On mechanical properties and bioactivity of PVDF-BCP composites

Propriedades mecânicas e bioativas do compósito PVDF-BCP

Abstract

A ceramic/polymer biocomposite with high potential for multifunctional practical applications in bone tissue engineering was synthesized by using a well-known piezoelectric polymer, polyvinylidene fluoride (PVDF), and a high bioactive biphasic calcium phosphate (BCP) ceramic obtained from recycled fish bones. High-bioactivity was observed for the PVDF-BCP composite when it was subjected to conditions that simulate the animal body once a very thick apatite layer (9 μm) was grown on its surface in an immersion experiment (7 days) in simulated body fluid. The structural characteristics of the PVDF-BCP composite showed similarities with highly bioactive young animal bones, overlapped with PVDF polymorphic phases. Mechanical tests revealed properties very similar to those of the human bone tissue with a resistance strength reaching 80 MPa. Together, all these factors indicated a very promising material for application in osseous implants/replacement with postoperative recovery controlled/accelerated by external stimuli.

Keywords:
biocomposites; PVDF; hydroxyapatite; bioactivity; biomaterials

Resumo

Um biocompósito cerâmico/polimérico com alto potencial para aplicações práticas multifuncionais em engenharia de tecidos ósseos foi sintetizado usando o conhecido polímero piezoelétrico, fluoreto de polivinilideno (PVDF), e a cerâmica altamente bioativa, fosfato de cálcio bifásica (BCP), obtida a partir de ossos de peixes reciclados. Uma alta bioatividade foi observada no compósito PVDF-BCP quando este foi submetido a condições que simulam um corpo animal. De fato, uma camada de apatita muito espessa (9 μm) cresceu em sua superfície no experimento de imersão (7 dias) em fluido corpóreo simulado (SBF). As características estruturais do compósito PVDF-BCP mostraram semelhanças com ossos de animais jovens, altamente bioativos, sobrepostos com fases polimórficas de PVDF. Ensaios mecânicos revelaram propriedades muito semelhantes às do tecido ósseo humano, com uma resistência à compressão atingindo 80 MPa. Juntos, todos esses fatores indicaram um material muito promissor para aplicação em implantes e/ou substituições ósseas com recuperação pós-operatória controlada/acelerada por estímulos externos.

Palavras-chave:
biocompósitos; PVDF; hidroxiapatita; bioatividade; biomateriais

INTRODUCTION

In the current research scenario of orthopedics and traumatology, the study of biomaterials has been intensified due to the development of new and improved medical treatment protocols that are directly correlated or dependent of the performance of these materials 11. B.D. Ratner, A.S. Hoffman, F.J. Schoen, J.E. Lemons, Biomaterials science: an introduction to materials in medicine, Academy Press, New York (1996).. For instance, their biocompatibility needs to be adequate because if these materials are inserted in an animal body they must not cause or stimulate any allergic or inflammatory reaction 11. B.D. Ratner, A.S. Hoffman, F.J. Schoen, J.E. Lemons, Biomaterials science: an introduction to materials in medicine, Academy Press, New York (1996).. In fact, bioactivity, easy absorption/integration by the human body and osseointegration, which is defined as the ability of the material to bind chemically to the bone by means of calcium phosphate formation, or apatite formation [Ca5-n(PO4)3(OH,F,Cl) - also called calcium deficient hydroxyapatite] 22. A.P.V. Pereira, W.L. Vasconcelos, R.L. Oréfice, Polímeros 9 (1999) 104., are key requirements for potentially applicable biomaterials 11. B.D. Ratner, A.S. Hoffman, F.J. Schoen, J.E. Lemons, Biomaterials science: an introduction to materials in medicine, Academy Press, New York (1996).. Among them, the so-called bioactive materials, which have the ability to bind or adhere to living tissues, have also attracted great interest 22. A.P.V. Pereira, W.L. Vasconcelos, R.L. Oréfice, Polímeros 9 (1999) 104.. Furthermore, advanced materials, as the multifunctional ones, have been pointed to drive the progress in this area because possess two or more properties or functionalities that can be used simultaneously or individually in the same device 11. B.D. Ratner, A.S. Hoffman, F.J. Schoen, J.E. Lemons, Biomaterials science: an introduction to materials in medicine, Academy Press, New York (1996).)-(44. R.L. Oréfice, Biomateriais: fundamentos e aplicações, Cultura Médica, Rio de Janeiro (2006).. Bioactive calcium phosphates, and specifically the hydroxyapatite [HA - Ca10(PO4)6(OH)2] that is one of their most interesting variations whose chemical, physical and mechanical characteristics are very close to the mineral phase of the human bone 33. M.I. Kay, R.A. Young, A.S. Posner, Nature 204 (1964) 1050., find large usability in medicine and dentistry, notably in bone implants, reconstruction and/or replacement of bone tissues 44. R.L. Oréfice, Biomateriais: fundamentos e aplicações, Cultura Médica, Rio de Janeiro (2006).. In fact, the use of HA has grown constantly due to the improved quality of life provided by its application in partial or full replacement of fractured bones 11. B.D. Ratner, A.S. Hoffman, F.J. Schoen, J.E. Lemons, Biomaterials science: an introduction to materials in medicine, Academy Press, New York (1996).. Moreover, HA-based ceramics tend to show special characteristics that are very similar to those of the animal bone as osteoconduction 55. S. Pollick, E.C. Shors, R.E. Holmes, R.A. Kraut, J. Oral Maxillofac. Surg. 53 (1995) 915., for instance, which is the process related to the bone growth on a surface 66. I. Ono, T. Tateshita, T. Nakajima, Biomaterials 21 (2000) 143.), (77. R.Z. Legeros, Clin. Orthop. Relat. Res. 395 (2002) 81.. These characteristics have been associated to the similar structure and chemical bonds usually found in mineral bone matrices and HA 88. P. Li, K.D.E. Groot, T. Kokubo, J. Sol-Gel Sci. Technol. 7 (1996) 27.), (99. W. Cao, L.L. Hench, Ceram. Int. 22 (1996) 493.), (1010. N. Specchia, A. Pagnotta, M. Cappella, A. Tampieri, F. Greco, J. Mater. Sci. 37 (2002) 577.), (1111. J. Venugopal, P. Vadgama, T.S.S. Kumar, S. Ramakrishna, Nanotechnology 18 (2007) 1.. Recently, a specific HA was obtained by an environmental friendly process which consists in the extraction of hydroxyapatite from the recyclable fish bones 1212. T.M. Coelho, E.S. Nogueira, A. Steimacher, A.N. Medina, W.R. Weinand, W.M. Lima, M.L. Baesso, A.C. Bento, J. Appl. Phys. 100 (2006) 094312.. This specific hydroxyapatite has an interesting structural biphasic formation hereinafter named as biphasic calcium phosphate (BCP), where BCP=HA+β-TCP [tricalcium phosphate in the β phase - Ca3(PO4)2], and shows elevated bioactivity and rapid natural absorption by the animal body 1313. C. Gao, B. Yang, H. Hu, J. Liu, C. Shuai, S. Peng, Mater. Sci. Eng. C 33 (2013) 3802.), (1414. Y. Tanimoto, Y. Shibata, A. Murakami, T. Miyazaki, N. Nishiyama, J. Hard Tissue Biol. 18 (2009) 2. due to the similarities between its properties and those of young osseous tissues. Interestingly, previous studies have also shown that BCP can be modified to achieve different mechanical configurations by controlling its porosity as a scaffold controlling 1515. S. Raynaud, E. Champion, J.P. Lafon, D. Bernache-Assollant, Biomaterials 23 (2002) 1081.. These studies also showed that BCP is more bioactive than pure HA or TCP 1616. M. Kohri, K. Miki, D.E. Waite, H. Nakajima, T. Okabe, Biomaterials 14 (1993) 299.. In this way, BCP emerges by showing a huge potential to practical applications in human bone substitution and can be combined with other materials to become a multifunctional material 1717. A.D.B.L. Ferreira, P.R.O. Nóvoa, A.T. Marques, Compos. Struct. 151 (2016) 3..

