During the cementation of ceramic veneers the polymerization of resin cements may be jeopardized if the ceramics attenuate the irradiance of the light-curing device. The aim of this study was to evaluate the effect of different types and thicknesses of ceramic veneers on the degree of conversion of a light-cured resin-based cement (RelyX Veneer). The cement was light-cured after interposing ceramic veneers [IPS InLine, IPS Empress Esthetic, IPS e.max LT (low translucency) and IPS e.max HT (high translucency) - Ivoclar Vivadent] of four thicknesses (0.5 mm, 1.0 mm, 1.5 mm and 2.0 mm). As control, the cement was light-cured without interposition of ceramics. The degree of conversion was evaluated by FTIR spectroscopy (n=5). Data were analyzed with one-way ANOVA and Tukey's test (α=0.05). Significant differences were observed among groups (p<0.001). The degree of conversion was similar to the control for all light-cured groups with interposition of ceramics of 0.5 mm and 1.0 mm (p>0.05). Among 1.5-mm-thick veneers, IPS e.max LT was the only one that showed different results from the control (p<0.05). At the thickness of 2.0 mm, only the IPS e.max LT and HT veneers were able to produce cements with degrees of conversion similar to the control (p>0.05). The degree of conversion of the evaluated light-cured resin cement depends on the thickness and type of ceramics employed when veneers thicker than 1.5 mm are cemented.
ceramics; degree of conversion; dental veneers; light-cured resin cements