Yellow Mombin (Spondias mombin L.) Seeds from Agro-Industrial Waste as a Novel Adsorbent for Removal of Hexavalent Chromium from Aqueous Solutions

Abstract

The objective of this study was to develop a low-cost and eco-friendly adsorbent from agro-industrial waste for the removal of hexavalent chromium in the aqueous medium. The adsorbent (BMC) produced from yellow mombin (Spondias mombin L.) seeds was characterized by the determination of the chemical composition, thermal analysis (thermogravimetric (TG) analysis and differential thermal analysis (DTA)), Fourier transform infrared spectroscopy (FTIR), pH in suspension and determination of the point of zero charge (PZC). The presence of proteins, fats and carbohydrates (15.690, 1.004, and 73.706%, respectively) suggests that the material can be a promising adsorbent, given the availability of functional groups. The following conditions were set: pH 2.0, adsorbent mass 450 mg, and equilibrium was reached after 80 min. The maximum adsorption capacity was approximately 98%. Kinetic studies showed that the pseudo-second-order kinetic equation was the one that best adjusted to the experimental data. Under the conditions investigated, the Langmuir isotherm model described the best balance data, signaling the adsorption in monolayer. According to the results, it was found that the BMC showed an outstanding performance for the removal of Cr^VI ions and may become a viable and efficient alternative for the treatment of industrial effluents containing trace elements.

Keywords:
biomass; agro-industrial waste; adsorbent; trace elements

Introduction

The pollution of water resources is a serious environmental problem associated with increased industrial and agricultural activity. Such activities generate toxic compounds of various classes and in large quantities which, in many cases, are inappropriately discarded in the environment.^1,2 Various industrial processes developed in the sectors of mining, fertilizers, fuel production, paint, pigments, metal plating, tanning, paper, pulp, leather, electroplating, textiles and chemicals, can cause negative environmental impacts when by-products and effluents from their processes are improperly disposed, especially in wastewaters.^1-4

Trace elements present in their chemical processes such as lead, copper, nickel, arsenic and chromium present high toxicity and bioaccumulation, and can pose incalculable risks to human health, as well as intensify environmental problems through the deterioration of fauna and flora.^3,5,6 Several diseases and physiological disorders are reported in the literature^3,7-12 by the dissemination of these elements.

Due to its toxicity, chromium is considered one of the most toxic metals and is on the priority pollutant list, as defined by the US Environmental Protection Agency (EPA), which establishes a maximum limit of total chromium in drinking water of 50 µg L^-1,¹³ as a function of its mutagenic and carcinogenic properties.^7,11 Chromium toxicity depends on the valence state. In aqueous solutions, chromium occurs more frequently as Cr^III and Cr^VI.¹⁴ Chromium(VI) has significantly higher toxicity levels than other valence states¹⁵ due to its high mobility and water solubility,¹⁰ in addition to being easily absorbed by the body.¹⁶ The chemistry of Cr^VI is very dependent on pH. Table 1 reports the predominant species at each pH range.⁹

Table 1
Composition of the Cr^VI solution as a function of pH

pH	Predominant species
< 1	H2CrO4 (chromic acid)
2-4	Cr2O72- (dichromate)
4-6	HCrO4- (hydrogen chromate), Cr2O72- (dichromate)
6-8	Cr2O72- (dichromate), CrO42- (chromate)
> 8	CrO42- (chromate)

Several conventional methodologies are frequently used to treat areas contaminated with trace elements: chemical and electrochemical precipitation,^17-20 chemical oxidation and reduction,^19,21 filtration,^19,21 ion exchange,^18,19,21,22 electrochemical treatment,^17,19 reverse osmosis²² and flotation.¹⁸ However, these methods have demonstrated several disadvantages that make their use in large scale unfeasible. Among the main drawbacks are the incomplete metal removal, sensitive operating conditions, low efficiency, culminating in the generation of toxic waste or other products that require treatment.^1,19 The adsorption process is considered promising for the removal of heavy metals from aqueous solutions using different adsorbent materials, as it has important advantages, such as high efficiency, low cost, minimization of chemical and biological sludge, no additional nutrient required, regeneration of the adsorbent and possibility of metal recovery.^4,23

