Carboplatin-loaded surface modified-PLGA nanoparticles confer sustained inhibitory effect against retinoblastoma cell in vitro

Nanopartículas de PLGA com superfície modificada carregada com carboplatina conferem efeito inibitório sustentado contra células de retinoblastoma in vitro

ABSTRACT

Purpose:

To investigate the antiproliferative effect of carboplatin-loaded surface-modified poly(lactide-co-glycolide) on retinoblastoma cells.

Methods:

Carboplatin-loaded poly(lactide-co-glycolide) with or without sodium alginate surface modification was prepared using sodium alginate-poly(lactide-co-glycolide) and poly(lactide-co-glycolide). The zeta potential and carboplatin release behavior were investigated. The cellular uptake of the released drug was observed in the retinoblastoma cell line Y79. The inhibitory effect of carboplatin-loaded nanoparticles against the Y79 cell line was evaluated using methyl thiazolyl tetrazolium assay and western blot. Native carboplatin and void nanoparticles without carboplatin loading were used as controls.

Results:

The zeta potential was -(26.1 ± 3.1) mV for carboplatin-loaded poly(lactide-co-glycolide) and-(43.1 ± 8.1) mV for carboplatin-loaded sodium alginate-poly(lactide-co-glycolide). The burst release percentages of carboplatin-loaded poly(lactide-co-glycolide) and sodium alginate-poly(lactide-co-glycolide) were (40.0% ± 8.2%) and (18.9% ± 4.3%) at 24 hours, respectively. A significant difference was identified regarding drug release between carboplatin-loaded sodium alginate-poly(lactide-co-glycolide) and carboplatin-loaded poly(lactide-co-glycolide). Fluorescence detection revealed that intense uptake of carboplatin into the cytoplasm of the Y79 cell line that was exposed to carboplatin-loaded sodium alginate-poly(lactide-co-glycolide). Carboplatin-loaded poly(lactide-co-glycolide) or sodium alginate-poly(lactide-co-glycolide) exposure inhibited proliferating cell nuclear antigen expression in Y79 cells on day 3. Extension of exposure to day 5 revealed that the sodium alginate-poly(lactide-co-glycolide) surface modification was superior to that of poly(lactide-co-glycolide) in terms of proliferating cell nuclear antigen inhibition. The cell viability test using methyl thiazolyl tetrazolium revealed a similar inhibitory effect. Furthermore, the carboplatin-loaded nanoparticles of lower concentration inhibited cell viability more strongly than native carboplatin of higher concentration in methyl thiazolyl tetrazolium assay.

Conclusions:

Carboplatin-loaded sodium alginate-poly(lactide-co-glycolide) inhibited retinoblastoma cell proliferation with superior effect as compared with poly(lactide-co-glycolide) and native carboplatin. Sodium alginate surface modification offers a potential strategy for the sustained carboplatin release system.

Keywords:
Carboplatin; Alginate; Retinoblastoma; Nano-particle