -- Specification and test methods. Geneva: ISO; 1987.
  • 36
    - Li Q, Yu H, Wang Y. Colour and surface analysis of carbamide peroxide bleaching effects on the dental restorative materials in situ J Dent. 2009;37(5):348-56.
  • 37
    - Lopes JH, Guimarães MS, Coldebella CR, Zu AC. Evaluation of ultrasonic waves application on glass ionomer cements: superficial roughness and hardness. Rev Odontol Bras Central. 2010;18(48):42-7.
  • 38
    - Wang E, Huang B. Discolouration of glass-ionomer cement at different fluoride concentration levels. Oral Health Dent Manag. 2014;13(2):1-4.
  • 39
    - Yu H, Pan X, Lin Y, Li Q, Hussain M, Wang Y. Effects of carbamide peroxide on the staining susceptibility of tooth-colored restorative materials. Oper Dent. 2009;34(1):72-82.
  • 40
    - Iazzetti G, Burgess JO, Gardiner D, Ripps A. Color stability of fluoride-containing restorative materials. Oper Dent. 2000;25(6):520-5.
  • 41
    - Gürdal P, Akdeniz BG, Hakan Sen B. The effects of mouthrinses on microhardness and colour stability of aesthetic restorative materials. J Oral Rehabil. 2002;29(9):895-901.
  • 42
    - Bezgin T, Özer L, Tulga Öz F, Özkan P. Effect of toothbrushing on color changes of esthetic restorative materials. J Esthet Restor Dent. 2015;27(Suppl 1):S65-73.
  • 43
    - Barutcigil C, Harorli OT, Yildiz M, Ozcan E, Arslan H, Bayindir F. The color differences of direct esthetic restorative materials after setting and compared with a shade guide. J Am Dent Assoc. 2011;142(6):658-65.
  • 44
    - Ayaz EA, Bagis B, Turgut S. Effect of antiasthmatic medication on the surface roughness and color stability of dental restorative materials. Med Princ Pract. 2014;23(1):24-8.
  • 45
    - Ayad NM. Susceptibility of restorative materials to staining by common beverages: an in vitro study. Eur J Esthet Dent. 2007;2(2):236-47.
  • 46
    - Autio-Gold JT, Barrett AA. Effect of fluoride varnishes on color stability of esthetic restorative materials. Oper Dent. 2004;29(6):636-41.
  • 47
    - Ashcroft AT, Cox TF, Joiner A, Laucello M, Philpotts CJ, Spradbery PS, et al. Evaluation of a new silica whitening toothpaste containing blue covarine on the colour of anterior restoration materials in vitro J Dent. 2008;36(Suppl 1):S26-31.
  • 48
    - Prabhakar A, Pattanshetti K, Sugandhan S. A comparative study of color stability and fluoride release from glass ionomer cements combined with chlorhexidine. Int J Clin Pediatr Dent. 2013;6(1):26-9.
  • 49
    - Prabhakar AR, Mahantesh T, Vishwas TD, Aparna Kabade. Effect of surface treatment with remineralizing on the color stability and roughness of esthetic restorative materials. Arch Oral Res. 2009;5(1):19-27.
  • 50
    - Wang E, Huang B. Discolouration of glass-ionomer cement at different fluoride concentration levels. Oral Health Dent Manag. 2014;13(2):1-4.
  • 51
    - Yu H, Pan X, Lin Y, Li Q, Hussain M, Wang Y. Effects of carbamide peroxide on the staining susceptibility of tooth-colored restorative materials. Oper Dent. 2009;34(2):246.
  • 52
    - Yasa B, Kucukyilmaz E, Yasa E, Ertas ET. Comparative study of radiopacity of resin-based and glass ionomer-based bulk-fill restoratives using digital radiography. J Oral Sci. 2015;57(2):79-85
  • 53
    - Fonseca RB, Branco CA, Quagliatto PS, Gonçalves LS, Soares CJ, Carlo HL, et al. Influence of powder/liquid ratio on the radiodensity and diametral tensile strength of glass ionomer cements. J Appl Oral Sci. 2010;18(6):577-84.
  • 54
    - Hara AT, Serra MC, Rodrigues Júnior AL. Radiopacity of glass-ionomer/composite resin hybrid materials. Braz Dent J. 2001;12(2):85-9.
  • 55
    - Hitij T, Fidler A. Radiopacity of dental restorative materials. Clin Oral Investig. 2013;17(4):1167-77.
  • 56
    - Prévost AP, Forest D, Tanguay R, DeGrandmont P. Radiopacity of glass ionomer dental materials. Oral Surg Oral Med Oral Pathol. 1990;70(2):231-5.
  • 57
    - Castro RY, Brasileiro CB, Giovannini JF. Evaluation of the gray-scale values of glass ionomer cement in indirect digital imaging. Arq Odontol. 2012;48(2):62-7.

Publication Dates

  • Publication in this collection
    21 Feb 2019
  • Date of issue
    2019

History

  • Received
    12 June 2018
  • Reviewed
    18 Sept 2018
  • Accepted
    20 Sept 2018
Faculdade De Odontologia De Bauru - USP Serviço de Biblioteca e Documentação FOB-USP, Alameda Dr. Octávio Pinheiro Brisolla 9-75, 17012-901 Bauru SP Brasil, Tel.: +55 14 3235-8373 - Bauru - SP - Brazil
E-mail: jaos@usp.br