The adsorption process is a phenomenon that mainly involves the use of surface forces. Alternatively, it can be defined as any division of chemical species between the primary phase and an interface or the accumulation of substances near the interface.²⁴ Agro-industrial waste has aroused considerable interest, once they consist of lignin, cellulose, hemicellulose, lipids, proteins, sugars, water, lignocellulosic substrate and many other compounds possessing a great variety of functional groups,^11,25-27 and these residues are the most abundant lignocellulosic raw materials in nature.²⁸ A variety of agricultural residues have already been evaluated in heavy metal adsorption processes, such as Cd^II, Cu^II, Cr^III, Cr^VI, Pb^II, Hg^II, Zn^II, etc., showing good performance.^1,29-33

The proposal of this study was to use yellow mombin (Spondias mombin L.) seeds, from the fruit processing in the agroindustry, to produce a new adsorbent and to apply it in the removal of hexavalent chromium in an aqueous medium. The processing of these fruits to produce pulp, juice, sweets and other products, generates high amounts of waste, formed mainly by seeds, which are normally discarded in the environment without any treatment. The use of these residues to produce natural adsorbent, without any chemical or physical treatment that requires financial investment, will add value to the waste and reduce the environmental impacts caused by inadequate disposal, in addition to contributing to the treatment of wastewater contaminated with trace elements.

Experimental

Material and methods

A 1000 mg L^-1 Cr^VI standard solution (Sigma-Aldrich, St. Louis, USA) was used for the preparation of all chromium solutions used in the experiments. All procedures were performed at room temperature (27 ± 2 ºC). The pH of the solution was adjusted with solutions of NaOH (PA, Vetec, Rio de Janeiro, Brazil) and HCl (37%, Synth, São Paulo, SP, Brazil), both at a concentration of 0.1 mol L^-1 and, for comparison, the most significant points in the pH study were repeated by adjusting with 1.0 mol L^-1 KCl (Synth, São Paulo, SP, Brazil)/HCl solution.

Obtention and characterization of the adsorbent

The yellow mombin fruit waste was supplied by a pulp company located in the southwest region of Bahia, Brazil. The fruit residue includes seeds and shell. The shells and pulp fragments were discarded. The still moist residues were taken to the laboratory and then washed with deionized water to separate the seeds and dried at the sun, then sieved for complete removal of pulp residues.

After the previous step, the material was dried in a stove (Marconi, model MA 120, São Paulo, SP, Brazil) with air circulation for 24 h and ground in a 2-mm knife mill. For the adsorption tests, the residue was sieved to obtain a smaller particle size, using an 18-mesh standard screen. The acronym BMC used in the text refers to the term “biosorbent from yellow mombin fruit seeds”.

The BMC was characterized by several techniques, such as: determination of the chemical composition,^34,35 obtaining spectra by Fourier transform infrared (FTIR) spectroscopy in the range of 4000 to 450 cm^-1 using a spectrometer (PerkinElmer, Spectrum UATR TWO, Massachusetts, USA) and obtaining thermogravimetric (TG, Shimadzu, TGA-50, Kyoto, Japan) and differential thermal analysis (DTA, Shimadzu, Thermobalance DTG 60-A, Kyoto, Japan) curves from 25 to 1000 ºC. The point of zero charge (PZC) was measured using the methodology called “11 point experiment”³⁶ and the suspended pH of BMC was determined following the literature.³⁷

Determination of the adsorption capacity of BMC

The adsorption experiments were performed in triplicate to estimate the BMC adsorption capacity and the errors of the experimental measurements were evaluated by the standard deviation calculation. Thus, appropriate masses of the BMC were weighed directly into 50 mL test tubes, and 25 mL of the Cr^VI solution at a concentration of 50 mg L^-1 with pre-adjusted pH was then added to the respective tubes. All tubes were brought to a shaker at room temperature. The adsorption capacity of the biosorbent, Q_e (mg of metal per g of BMC) was determined using equation 1:³⁸

(1) $Q_e=\frac{\left(C_o-C_e\right)}{m}V$

where, C_o and C_e (mg L^-1) are the initial and final concentrations of the Cr^VI solution, respectively; m (g) is the amount of adsorbent, and V (L) is the volume of the Cr^VI solution. The capacity of Cr^VI removal by the adsorbent can also be expressed in terms of percentage, according to equation 2:^11,39

(2) $\mathrm{Removal}\left(\%\right)=\frac{\left(C_o-C_e\right)}{C_o}\times 100$

The quantification of Cr^VI in the supernatant solution was performed by using a flame atomic absorption spectrometer (PerkinElmer, AAnalyst 200, Massachusetts, USA).