Composite materials naturally emerge as potential candidates for advanced applications due to the possibility of integrating two or more properties from different materials in a single component or device 1818. T.G.M. Bonadio, V.F. Freitas, T.T. Tominaga, R.Y. Miyahara, J.M. Rosso, L.F. Cótica, M.L. Baesso, W.R. Weinand, I.A. Santos, R. Guo, A.S. Bhalla, Curr. Appl. Phys. 17 (2017) 767.. For instance, a bioactive and a piezoelectric biocompatible material can be combined in a biocomposite to accelerate the bone calcification in the fracture healing process, whereas applied external oscillating electrical fields can activate the piezoelectric response, reorganizing the electric charges on the biocomposite surface and accelerating the bone healing 1919. F.R. Baxter, C.R. Bowen, I.G. Turner, A.C.E. Dent, Ann. Biomed. Eng. 38 (2010) 2079.. In this process, the direction of the surface induced electric dipoles () can be changed by using an external oscillating electric field (), as schematically shown in Fig. 1. This arrangement promotes a constant ionic exchange between the biomaterial surface and the osteoinductive medium or animal body, inducing and accelerating the formation of an HA layer, catalyzing the curing process. In the last years many studies with electrically polarized hydroxyapatite (HA) 2020. K. Yamashita, N. Oikawa, T. Umegaki, Chem. Mater. 8 (1996) 2697., BaTiO3 (BT) 2121. K.S. Hwang, J.E. Song, J.W. Jo, H.S. Yang, Y.J. Park, J.L. Ong, H.R. Hawls, J. Mater. Sci. Med. 13 (2002) 133., polyvinylidene fluoride (PVDF) 2222. M.P. Mahabole, R.C. Aiyer, C.R. Ramakrishna, B. Sheedhar, R.S. Khairnar, Bull. Mater. Sci. 28 (2005) 535., hydroxyapatite-barium titanate (HABT) 2323. J. Feng, H.P. Yuan, X.D. Zhang, Biomaterials 18 (1997) 1531., and poly(vinylidenefluoride-co-trifluoroethylene)-barium titanate [P(VDF-TrFE)-BaTiO3] 2424. M.M. Beloti, P.T. Oliveira, R. Gimenes, M.A. Zaghete, M.J. Bertolini, A.L. Rosa, J. Biomed. Mater. Res. 79 (2006) 282. composites were conducted in in vitro and in vivo experiments. The obtained results indicated a higher bioactivity for ceramics and polarized composites in comparison with non-polarized ones. Furthermore, high segregation/adsorption and formation of bone cells were observed in the negative surface of electrically polarized samples. In fact, polarized samples can be obtained when piezoelectric/ferroelectric materials are exposed to static external electrical fields. In this process, the internal dipoles/domains are oriented along the field direction, and one of the surfaces of the polarized material become negatively charged, while the other acquires a positive charge. In this way, considering previous reports where the influence of the electric charge surface on the activity of biomaterials 2525. J.E. Davies, Surface characterization of biomaterials, Elsevier, Amsterdam (1988). was pointed out and discussed, it is ease to intuit that piezoelectric materials can be used to catalyze biological responses. Recent studies have been conducted in order to understand the potentialities of the polyvinylidene fluoride [(C2H2F2)n or PVDF] matrix composites in human implants 2626. D.M. Correia, R. Gonçalves, C. Ribeiro, V. Sencadas, G. Botelho, J.L.G. Ribelles, S.L. Mendez, RSC Adv. 4 (2014) 33013.)-(3232. A.A. Ribeiro, L.G. Vaz, A.C. Guastaldi, J.S.C. Campos, Appl. Surf. Sci. 258 (2012) 10110.. In this way, different biological applications have been thought for PVDF polymer, leading to different synthesis technique and sample architectures, as scaffold, for example 2727. D.M. Correia, C. Ribeiro, V. Sencadas, L. Vikingsson, M.O. Gasch, J.L.G. Ribelles, G. Botelho, S.L. Mendez, Colloids Surf. B Biointerfaces 140 (2016) 430.. In fact, studies conducted in cell culture have indicated some advantageous aspect of PVDF polymer for animal implants. These results indicated high proliferation of the osteoblast cells, which are bone cells, in PVDF films 2828. C. Ribeiro, S. Moreira, V. Correia, V. Sencadas, J.G. Rocha, F.M. Gama, J.L.G. Ribelles, S.L. Mendez, RSC Adv. 2 (2012) 11504., and more bioactivity in the polar PVDF phase (β-PVDF) and poled PVDF films, mainly under mechanical stimuli 2929. J. Parssinen, H. Hammaren, R. Rahikainen, V. Sencadas, C. Ribeiro, S. Vanhatupa, S. Miettinen, S.L. Mendez, V.P. Hytonen, J. Biomed. Mater. Res. A 103 (2015) 919.), (3030. C. Ribeiro, J. Parssinen, V. Sencadas, V. Correia, S. Miettinen, V.P. Hytonen, S.L. Mendez, J. Biomed. Mater. Res. A 103 (2015) 2172.. Currently, a novel generation of highly advanced PVDF-based implants has been thought and developed, as those where PVDF-based nanogenerators, that were successfully implanted/tested in rats 3131. Y. Yu, H. Sun, H. Orbay, F. Chen, C.G. England, W. Cai, X. Wang, Nano Energy 27 (2016) 275., attested the applicability of PVDF for bio-applications. Furthermore, a PVDF-HA composite was also developed as an osseous implant 3232. A.A. Ribeiro, L.G. Vaz, A.C. Guastaldi, J.S.C. Campos, Appl. Surf. Sci. 258 (2012) 10110..

