Synthesis and characterization of aliphatic polyesters from glycerol, by-product of biodiesel production, and adipic acid

Synthesis and characterization of aliphatic polyesters from glycerol, by-product of biodiesel production, and adipic acid

Michel de Meireles Brioude^I; Danilo Hansen Guimarães^I; Raigenis da Paz Fiúza^I; Luis Antônio Sanches de Almeida Prado^II; Jaime Soares Boaventura^I; Nadia Mamede José^I,*

^IPrograma de Pós-graduação de Engenharia Química, Instituto de Química, Universidade Federal da Bahia, Campus de Ondina, 40170-290 Salvador - BA, Brazil

^IIInstitute of Polymer and Composites, Technische Universität Hamburg, Harburg

ABSTRACT

In the present work, polyesters were prepared from the polycondensation between glycerol and adipic acid using dibutyltin dilaurate as catalyst. Three glycerol: adipic acid molar ratio were used for the bulk polymerization namely: 2:2; 2:3 and 2:4. FTIR confirmed the esterification of glycerol by the acid for all the polymers. DSC and XRD indicated no crystallinity for all the polymers. The morphology of the materials are characterized by globular structure, which may suggest compositional fluctuations throughout the samples.

Keywords: polyester, glycerol, biodiesel

1. Introduction

In the past decades, the development of biomaterials received a great deal of attention. The first material derived from biological/natural sources is cellulose acetate, which is actually a biodegradable thermoplastic with many applications which includes reverse osmosis membranes¹. The development of the "green" composites based on vegetable fibres (juta, sisal among others) represent a new step into the use of renewable sources for engineering applications².

Recently the use of vegetal oils to produce monomers tailored for the synthesis of new polymers became a new and promising issue for the development of new materials with reduced cost production and interesting properties^3,4. Not only the manufacturing of thermoplastics and duromers (thermosets) may benefit from the use of these oils, but also the production of alternative fuels as renewable sources of energy. In this context, the development of new fuels (like the bio-diesel) and other products derived from the ricinus oil (castor oil) seems to be very promising^5-7.

Since bio-diesel is a renewable and environmentally friendly fuel, its production has been encouraged by the Brazilian government⁷. The ricinus oil is an interesting precursor for biodiesel production. Ricinus can be grown up in the arid north-western regions of Brazil, therefore Ricinus plants may become an income for rural population. As a result, 1 employee per 2 hectares may be contracted. The ricinus oil production is about 1 t/ha⁹.

During the cracking/processing of castor oil, huge amounts (30 wt. (%)) of glycerol are obtained as by-product¹⁰. Therefore, the development of new materials derived from the glycerol may contribute to make the production of bio-diesel even more attractive from the economical and technological point of view^11,12. In this context, we purpose the use of glycerol as monomer for the synthesis of aromatic and/or aliphatic polyesters¹³ with potential applications as membranes, additives for polyurethanes among others¹⁴.

2. Experimental

The starting materials were adipic acid, dibutyltin dilaurate (10 wt. (%) in hexanes) and glycerol were purchased from Vetec, Sigma-Aldrich and Synth, respectively.

For the polymerization process, glycerol and adipic acid were mixed in a three-necked round-bottomed flask equipped with a contact thermometer and a Claisen-condenser. The mixture was heated up to 100 °C under constant stirring. After the homogenisation of the mixture, the dibutyltin dilaurate was added and the temperature was increased up to 150 °C. As the polymerisation proceeded, the water produced during the reaction was distilled off and removed by the condenser. The glycerol/adipic acid molar ratio was varied in order to obtain polymers with different properties. The catalyst amount was kept constant at 0.15% (weight percentage) in relation to the total mass of monomers. The formulations used for the preparation of the poly(glycerol adipate) polymers are summarized in Table 1. For the sake of simplicity, these samples were coded as POLA.

The polymers were obtained as resinous solids and were dried under vacuum at 50 °C for at least 48 hours.

Powder X ray data for structural analysis were collected on a Shimadzu XRD-600 diffractometer, with Cu-Ka radiation (l = 1.54 Å), 30 kV potential and 20 mA current from 5 to 80 degrees.

The infra-red spectra were recorded on a Spectrum One (Perkin Elmer) instrument in the range of 4000 to 500 cm^–1 and the samples were analyzed as fine films, aiming at confirming the efficiency of the glycerol esterification process.

The thermal behavior of the polyesters was evaluated by a TGA/DTA 851 (Metler Toledo) thermo-balance. The samples were heated from 25 up to 1000 °C under N₂ flow using a heating rate of 20 °C/min, and on a DSC 60 (Shimadzu) calorimeter, using a heating rate of 20 °C/min from room temperature up to 600 °C.

The morphological analysis were carried out using a SS 550 Scanning Electron Microscope (Shimadzu). The acceleration voltage was 7 kV and the samples were sputtered with gold prior to the analysis.