Adsorption tests: optimization of experimental parameters

Effect of adsorbent mass on the adsorption of Cr^VI

The study of adsorbent mass was carried out through the addition of different quantities of BMC. The following masses were investigated: 0.0500; 0.1000; 0.2000; 0.3000; 0.4000; 0.5000; 0.6000 and 0.7000 g. Thus, the respective masses were weighed on an analytical balance directly into the test tubes, and 25 mL of the 50 mg L^-1 metal solution was then added. The pH of the solution was adjusted to 2.44 by the addition of small amounts of NaOH and HCl, both at a concentration of 0.1 mol L^-1. Subsequently, the tubes were agitated in an orbital table and the solution was in contact with the adsorbents for 1 h. After this time, the solutions were filtered and immediately quantified for the concentration of chromium in the supernatant solution by flame atomic absorption spectrometry (FAAS).

Effect of pH on Cr^VI adsorption

From the mass that resulted in the best adsorption results in the previous step, the assays were repeated by varying the pH of the solution, monitoring with the aid of a digital pHmeter (Quimis, G 400 AS, São Paulo, SP, Brazil). The pH was adjusted with the NaOH and HCl solutions described above. The investigated pH values were: 1.0; 1.5; 2.0; 3.0; 4.0; 6.0; 7.0; 8.0 and 10. At each pH, the solution remained in contact with the BMC for 1 h, and measurements were then made by FAAS to observe the adsorbed mass at each step of the analysis. For comparison purposes, the most important pH values for the study (1.5, 2.0, and 3.0) were repeated with the adjustment with 1.0 mol L^-1 KCl/HCl solution.

Adsorption studies

After the optimization of the previous parameters, the time necessary to reach the adsorption equilibrium was also investigated. The solutions containing the adsorbents remained under stirring at room temperature in periods of 10; 20; 30; 40; 60; 80; 100; 120; 140; 160 and 180 min. At each time interval, measurements were performed by FAAS. The purpose of this study was to determine the time required for the two phases (adsorbent/adsorbate) to reach equilibrium.

The kinetic data were fitted to the following non-linear kinetic models: pseudo-first-order, pseudo-second-order, and Elovich, according to the equations described in Table 2.

Table 2
Some adsorption kinetic models

Name	Model	Linear form	Reference
Lagergren pseudo first-order model	$\frac{\mathrm{dQ}}{\mathrm{dt}}=K_1\left(Q_e-Q_t\right)$	$\log \left(Q_e-Q_t\right)=\log Q_e-\frac{K_1}{2,303}t$	40
Pseudo-second order model	$\frac{{\mathrm{dQ}}_t}{\mathrm{dt}}=K_2{\left(Q_e-Q_t\right)}^2$	$\frac{t}{Q_t}=\frac{1}{K_2{Q}_e^2}+\frac{t}{Q_e}$	41
Elovich	$\frac{{\mathrm{dQ}}_t}{\mathrm{dt}}=\alpha \exp \left(-\beta q_t\right)$	$q_t=\beta \ln \left(\alpha \beta \right)+\beta \ln t$	42

• Q_e and Q_t: adsorption capacities at equilibrium and at time t, respectively; K₁: pseudo-first-order adsorption rate constant; K₂: pseudo-second-order adsorption rate constant; q_t: adsorbed amount at time t; α and β: constants during an experiment.

The adsorption isotherm is essential to understand how the adsorbent interacts with the adsorbate, not only to give an idea of its adsorption capacity, but also playing a vital role in understanding the adsorption mechanism. The isotherms were adjusted using the Langmuir, Freundlich, and Redlich-Peterson nonlinear models, which are described in Table 3.