Figure 1:
Schematic representation of a possible post-trauma treatment with the excitation of an external electric field (E) in a bioactive/piezoelectric composite to accelerate a fracture healing process by the oscillation of the electric dipoles (P).
Figura 1:
Representação esquemática de um possível tratamento pós-trauma com a excitação de um campo elétrico externo (E) em um composto bioativo/piezoelétrico para acelerar um processo de cicatrização pela oscilação dos dipolos elétricos (P).

It seems clear that new multifunctional biomaterials must show a bioactivity influenced by another property, which should be externally controlled. In addition, these biomaterials must have specific properties (mechanical, thermal, electrical, etc.) that fit the needs of human body implants. In this context, interesting requirements for biocompatible composites, as adjustable mechanical, thermal and possibly piezoelectric properties, can be fitted by PVDF-BCP composites. In fact, PVDF can exhibit four crystalline phases (α, β, γ and δ) that can be differentiated by the C-C bond conformation along its main polymeric chain and by their piezoactivity 3333. H. Kawaii, Jap. J. Appl. Phys. 8 (1969) 975.. The polar β-phase is the most interesting for practical applications once it shows very intense piezoelectric and pyroelectric responses 3434. C. Constantino, A. Job, R. Simões, J. Giacometti, V. Zucolotto, O. Oliveira, J. Gozzi, D. Chinaglia, Appl. Spectrosc. 59 (2005) 275.. Furthermore, the amounts of crystalline phase and the percentage of the β-phase can be tuned by adequate protocols of samples processing. On the other hand, BCP is a highly bioactive material with mechanical properties very different (it is stronger and harder) from that of PVDF. Thus, a possible mixing of the BCP ceramic with PVDF polymer can result in an interesting multifunctional bioactive composite that can be used in a vast range of novel biomedical applications. In fact, different structural and physical (mechanical, thermal, electrical, etc.) properties can be achieved in these composites by simply adjusting/tuning the PVDF and BCP concentrations, leading to different materials that can be used in different parts of the body. However, for reaching the desired applications a long way still needs to be covered and basic characterization on synthesis processes and bioactivity responses must be developed. In this work, a PVDF-BCP composite was synthesized in order to obtain a multifunctional bioactive material for replacement of animal osseous tissues. Its structural, microstructural and mechanical properties, as well its bioactivity, were investigated and the combined results indicate that this composite can be adequately used for implants in different areas of the human body. In fact, the structural investigations revealed the formation of a biphasic composite material formed by the PVDF polymer, α and β phases, and the BCP ceramic, HA+β-TCP, whose structure favors biocompatibility. The mechanical properties of the PVDF-BCP composite were found very close to those of the human bone tissue and the scanning electron microscopy images revealed that a very thick HA layer was grown on the composite surface in the SBF experiment, attesting the high-bioactivity of the PVDF-BCP composite.