3. Results and Discussions

3.1. Polymerisation reaction

The polyesters were produced through polycondensation polymerisation reactions between adipic acid and glycerol, as illustrated by Equation 1:

Since glycerol has three –OH groups, the formation of ramified and/or cross-linked structures can be postulated. The cross-linking degree is determined by the composition of the initial formulation. Highly cross-linked polyesters derived from glycerol and adipic acid is expected to be produced, if 2 mols of glycerol were fully esterified by 3 mols of adipic acid. Therefore, assuming the esterifcation reaction was complete, the polyester POLA II should present the highest cross-linking density of all the polymers prepared in the present work. The polymers POLAI and POLAIII have excess of –OH and –COOH functional groups, respectively. Hence, the structures of these materials should contain more branches.

The final structure of the networks does not depend solely on the composition, but also on the changes of the viscosity during the reaction¹⁵. Since the adipic acid is a solid material, the viscosity of the polymer reactions of mixtures containing higher amounts of adipic acid (POLA II and POLA III) should be higher than that obtained from mixtures having higher amounts of glycerol (POLA I). Since all the polymerization reactions were carried out without any solvent; the viscosity of the reaction media might be very high. In this case, the conversion could be hindered by the restricted diffusion of the monomers in the high viscous polymer dispersion. The high conversion could be guaranteed by removing the water produced during the polymerisation process. The removal of the water shifts the equilibrium to product generation; therefore, the formation of a polymer with higher molecular weight can be favoured.

In fact, the polymers were obtained as resinous materials as shown in Figure 1.

3.2. Characterization of the polyesters

3.2.1. X ray powder diffraction

The X ray diffractograms (Figure 2) showed a broad peak at 2q = 20°. This peak is associated to the intra-chain segments distance of 0.45 nm (determined using the Bragg's law)¹⁶. Since the intensity increased for the polyester containing higher amounts of adipic acid, it can be suggested that the excess of –COOH group favoured some mesomorphic (or crystalline) organization of the polyester chains.

3.2.2. Infrared spectroscopy (FTIR)

The infrared spectra of the polyesters POLA and of the adipic acid are shown in Figure 3. The esterification of glycerol is confirmed by the presence of the bands at 1739 cm^–1; 1134 and 1118 cm^–1; and 1080 and 1064 cm^–1, which can be assigned to the ester groups. The band at 1711 cm^–1 is indicative of the presence of un-reacted –COOH^17,18. The intensity of this band increases proportionally to the adipic acid content in the polymer. The assignment of the absorption bands is summarized in Table 2.

3.2.3. Evaluation of the thermal stability

The thermal stability of the POLA polyester was evaluated by thermogravimetric analysis (TGA). As can be seen in Figure 6a, the decomposition patterns of the POLA polymers present two steps. At temperatures below 100 °C, 2% of weight loss can probably be attributed to the volatilization of low molecular weight compounds (e.g. adsorbed water) and post-curing processes. The degradation of the polyester chain took place at temperatures higher than 300 °C, as observed for many aliphatic polyesters^19-22. The main degradation step occurred at ~ 300 to 485 °C, with a weight loss in the range of 96 to 98%. The chain scission takes place via transfer of the H (in the b position to the oxygen atoms of esterified –OH groups of the glycerol), followed by cleavage of the C-C bond of the glycerol moiety, yielding an alkene and free carboxylic acid as illustrated by the Figure 4.

In spite of the structural complexity, which is expected for the poly(glycerol adipate)s POLA I, II and III; there will be always an hydrogen atom in the suitable configuration for the occurrence of the scission described in Figure 4. Figure 5 detaches the H_b of the mono-esterified and the di-esterified moieties of the POLA polymers. It is clearly demonstrated here that, there will be always at least one H_b for all the isomers, therefore, all the networks prepared in this work should have very similar thermal stability.

In fact, the DTG curves of all polymers prepared in this work (Figure 6b) are very similar, on account of the presence of H_b in all the networks.

3.2.4. Analysis of the thermal behavior

The DSC curves of the POLA polymers are shown in Figure 7. The DSC results supported the conclusions drawn from the TGA and DTG. The evaporation and degradation processes could be identified as peaks associated to two endothermic processes in the intervals between 25-100 and 390-470 °C. Since no melting peaks could be identified in the DSC curves, these polyesters can be regarded as amorphous materials.

3.2.5. Scanning Electron Microscopy (SEM)

The polymers of series POLA had presented surface with roughness details, uniformly distributed in all the extension of the sample, as it can be seen in Figure 8.

4. Conclusions

The bulk polymerization between adipic acid and glycerol proved to be an efficient method for the production of new polyesters, though evidences for the presence of un-reacted –COOH groups were found for all the polymers prepared in this work. The materials had good mechanical and thermal stability (up to 390 °C). DSC and XRD results suggested that these materials are amorphous, although some organization may arise for the samples containing higher amounts of adipic acid.

These features could enable the use of these polyesters as modifiers for thermosets (epoxy resins) or polyurethanes. The use of these materials for the development of new membranes for gas-separation and pervapouration will be also considered and it is going to be a topic of research in our group for the coming years.