Table 3
Different isotherm models

Name	Model	Linear form	Reference
Langmuir	$q_e=\frac{Q^{o}b{C}_e}{1+b{C}_e}$	$\frac{C_e}{q_e}=\frac{1}{Q^{o}b}+\frac{1}{Q^o}{C}_e$	43
Freundlich	$q_e=K_{F}C_e{}^{1/n}$	$\log q_{\mathit{e}}=\log K_F+\frac{1}{n}\log C_e$
Redlich-Peterson	$q_e=\frac{K_R{C}_e}{1+a_R{C}_e^g}$	$\log \left(k_R\frac{C_e}{q_e}-1\right)=\log \left(a_R\right)+\alpha \log \left(C_e\right)$

• q_e: amount of solute adsorbed per unit mass of the adsorbent; C_e: equilibrium concentration of the adsorbate; Q^o: adsorption capacity of the monolayer; b: constant related to the free energy of adsorption; K_F: Freundlich isotherm constant; K_R and a_R: Redlich-Peterson isotherm constants; α: Redlich-Peterson isotherm exponent; n: constant indicative of the intensity of adsorption.

Adjustments to mathematical models for both kinetic studies and equilibrium data were assessed statistically by correlation coefficient (R²) and (χ²) Chi-square statistic test; the error functions sum of squared errors (SSE); average relative error (ARE) and hybrid fractional error function (HYBRID) were considered for adsorption isotherms.²⁷

Effect of the initial concentration of the metal solution

The concentration of the initial metal solution was also determined. Thus, 25 mL of the Cr^VI solution at pH 2.0 were added to the mass adopted at the following concentrations: 10; 20; 50; 80; 100; 150; 200; 250 and 350 mg L^-1. The time the BMC came into contact with the solution was obtained in the previous procedure.

Results and Discussion

Characterization of BMC

Chemical composition

According to the chemical composition results, humidity and ash contents were found to be low (9.150 and 0.450%, respectively). The presence of proteins, fats and carbohydrates (15.690, 1.004, and 73.706%, respectively) suggests that the material may be a suitable adsorbent, considering the availability of critical functional groups such as carboxylates and hydroxyls. These functional groups can cause weak van der Waals interparticle bonds between the Cr^VI solution species and the adsorbent.

Fourier transform infrared spectroscopy (FTIR)

The FTIR spectrum obtained for the BMC before and after the metal adsorption process is shown in Figure 1.

Figure 1
FTIR spectra before and after Cr^VI biosorption.

The FTIR spectrum before the process was essential to identify the major functional groups present on the surface of the biomass. A broad band centered around 3300 cm^-1 can be assigned to stretches of the OH (alcohol, phenol and carboxylic acid) bond due to inter- and intramolecular interactions, as a consequence of deformations of hydrogen bonds and/or NH stretches and the presence of amino groups,^7,10,18 in view of the presence of proteins in the chemical composition of BMC. This band can also be assigned to the intermolecular stretches of O-H bonds from the cellulosic component present in the biomass.⁴⁴ Low-intensity bands around 2915 cm^-1 were also observed, which may indicate the presence of C-H stretch of the CH₂ group relative to the lipid component of the sample, in addition to being an indicative of the presence of lignin. The band appearing at 1617 cm^-1 is characteristic of vibrational carbonyl stretches (stretching of C=O in COO-).^22,45 In the case of the study sample, it is possible that the said band refers to the stretching vibrations of the C=O bond of carbonyl, which is part of the structure of the proteins and fatty acids of the lipid fraction. It is possible to observe the presence of low intensity bands in the region 1430-1360 cm^-1, which is an indication of the presence of angular deformation in the plane of the O-H bond. Therefore, the presence of phenol is represented by the near 1370 cm^-1 band that can be related to Ar(OH).^22,46 The band at 1370 cm^-1 can be assigned to the presence of CH bonds in cellulose and hemicellulose.⁴⁴ The absorptions at 1260 and 1230 cm^-1 can be assigned to the C–O stretch of phenol.⁴⁶ The relatively broad band appearing at 1030 cm^-1 can be assigned to the stretching of the C–O bond of alcoholic groups.^47,48 It can also be assigned to the presence of stretches of C–O bond in lignocellulosic compounds.⁴⁴ Not only does this band justify the high total carbohydrate content, evidenced in the chemical composition, but also the presence of lignin in the biomass. Considering the vibrational modes of the –OH, -COOH and –NH₂ groups, it is possible to suggest that Cr^VI can be adsorbed through electrostatic attractions.