MATERIALS AND METHODS

The 60%PVDF-40%BCP (PVDF-BCP) composite was prepared by a conventional powder mixture protocol (mass - wt%), starting from synthetic PVDF powder (Alfa-Aesar 99.8%, melting point 155 to 170 ºC, density 1,78 g/mL) and BCP (90% HA-10% β-phase) obtained from Brazilian rives fish bones (Pintado - Pseudoplatystoma corruscans) in a recycling process. The bulk of PVDF polymer was formed in disk (thickness 1 mm, diameter 10 mm) by uniaxial pressure (<50 MPa) and consolidated at 170 ºC in air for 1 h. Then, the BCP ceramic was achieved by 8 h of calcination at 900 ºC and milled for 8 h at 300 rpm in a mill (Retsh, PM 100) using a sphere/powder mass ratio of 6:1 1212. T.M. Coelho, E.S. Nogueira, A. Steimacher, A.N. Medina, W.R. Weinand, W.M. Lima, M.L. Baesso, A.C. Bento, J. Appl. Phys. 100 (2006) 094312.. The composite powder was homogenized (agate mortar, 30 min), conformed in bars (thickness 1 mm, width 5 mm, length 10 mm), discs (thickness 1.1 mm, diameter 10 or 25 mm) and cylinder (height 10 mm, diameter 10 mm) shapes (for different characterization protocols) and compacted under uniaxial pressure of 114 MPa. After that, the sample was consolidated at 170 °C in air for 1 h.

Simulated body fluid (SBF), which simulates the conditions of the human body for preliminary bioactivity tests, in-vitro tests 3535. H.M. Kim, F. Miyaji, T. Kokubo, C. Ohtsuki, T. Nakamura, J. Am. Ceram. Soc. 78 (1995) 2405.), (3636. Y. Abe, M. Kawashita, T. Kokubo, T. Nakamura, J. Ceram. Soc. Jpn. 109 (2001) 106., was prepared in agreement with Kokubo protocol, or ISO 23317:2014, and used to investigate the bioactivity of the composite and its precursors. The samples’ densities were obtained by the Archimedes method using distilled water. Structural characterizations were performed by X-ray diffraction (XRD) using a Shimadzu XRD7000 diffractometer (CuKα radiation) in the 2θ range of 15º to 50º and a scan rate of 2 º/min. The samples’ hardness was investigated by performing Vickers hardness (HV) tests (averaging 10 indentations on each sample) with an applied force of 204 gf in a Digital Multi Specimen Test System (UMT, CETR/Bruker) with a diamond indenter. Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) analyzes were performed in gold metalized samples by using an SEM-FEG HR (FEI, Inspect F50) microscope. The mechanical tests, performed to obtain the maximum compressive strength (σ), were conducted in a Shimadzu universal mechanical testing machine AGS-X 100 kN according to the ASTM C773-88 3737. Am. Soc. Test. Mater., ASTM C773-88: “Standard test method for compressive (crushing) strength of fired whiteware materials”, B. Stand. (2011).. The mechanical elastic coefficients [Young (E) and shear (G) moduli] were obtained by using the impulse excitation technique (dynamic method) by following the ASTM E 1876 3838. Am. Soc. Test. Mater., ASTM E1876-09: “Standard test method for dynamic Young’s modulus, shear modulus, and Poisson’s ratio by impulse excitation of vibration”, B. Stand. (2012). in an ATCP Sonelastic tester. The Poisson’s ratio (ν) was obtained using the following equation 3939. E.S.S. Yousef, J. Phys. D Appl. Phys. 38 (2005) 3970.), (4040. J.A. Sampaio, M.L. Baesso, S. Gama, A.A. Coelho, J.A. Eiras, I.A. Santos, J. Non-Cryst. Solids 304 (2002) 293.:

υ = ( 1 6 H V E ) ( 6 H V E + 2 ) 1 (A)

where HV is the measured Vickers hardness and E Young’s modulus. The longitudinal modulus was obtained from:

L = 2 G ( υ 1 ) 2 υ 1 (B)

where G is the shear modulus. The shear and longitudinal velocities of sound were given by:

V S = ( G ρ ) 1 2 (C)

V L = ( L ρ ) 1 2 (D)

Finally, the mean velocity of sound, or Debye mean velocity, was obtained from:

V M = [ 1 3 ( 1 V S 3 + 1 V L 3 ) ] 1 / 3 (E)

RESULTS AND DISCUSSION

Fig. 2 shows the XRD results for disk shape PVDF (polymer), BCP (ceramic), and PVDF-BCP (composite) samples. The XRD pattern of the PVDF sample (Fig. 2a) shows a typical amorphous pattern overlapped by two crystalline ones, which are associated to the nonpolar (α) and polar (β) PVDF polymorphic phases. The XRD pattern obtained for the BCP ceramic (Fig. 2c) was perfectly indexed by overlapping the diffraction patterns of HA and β-TCP phases. The typical well-structured diffraction pattern of BCP, overlapped with the amorphous PVDF signature, was observed in the XRD pattern of the PVDF-BCP composite (Fig. 2b). As expected, the well-crystallized BCP structure was predominant in this pattern due to the elevated X-ray scattering of BCP phase in comparison with that of the PVDF 4141. T.H. Lee, F.Y.C. Boey, K.A. Khor, Polym. Compos. 16 (1995) 481-488.. Furthermore, a line broadening was also observed in this pattern as an indicative of a well-homogenized mixture.

Figure 2:
X-ray diffraction patterns for: (a) PVDF polymer; (b) PVDF-BCP composite; and (c) BCP ceramic, before immersion in simulated body fluid (SBF).
Figura 2:
Difratogramas de raios X para: (a) polímero PVDF; (b) compósito PVDF-BCP; e (c) cerâmica BCP, antes da imersão em fluido corporal simulado (SBF).