Acknowledgments

The authors acknowledge FAPESB (Fundação de Amparo à Pesquisa do Estado da Bahia) for the financial and technical support given to this work

Received: December 15, 2006; Revised: November 21, 2007

• 1. Duarte AP, Borado JC, Ciadade MT. Celulose acetate reverse osmosis membrances. Jornal of Applied Polymer Science 2007; 103(1):134.
• 2. Araguren MI, Mosiewicki M, Fernández JB. Natural composites: Polymeric matrices base on vegetable resources. Molecular Crystals and Liquid Crystals 2006; 448:747.
• 3. Can E, Wool RP, Kusefoglu S. Soybean and castor oil based monomers: Synthesis and copolymerization with styrene. Journal of Applied Polymer Science 2006a; 102(3):2433.
• 4. Can E, Wool RP, Kusefoglu S. Soybean. and castor-oil-based thermosetting polymers: mechanical properties. Journal of Applied Polymer Science 2006b; 102(3):1497.
• 5. Knothe G, Dunn RO, Bagby MO. Biodiesel: The use of vegetable oils and their derivatives as alternative diesel fuels. ACS Symposium Series 1997; 666:172.
• 6. Ma FR, Hanna MA. Biodiesel production. Bioressource Technology 1999; 70(1):1.
• 7. Fukuda H, Kondo A, Noda H. Biodiesel fuel production by transesterification of oils. Journal of Bioscience and Bioengineering 2001; 92(5):405.
• 8. Biodiesel no Brasil. [homepage on the Internet]. Curitiba: Biodiesel Online ltda; c. 2006-2007 [updated 2007 Nov 25; cited 2006 Aug]. Availabe from: http://www. biodieselbr.com/biodiesel/biodiesel-brasil.htm, accessed on 07/08/2006.
• 9. Tudo sobre a mamona [homepage on the Internet]. Curitiba: Biodiesel Online ltda; c. 2006-2007 [updated 2007 Nov 25; cited 2006 Aug]. Availabe from: http:// biodieselbr.com/plantas/mamona/index.htm accessed on 14/08/2006.
• 10 Muniyappa PR, Brammer SC, Noureddini H. Improved conversion of plant oils and animal fats into biodiesel, and co-product. Bioressouce Technology 1996; 56(1):19.
• 11. Bucio E, Lara-Estevez JCI, Ruiz-Trevino FA, Acosta-Huerta A. Synthesis and characterization of new polyesters derived from diphenols and aromatic diacids chlorides. Polymer Buletin 2006; 56(2-3):163.
• 12. Kiyotsukuri T, Kanaboshi M, Tsutsumi N. Network polyester films from glycerol and dicarboxylic acids. Polymer International 1994; 33(1):1.
• 13. Stumbe JF, Brunchmann B. Hyperbranched polyesters based on adipic acid and glycerol. Macromolecular Rapid Communications 2004; 25(9):921.
• 14. Polióis [homepage on the Internet]. Rio de Janeiro: Walter Vilar; c. 2004-2007 [updated 2007 Nov 25; cited 2006 Mar]. Availabe from:http://www.poliuretanos .com.br/Poliois, accessed on 06/03/2006.
• 15. Bryan E. Chemistry and technology of Epoxy Resins London: Champman & Hall; 1993. p. 72.
• 16. Azaroff LV. Elements of X-Ray Cristallography 1. ed. New York: McGraw-Hill; 1968.
• 17. Pavia DL, Lampman GM, Kriz GS. Introduction to Spectroscopy 2. ed. New York: Saunders College Publishing; 1996.
• 18. Nakanishi K, Solomon PH. Infrared Absorption Spectroscopy 2. ed. Oakland: Holden-Day; 1977.
• 19. Zorba T, Chrissafis K, Paraskevopoulos KM, Bikiaris DN. Efefect of molecular weight on thermal degradation mechanism of three poly(alkylene adipate)s: Comparative study. Polymer Degradation and Stability 2007; 92(2):222.
• 20. Chrissafis K, Paraskevopoulos KM, Bikiaris DN. Effect of molecular weight on thermal degradation mechanism of the biodegradable polyester poly(ethylene succiante). Thermochimica Acta 2006; 440(2):166.
• 21. Aoyagi Y, Yamashita K, Doi Y. Termal degradation of poly[(R)-3-hydroxybutyrate], poly[epsilon-caprolactone], and poly[(S)-lactide]. Polymer Degradation and Stability 2002; 76(1):53.
• 22. Arvanitoyannis I, Nakayama A, Kawasaki N, Yamamoto N. Novel star-shaped polylactide with glycerol using stannous octoate or tetraphenyl tin as catalyst.1.1 sysnthesis, characterization and study of their biodegradability. Polymer 1995; 36(15):2947.

Publication Dates

• Publication in this collection
  07 Feb 2008
• Date of issue
  Dec 2007

History

• Reviewed
  21 Nov 2007
• Received
  15 Dec 2006