The FTIR spectrum of the BMC obtained after the chromium adsorption process, evidenced that the leading bands are preserved. However, some perturbations, such as the decrease in transmittance and change in wavenumber were perceived. These perturbations can be attributed to the interaction of the metal with the adsorbent. A close analysis of the two spectra allows to verify that the bands around 3300, 1620 and 1030 cm^-1 in the biomass after the adsorption had a decrease in transmittance, concerning the biomass before adsorption. The band at 3344 cm^-1 shifted to a lower frequency (3339 cm^-1), while the band at 1617 cm^-1 shifted to a higher frequency (1634 cm^-1). Similar results have been reported in previous studies,^48-52 in which changes in vibrational frequencies, decrease and banding were verified. These changes are an evidence of Cr^VI adsorption in aqueous media through functional groups present in the biomass structure.

Thermal analysis: thermogravimetric (TG) analysis and differential thermal analysis

According to the TG result, it was possible to verify that the BMC exhibited three stages of mass loss. The first stage occurred at a temperature of 100 to 150 ºC and may be assigned to water loss. This result is consistent with the biomass moisture content of 9.150%. The second stage of mass loss was observed in the 220-380 ºC range and can be assigned to the decomposition of the organic extractives present in the biomass. The third stage of decomposition occurred between 380 and 600 ºC. This third mass loss event can be associated with the thermal degradation of cellulose, hemicellulose, and lignin, leading to the production of coal. Above 650 ºC, the mass loss curve did not exhibit any other thermal events, indicating the thermal stability of the carbonaceous structure formed.

The DTA curve showed a discrete endothermic peak around 80 ºC, confirming the exit of water signaled by the mass loss in the TG curve. This behavior confirms the low humidity of the BMC. An endothermic peak around 350-380 ºC was also observed, which can be assigned to the release of volatiles from the decomposition of organic compounds. There was also a weak exothermic peak at 450 ºC and a sharp exothermic peak at 500 ºC, which may be associated with the combustion of cellulose, hemicellulose and lignin.

Point of zero charge (PZC) and suspended pH

The results obtained for PZC and suspended pH indicate that BMC has a pH close to neutrality, considering that these results were approximately 6.50. In the case of PZC, this data indicates that when the solution is maintained at pH lower than the zero charge pH (pH_PZC) of the biomass, the protonation of specific functional groups occurs, and the biomass behaves like a positively charged matrix, attracting negatively charged ions present in solution.²⁵ On the other hand, when the pH value of the solution increases and the pH is higher than pH_PZC, the surface charge of the adsorbent is negative, and cation binding is favored,⁷ since there is deprotonation of active functional groups on the biomass surface.

Adsorption studies

Mass of BMC

The result for the effect of the mass of BMC on Cr^VI adsorption is shown in Figure 2.

Figure 2
Adsorption of Cr^VI on BMC as a function of adsorbent dosage (298 K, initial pH = 2.5).

From the results of the mass study, it was possible to verify that Cr^VI removal has a sharp increase up to 0.30 when it reaches about 80% removal. After this point, adsorption capacity does not vary significantly, reaching equilibrium. With the lowest mass, the number of active sites available for the interaction between adsorbate and adsorbent is small, which explains the low removal of the metal. By increasing the mass of the BMC, the availability of active sites also increases, thus yielding better efficiency in the adsorption process.^9,10,52

The maximum adsorption point of Cr^VI, approximately 85%, was reached with a mass of approximately 0.4000 g, indicating that the metal occupied the available sites in the biomass structure. For later studies, the adopted mass was 0.4500 g, considering that, from this point, the system reached equilibrium and there was no significant increase in metal removal.

Effect of pH on Cr^VI adsorption

One of the most critical parameters in the removal processes of metals present in an aqueous medium through adsorption is pH. The variation in pH can affect the characteristics and the availability of metallic ions in solution, as well as modify the chemical state of the functional groups responsible for the interactions.⁷ To better understand such behavior, it is essential to remember that Cr^VI chemistry is very pH-dependent and the HCrO₄^- ion is the main hexavalent chromium species present at low pH.²¹ Figure 3 shows the effect of pH on Cr^VI adsorption.

Figure 3
Effect of initial pH on the adsorption of Cr^VI.