Fig. 3 shows stress-strain curves, obtained from compressive mechanical tests, for the three studied samples (BCP, PVDF and PVDF-BCP) formed in a cylinder shape. As shown by the maximum loads (LoadMAX) highlighted in Fig. 3, the PVDF-BCP composite holds out higher mechanical stresses than PVDF or BCP samples. On the other hand, Young’s modulus of the BCP phase, as expected for ceramics in comparison with polymer-ceramic composites, was higher than that obtained for the PVDF-BCP sample. However, a close look at the low load region revealed a very interesting behavior. As can be seen, in the very low-stress regime (inset in Fig. 3, ε<0.5%) the drawn lines under the curves (solid, dashed and dotted) show considerable high inclinations in all cases. In fact, as high as the slope of stress (σ)-strain (ε) curve (σ=E.ε) in the elastic region, higher is Young’s modulus of the analyzed sample. In this way, it is seen that in the elastic regime the PVDF-BCP composite showed the highest Young’s modulus and can be potentially used in implants where low compressive stress charges are required, as in bone grafts. However, with strain increasing (ε<1.2%) the composite microstructure tended to accommodate the applied stress and an intermediate Young’s modulus, between those observed for PVDF and BCP, was observed for the PVDF-BCP composite (Fig. 3).

Figure 3:
Compressive stress-strain curves for PVDF polymer, BCP ceramic, and PVDF-BCP composite. The draw lines are linear fit in elastic regions of the PVDF-BCP (solid line), BCP (dashed line) and PVDF (dotted line) compounds. Inset: enlarged view of the low strain region.
Figura 3:
Curvas tensão-deformação de compressão para o polímero PVDF, cerâmica BCP e compósito PVDF-BCP. As linhas foram ajustadas linearmente em regiões elásticas dos compostos PVDF-BCP (linha contínua), BCP (linha tracejada) e PVDF (linha pontilhada). Inserto: visão ampliada da região de baixa deformação.

The mechanical-elastic coefficients, total apparent densities and Vickers hardness obtained for PVDF polymer, BCP ceramic, and PVDF-BCP composite are listed in Table I. Previously reported mechanical coefficients for cortical and cancellous human bone tissue 4242. S.C. Cowin, Bone mechanics handbook, 2nd Ed., CRC Press, New York (2001).), (4343. S. Pal, Design of artificial human joints & organs, Spring, New York (2014). are also listed in Table I for comparison. It is worth noting that the mechanical properties of human bone tissues are very dependent on the bone type, part of the body, age and even the sex of the specimen 3737. Am. Soc. Test. Mater., ASTM C773-88: “Standard test method for compressive (crushing) strength of fired whiteware materials”, B. Stand. (2011).), (3838. Am. Soc. Test. Mater., ASTM E1876-09: “Standard test method for dynamic Young’s modulus, shear modulus, and Poisson’s ratio by impulse excitation of vibration”, B. Stand. (2012).. In addition, the osseous density of each individual animal body must be associated with personal characteristics (biotype, genetics, place and style of life, etc.) 3737. Am. Soc. Test. Mater., ASTM C773-88: “Standard test method for compressive (crushing) strength of fired whiteware materials”, B. Stand. (2011).), (3838. Am. Soc. Test. Mater., ASTM E1876-09: “Standard test method for dynamic Young’s modulus, shear modulus, and Poisson’s ratio by impulse excitation of vibration”, B. Stand. (2012).. Likewise, the mechanical properties of the test-bodies are also dependent on their preparation, dry or wet bone, type of analysis, and others. Nevertheless, the obtained experimental data (Table I) can be used in our analyses as a base for comparison with those reported in the literature. The elastic moduli (Young and shear) of the PVDF-BCP composite reached intermediate values between PVDF and BCP. However, the Vickers hardness of the PVDF-BCP composite seemed to be closer to that of bone, both cortical and cancellous, than BCP ceramic. A significant result was also observed by comparing the densities of the studied samples. The composite density achieved an intermediate value (2160 kg/m3) between cortical bone (1810 kg/m3) and porous BCP ceramic (2360 kg/m3) that is closer to the human bone than BCP, even more if this result is compared with that reported for non-porous HA (3156 kg/m3) 4444. W.R. Weinand, A.C. Bento, M.L. Baesso, W.M. Lima, J. Appl. Phys. 104 (2008) 2.. The shear modulus of the composite was also more similar to that of bone than that observed for PVDF or BCP, as shown in Table I. On the other side, the Poisson’s ratio of the PVDF-BCP composite was very similar to that of bone and BCP. The maximum compressive strength reached by the composite (~80 MPa) was the greatest among those investigated samples and was close to the observed for human femur (107 MPa) 4444. W.R. Weinand, A.C. Bento, M.L. Baesso, W.M. Lima, J. Appl. Phys. 104 (2008) 2.. Finally, the sound velocities were also calculated and showed to be proportional to the respective elastic modulus and Vickers hardness, as expected. As observed by comparatively analyzing the mechanical properties of PVDF-BCP composite, its huge potential for multifunctional applications in bone implants become evident.

