Abstract
The aim of this investigation was to characterize three samples of kaolin (DD1, DD2 and DD3) collected from Djebel Debbagh deposit (East of Algeria) to be used in electrical porcelain insulators. Grain-size analysis, X-ray fluorescence, X-ray diffraction, scanning electron microscopy and thermal analysis (TG-DTA) were performed. Each sample was mixed with feldspar and silica to obtain three porcelain formulations. The obtained results indicated that the three kaolins were composed by kaolinite and halloysite with variable contents of MnO and Fe2O3 as associated impurities. It was found that the DD1 was the appropriate kaolin as raw material for making the high-voltage electrical insulator which had the highest electrical and mechanical properties (dielectric strength, bending strength and bulk density), while DD2 and DD3 were less suitable due to their lower properties caused by the presence of impurities which must be removed.
Keywords:
Djebel Debbagh kaolin; electrical insulators; dielectric strength; bending strength