It can be inferred from Figure 3 that the adsorption process in the system under study was favored at low pH, specifically between 1.5 and 2.0, where the maximum amount removed was 2.40 mg g^-1 (metal removal of approximately 90%). Above pH 2, a decline in removal efficiency was noted, with the amount removed below 1.40 mg g^-1. According to information reported in the literature,^{7,10,14,18,19} it was verified that the best pH value found in this study is in agreement with the results obtained by other researchers when using biomass for Cr^VI removal.

Considering the results of infrared spectroscopy (Figure 1), the presence of –OH, -COOH and NH₂ groups, which are considered as active sites,⁵² may be responsible for the electrostatic attraction of positive species in solution. On the other hand, at low pH, there is an excellent availability of H₃O⁺ ions in solution that protonate these groups and, therefore, the attraction of Cr^VI oxyanion (in aqueous solution, low pH and concentration lower than 500 mg L^-1, the HCrO₄^- ion predominates), is favored.⁵³ As pH increases, the protonation of the groups present on the surface of the biomass (forming electrophilic centers) is less intense, which explains the decrease in adsorption, as can be seen in Figure 3. Thus, adsorption is not favored in alkaline pH as a function of the repulsion between the metal species and the active functional groups of the biomass. Therefore, pH 2.0 was considered the best and was used for subsequent studies.

The result obtained for the pH effect ratifies the result of pH_PZC, which describes that, at pH values below 6.50, the protonation of specific functional groups occurs and biomass behaves as a positively charged matrix, attracting the negatively charged ions present in solution, which yielded the removal of Cr^VI species.

Adsorption kinetics and equilibrium

The adsorption kinetics of Cr^VI on BMC is shown in Figure 4, in which the effects of the nature of the adsorbent BMC and its adsorption metal capacity can be observed. The Cr^VI removal rate is 80% in the first 10 min of adsorption at the most readily available active sites on the surface of the adsorbent,⁵³ but equilibrium is reached after 80 min, suggesting the existence of active sites on the inner surface of the BMC.^17,18

Figure 4
Nonlinear fit of Cr^VI adsorption data on BMC adsorbent (mass = 0.45 g, initial pH = 2.0).

The kinetic data were fitted to the non-linear kinetic models of pseudo-first order, pseudo-second order, and Elovich. The results are presented in Figure 4 and Table 4.

Table 4
Kinetic parameters for Cr^VI adsorption on BMC using different models

Kinetic model	Parameter	BMCa
Pseudo-first order	qm / (mg g-1)	2.46
	KS1 / min-1	0.237
	R2	0.495
	χ2	0.0043
Pseudo-second order	qm / (mg g-1)	2.52
	KS2 / (g mg-1 min-1)	0.289
	R2	0.897
	χ2	8.73 × 10-4
Elovich	a / (mg g-1 min-1)	8.54 × 107
	b / (g mg-1)	10.10
	R2	0.962
	χ2	3.20 × 10-4

• ^a
  Adsorbent from the yellow mombin seeds. q_m: maximum sorption capacity of the biosorbent; K_S1: Lagergren rate constant of the first sorption; K_S2: adsorption rate constant; R²: coefficient of determination; χ²: Chi-square statistic test for determination of a non-linear model; a and b: initial sorption rate and desorption constant, respectively.

According to Table 4, R² values suggest that the data were better suited to the pseudo-second-order models (R² = 0.897) and the Elovich model (R² = 0.962). When the function χ² was used as a measure of comparison, the result indicates that the Elovich model better describes Cr^VI adsorption on BMC. In fact, the constants a and b represent a suitable combination involving valence forces through the sharing or exchange of electrons between the adsorbent and the adsorbate, suggesting chemisorption as the predominant mechanism, in addition to the Elovich model being considered adequate to describe the adsorption process on heterogeneous surfaces.⁵⁴ Similar results were found in the literature.^19,55,56

The adsorption isotherms were adjusted using the Langmuir, Freundlich, and Redlich-Peterson non-linear models (Figure 5), and the parameters are shown in Table 3. It can be observed that, regardless of the number of isothermal parameters, the data were well adjusted for all three models. This result confirms that the Langmuir, Freundlich, and Redlich-Peterson models are relevant to describe the equilibrium established between Cr^VI adsorbed ions and Cr^VI ions remaining in solution.²¹

Figure 5
Adsorption isotherms of Cr^VI on BMC and adjustments using Langmuir, Freundlich, and Redlich-Peterson models.