Table I -
Mechanical properties for PVDF polymer, BCP ceramic, PVDF-BCP composite, cortical and cancellous human bone tissues: Vickers hardness (HV), Young’s or elastic modulus (E), shear modulus (G), maximum compressive strength (σ), Poisson’s ratio (ν), density (ρ), and shear (VS), longitudinal (VL), and mean (VM) velocities of sound in the medium.
Tabela I -
Propriedades mecânicas para polímero PVDF, cerâmica BCP, compósito PVDF-BCP, tecido cortical e tecido esponjoso dos ossos humanos: dureza Vickers (HV), módulo de Young ou elástico (E), módulo de cisalhamento (G), resistência de compressão máxima (σ), razão de Poisson (ν), densidade (ρ) e velocidades de cisalhamento (VS), longitudinal (VL) e média (VM) do som no meio.

Fig. 4 shows the FEG-SEM images and the EDS analysis performed on the surfaces and fractured surfaces of BCP, PVDF and PVDF-BCP disk shape samples recovered from immersion in simulated body fluid (SBF) for 7 days. These tests in SBF can reveal the bioactivity of material by the direct observation (preferentially by SEM) of an HA layer formed on the surface/pores of the analyzed sample, as well as by the determination of the dimensions of this layer. In this way, as high the material bioactivity, higher is the HA layer observed in the SEM analysis. As can be seen, the apatite layer on the surface of BCP ceramic reached a thickness of ~3 μm (Fig. 4a), attesting its elevated bioactivity. Images of fractured surfaces were also obtained for helping understand the growth paths of HA in this sample. The SEM analysis of fractured surfaces of the BCP sample ceramic revealed a high porous sample with an HA layer grown inside the pores (Fig. 4d). This result is in agreement with previous works on modified BCP ceramics, where an HA layer was also observed inside the ceramics’ pores 4545. G. Ciobanua, S. Ilisei, C. Lucaa, G. Carjaa, O. Ciobanub, Prog. Org. Coat. 74 (2012) 648.. In fact, in most cases, the intra-porous growth is desired because it can create a more interconnected structure that can help in the healing process by changing its kinetics in a faster osteointegration 55. S. Pollick, E.C. Shors, R.E. Holmes, R.A. Kraut, J. Oral Maxillofac. Surg. 53 (1995) 915.. Interestingly, a still larger HA layer was observed on the surface of the PVDF-BCP composite, reaching a thickness of ~9 μm, which was 3 times higher than that observed in the BCP ceramic. This may be due to porosity difference and/or the biocompatibility itself. In fact, usually BCP ceramics are more porous and because this the apatite formation can occur into the pores. Furthermore, spheres with ~10 μm in diameter can be observed on the surface of the PVDF-BCP composite (Fig. 4b) in a clear evidence of a uniform HA formation 4646. A. Takeuchi, C. Ohtsuki, T. Miyazaki, M. Kamitakahara, S.-I. Ogata, M. Yamazaki, Y. Furutani, H. Kinoshita, M. Tanihara, J. R. Soc. Interface 2 (2005) 373.. Differently, the SEM analysis of the fractured PVDF-BCP surface (Fig. 4e) did not reveal pores filled by HA. It is worth noting that in many cases, such as cartilaginous tissue of the ear or the confection of a mesh to support broken tissues, surface growth can be most desired to maintain the flexibility of this kind of tissue. Thus, it is clear that the PVDF-BCP composite can be potentially used in such kind of application. Moreover, techniques for obtaining controlled scaffolds can be used to produce pores in the PVDF-BCP composite, increasing its range of medical and biological applicability. Conversely, an HA layer was not observed in the PVDF polymer (Fig. 4c). In fact, a high dense and high compressed polymer matrix was observed in the SEM analysis of the PVDF fractured surface (Fig. 4f). It is worth noting that the EDS analyzes showed different surface compositions for the three studied samples (Figs. 4g to 4i). In fact, the EDS analysis shown in Fig. 4g reveals the presence of Ca and P ions on the surface of the BCP ceramic, indicating this phase as a typical HA layer. Likewise, EDS results (Fig. 4h) confirmed the HA type growth on the surface of the PVDF-BCP composite. Besides, the F EDS peak [characteristic of PVDF (C2H2F2)n] observed in the apparent layer grown on the surface of the PVDF polymer (Fig. 4c) indicated that it was only a piece of the own polymer that had broken in the grinding process used before the SBF immersion. Unfortunately, the overlap of EDS peaks originating from Au and P ions prevents the establishment of the atomic percentage of Ca and P, which help to specify the type of HA grown on the PVDF-BCP composite.

Figure 4:
SEM images of surfaces profile (top), fractured surfaces (middle), and EDS spectra of the surfaces for: (a,d,g) BCP ceramic; (b,e,h) PVDF-BCP composite; and (c,f,i) PVDF polymer.
Figura 4:
Micrografias obtidas por microscopia eletrônica de varredura do perfil de superfícies, das superfícies de fratura e espectros de EDS das superfícies de: (a,d,g) cerâmica BCP; (b,e,h) compósito PVDF-BCP; e (c,f,i) polímero PVDF.

