Effect of S. mutans biofilm on the hybrid ceramic-resin cement bond strength assessed by different methods

Aim

The purpose of this study was to investigate the biofilm effect on the hybrid ceramic-resin cement bond strength (BS) by comparing two methods.

Methods

Teeth were distributed into groups (n=5), according to the resin cement (Maxcem Elite-(MC) or NX3 Nexus-(NX)) and degradation method (24h or 7 days in distilled water; 7 or 30 days incubated with biofilm and 30 days in sterile media). Treated surfaces of Vita Enamic blocks (5x6x7mm) were luted to treated or no treated dentin surfaces and light-cured. After 24h, beams were obtained (1x1x10mm) and stored accordingly. The flexural bond strength (FBS) was assessed by four-point bending test. Additional beams were obtained from new teeth (n=5), stored for 24h or 7 days in distilled water, and submitted to a microtensile bond strength (µTBS) assay. Failure modes were determined by scanning electron microscopy (100X). The flexure strength of the cements (n=10) was assessed by a four-point bending test. Data were analyzed by 1 and 2-ways ANOVA, and Tukey’s test (α=0.05).

Results

There was no significant difference between the degradation methods for the FBS groups. For the µTBS, the significant difference was as follows: NX 7days > NX 24h > MC 7days = MC 24h. Failure mode was mainly adhesive and mixed, but with an increase of cohesive within cement and pre-failures for the MC groups assessed by µTBS. NX had better performance than MC, regardless of the method.

Conclusions

The biofilm had no effect on the materials BS and FBS test was a useful method to evaluate BS of materials with poor performance.

Biofilms; Resin cements; Dental bonding; Tensile strength