In summary, a PVDF-BCP biocomposite, with elevated bioactivity and mechanical properties close to that of human bone tissue (both cortical and cancellous), was successfully obtained and characterized. The young osseous structural characteristics of the PVDF-BCP composite indicated its great potential for practical applications because this type of bone is highly bioactive. Furthermore, the overlapping with PVDF polymorphic phases can add multifunctional characteristics to this composite 3030. C. Ribeiro, J. Parssinen, V. Sencadas, V. Correia, S. Miettinen, V.P. Hytonen, S.L. Mendez, J. Biomed. Mater. Res. A 103 (2015) 2172.. In addition, different thermal and mechanical properties of the BCP ceramic and PVDF polymer can be tuned to obtain a biocomposite with a wide range of properties. In this way, the PVDF-BCP biocomposite can be potentially applied as an osseous implant in different parts of the animal/human body. The potential to explore the piezoelectric properties of the PVDF matrix on the PVDF-BCP composite, focusing to activate and change the kinetics of the healing process in the implanted prosthesis, can expand the multifunctional characteristics of this composite 3030. C. Ribeiro, J. Parssinen, V. Sencadas, V. Correia, S. Miettinen, V.P. Hytonen, S.L. Mendez, J. Biomed. Mater. Res. A 103 (2015) 2172.. In fact, these properties can be used in the future to activate the healing process by promoting the ion exchange on the surfaces of the bioactive material 4747. H.S. Nalwa, Ed., Ferroelectric polymer: chemistry, physics and applications, Hitachi, lbaraki (1995).. This methodology can be employed in future physiotherapeutic treatments to accelerate the complete restoration of damaged bone tissues. Finally, and considering the possibilities for the improvement of the thermal, piezoelectric and mechanical properties, as well as the biocompatible characteristics and even that the structure of the PVDF-BCP composite is very similar to that of the highly regenerating young bone, it is plausible to intuit the possibilities for multifunctional practical applications for these composites.

CONCLUSIONS

A bioactive PVDF-BCP composite was synthesized and its structural microstructural and mechanical properties, as well as its bioactivity, were studied. The PVDF-BCP composite proved to be a highly bioactive material because a thick apatite layer (~9 μm) was observed on its surface after just 7 days under immersion in simulated body fluid. Mechanical tests revealed a strong composite with properties similar to the human bone, with a strength reaching 80 MPa. In fact, piezoelectrically bioactive PVDF-BCP composites can be potentially used in the future physiotherapeutic process, in which electric field would be used to reorganize electric ions on the bioactive surface of the composite and accelerate the healing process. Nevertheless, the wide range of properties that are possible to be obtained in this family of materials enhances their use in osseous implants for different parts of the animal/human body.

ACKNOWLEDGEMENTS

The authors would like to thank the Brazilian agencies CNPq (proc. 474554/2013-9, 308622/2013-8 and 446565/2014-8), CAPES (PVE 88881.030465/2013-01, PROCAD 88881.068509/2014-01) and Fundação ARAUCÁRIA de Apoio ao Desenvolvimento Cientifico e Tecnológico do Paraná for financial support. Special thanks to LME/LNNano/CNPEM (Campinas-Brazil) for the technical assistance for the electron microscopy work.

REFERENCES

  • 1
    B.D. Ratner, A.S. Hoffman, F.J. Schoen, J.E. Lemons, Biomaterials science: an introduction to materials in medicine, Academy Press, New York (1996).
  • 2
    A.P.V. Pereira, W.L. Vasconcelos, R.L. Oréfice, Polímeros 9 (1999) 104.
  • 3
    M.I. Kay, R.A. Young, A.S. Posner, Nature 204 (1964) 1050.
  • 4
    R.L. Oréfice, Biomateriais: fundamentos e aplicações, Cultura Médica, Rio de Janeiro (2006).
  • 5
    S. Pollick, E.C. Shors, R.E. Holmes, R.A. Kraut, J. Oral Maxillofac. Surg. 53 (1995) 915.
  • 6
    I. Ono, T. Tateshita, T. Nakajima, Biomaterials 21 (2000) 143.
  • 7
    R.Z. Legeros, Clin. Orthop. Relat. Res. 395 (2002) 81.
  • 8
    P. Li, K.D.E. Groot, T. Kokubo, J. Sol-Gel Sci. Technol. 7 (1996) 27.
  • 9
    W. Cao, L.L. Hench, Ceram. Int. 22 (1996) 493.
  • 10
    N. Specchia, A. Pagnotta, M. Cappella, A. Tampieri, F. Greco, J. Mater. Sci. 37 (2002) 577.
  • 11
    J. Venugopal, P. Vadgama, T.S.S. Kumar, S. Ramakrishna, Nanotechnology 18 (2007) 1.
  • 12
    T.M. Coelho, E.S. Nogueira, A. Steimacher, A.N. Medina, W.R. Weinand, W.M. Lima, M.L. Baesso, A.C. Bento, J. Appl. Phys. 100 (2006) 094312.
  • 13
    C. Gao, B. Yang, H. Hu, J. Liu, C. Shuai, S. Peng, Mater. Sci. Eng. C 33 (2013) 3802.
  • 14
    Y. Tanimoto, Y. Shibata, A. Murakami, T. Miyazaki, N. Nishiyama, J. Hard Tissue Biol. 18 (2009) 2.
  • 15
    S. Raynaud, E. Champion, J.P. Lafon, D. Bernache-Assollant, Biomaterials 23 (2002) 1081.
  • 16
    M. Kohri, K. Miki, D.E. Waite, H. Nakajima, T. Okabe, Biomaterials 14 (1993) 299.
  • 17
    A.D.B.L. Ferreira, P.R.O. Nóvoa, A.T. Marques, Compos. Struct. 151 (2016) 3.
  • 18
    T.G.M. Bonadio, V.F. Freitas, T.T. Tominaga, R.Y. Miyahara, J.M. Rosso, L.F. Cótica, M.L. Baesso, W.R. Weinand, I.A. Santos, R. Guo, A.S. Bhalla, Curr. Appl. Phys. 17 (2017) 767.
  • 19
    F.R. Baxter, C.R. Bowen, I.G. Turner, A.C.E. Dent, Ann. Biomed. Eng. 38 (2010) 2079.
  • 20
    K. Yamashita, N. Oikawa, T. Umegaki, Chem. Mater. 8 (1996) 2697.
  • 21
    K.S. Hwang, J.E. Song, J.W. Jo, H.S. Yang, Y.J. Park, J.L. Ong, H.R. Hawls, J. Mater. Sci. Med. 13 (2002) 133.
  • 22
    M.P. Mahabole, R.C. Aiyer, C.R. Ramakrishna, B. Sheedhar, R.S. Khairnar, Bull. Mater. Sci. 28 (2005) 535.
  • 23
    J. Feng, H.P. Yuan, X.D. Zhang, Biomaterials 18 (1997) 1531.
  • 24
    M.M. Beloti, P.T. Oliveira, R. Gimenes, M.A. Zaghete, M.J. Bertolini, A.L. Rosa, J. Biomed. Mater. Res. 79 (2006) 282.
  • 25
    J.E. Davies, Surface characterization of biomaterials, Elsevier, Amsterdam (1988).
  • 26
    D.M. Correia, R. Gonçalves, C. Ribeiro, V. Sencadas, G. Botelho, J.L.G. Ribelles, S.L. Mendez, RSC Adv. 4 (2014) 33013.
  • 27
    D.M. Correia, C. Ribeiro, V. Sencadas, L. Vikingsson, M.O. Gasch, J.L.G. Ribelles, G. Botelho, S.L. Mendez, Colloids Surf. B Biointerfaces 140 (2016) 430.
  • 28
    C. Ribeiro, S. Moreira, V. Correia, V. Sencadas, J.G. Rocha, F.M. Gama, J.L.G. Ribelles, S.L. Mendez, RSC Adv. 2 (2012) 11504.
  • 29
    J. Parssinen, H. Hammaren, R. Rahikainen, V. Sencadas, C. Ribeiro, S. Vanhatupa, S. Miettinen, S.L. Mendez, V.P. Hytonen, J. Biomed. Mater. Res. A 103 (2015) 919.
  • 30
    C. Ribeiro, J. Parssinen, V. Sencadas, V. Correia, S. Miettinen, V.P. Hytonen, S.L. Mendez, J. Biomed. Mater. Res. A 103 (2015) 2172.
  • 31
    Y. Yu, H. Sun, H. Orbay, F. Chen, C.G. England, W. Cai, X. Wang, Nano Energy 27 (2016) 275.
  • 32
    A.A. Ribeiro, L.G. Vaz, A.C. Guastaldi, J.S.C. Campos, Appl. Surf. Sci. 258 (2012) 10110.
  • 33
    H. Kawaii, Jap. J. Appl. Phys. 8 (1969) 975.
  • 34
    C. Constantino, A. Job, R. Simões, J. Giacometti, V. Zucolotto, O. Oliveira, J. Gozzi, D. Chinaglia, Appl. Spectrosc. 59 (2005) 275.
  • 35
    H.M. Kim, F. Miyaji, T. Kokubo, C. Ohtsuki, T. Nakamura, J. Am. Ceram. Soc. 78 (1995) 2405.
  • 36
    Y. Abe, M. Kawashita, T. Kokubo, T. Nakamura, J. Ceram. Soc. Jpn. 109 (2001) 106.
  • 37
    Am. Soc. Test. Mater., ASTM C773-88: “Standard test method for compressive (crushing) strength of fired whiteware materials”, B. Stand. (2011).
  • 38
    Am. Soc. Test. Mater., ASTM E1876-09: “Standard test method for dynamic Young’s modulus, shear modulus, and Poisson’s ratio by impulse excitation of vibration”, B. Stand. (2012).
  • 39
    E.S.S. Yousef, J. Phys. D Appl. Phys. 38 (2005) 3970.
  • 40
    J.A. Sampaio, M.L. Baesso, S. Gama, A.A. Coelho, J.A. Eiras, I.A. Santos, J. Non-Cryst. Solids 304 (2002) 293.
  • 41
    T.H. Lee, F.Y.C. Boey, K.A. Khor, Polym. Compos. 16 (1995) 481-488.
  • 42
    S.C. Cowin, Bone mechanics handbook, 2nd Ed., CRC Press, New York (2001).
  • 43
    S. Pal, Design of artificial human joints & organs, Spring, New York (2014).
  • 44
    W.R. Weinand, A.C. Bento, M.L. Baesso, W.M. Lima, J. Appl. Phys. 104 (2008) 2.
  • 45
    G. Ciobanua, S. Ilisei, C. Lucaa, G. Carjaa, O. Ciobanub, Prog. Org. Coat. 74 (2012) 648.
  • 46
    A. Takeuchi, C. Ohtsuki, T. Miyazaki, M. Kamitakahara, S.-I. Ogata, M. Yamazaki, Y. Furutani, H. Kinoshita, M. Tanihara, J. R. Soc. Interface 2 (2005) 373.
  • 47
    H.S. Nalwa, Ed., Ferroelectric polymer: chemistry, physics and applications, Hitachi, lbaraki (1995).

Publication Dates

  • Publication in this collection
    Jul-Sep 2018

History

  • Received
    21 July 2017
  • Reviewed
    29 Dec 2017
  • Accepted
    14 Jan 2018
Associação Brasileira de Cerâmica Av. Prof. Almeida Prado, 532 - IPT - Prédio 36 - 2º Andar - Sala 03 , Cidade Universitária - 05508-901 - São Paulo/SP -Brazil, Tel./Fax: +55 (11) 3768-7101 / +55 (11) 3768-4284 - São Paulo - SP - Brazil
E-mail: ceramica.journal@abceram.org.br