When the correlation factors R² and values of χ² are compared between the three models, they are very close, as shown in Table 5 (R² = 0.983 for Langmuir, R² = 0.985 for the Freundlich model and R² = 0.984 for Redlich-Peterson), indicating that any of the models can be used to describe chromium(VI) adsorption through BMC. In an attempt to define more precisely which of the models best fits the equilibrium data, the error functions sum of squared errors (SSE); average relative error (ARE) and hybrid fractional error function (HYBRID) were used, as can be observed in Table 6.

Table 5
Langmuir, Freundlich, and Redlich-Peterson isotherm parameters in the Cr^VI adsorption by using BMC

Isotherm	Parameter	Value
Langmuir	qm / (mg g-1)	30.543
	KL / (L mg-1)	0.008
	R2	0.983
	χ2	0.349
Freundlich	KF / (mg g-1) (L g-1)n	0.450
	n	1.338
	R2	0.985
	χ2	0.318
Redlich-Peterson	KR / (L g-1)	0.366
	aR / mg-1	0.149
	g	0.521
	R2	0.984
	χ2	0.333

• q_m: maximum sorption capacity of the adsorbent; K_L: Langmuir constant; K_F and n: Freundlich constant; K_R, g and a_R: Redlich-Peterson isotherm constants; R²: coefficient of determination; χ²: Chi-square statistic test for determination of a non-linear model.

Table 6
Comparison of isotherm models using error functions

Model	Error functions
	SSE	ARE	HYBRID
Langmuir	2.451	15.324	7.534
Freundlich	2.228	28.101	19.522
Redlich-Peterson	1.996	21.649	13.810

• SSE: sum of squared error; ARE: average relative error; HYBRID: hybrid fractional error function.

The values presented by the error functions ARE and HYBRID in Table 6 indicate that the equilibrium data fits the Langmuir model. The advantage of using these functions is in minimizing the fractional distribution of errors over the entire concentration range.²⁷ This result corroborates the FTIR results (Figure 1), which indicates the adsorption in specific sites, but does not exclude the occurrence of the chemisorption indicated by the Freundlich model, since the transport phenomena and chemical reactions occur simultaneously in real systems.⁵⁴

Study of the initial concentration of the metal solution

The performance of BMC in Cr^VI removal can also be evaluated as a function of the initial concentration of the solution containing the metal and the removal efficiency at the time of equilibrium (Figure 6).

Figure 6
Effect of initial concentration (condition: amount of adsorbent 0.45 g; pH 2.0; contact time 120 min).

The results show that the removal efficiency of the metal decreased significantly with the increase in the initial concentration of the solution, and 98% removal was achieved at a concentration of 10 mg L^-1 Cr^VI. As the saturation of the sites available for adsorption occurs, an increase in the adsorbed amount was observed but, naturally, the effect on the removal percentage is inverse.¹³ However, efficiency remains high, removal > 85%, even when the initial concentration reaches 100 mg L^-1. This means that, from the environmental point of view, the BMC is a promising alternative in the remediation of Cr^VI contaminated effluents. The same behavior was obtained by other researchers when using different natural adsorbents for metal adsorption.^9,13,57

Table 7 shows a summary of some studies used in the adsorption of chromium in aqueous solutions. These have been recently published not only on the use of natural adsorbent, but on activated carbon and chemically treated residues. In comparison with previous studies, the new adsorbent obtained in this research showed better results than some of the highlighted adsorbent materials, including some that received physical or chemical treatment. Considering the adsorbents with better results, it was observed that the BMC presented a similar performance, indicating that this material could become a promising low cost and eco-friendly alternative.

Table 7
Comparison of the adsorption capacity of some adsorbents for removal of chromium Cr^VI

Adsorbent	Pre-treatment	pH	time / min	Removal / %	Reference
Activated carbon-apple peels	concentrated phosphoric acid (85% H3PO4) in 2.7:1 ratio (H3PO4 volume (mL)/dried apple peels mass (g)) and activated in a muffle furnace maintained at 619 ºC for 56 min	2.0	120	95	58
Treated waste newspaper	concentrated sodium bicarbonate solution for removing foreign materials then refluxed with 5.0% Na2HPO4 using a water condenser for 3 h to impregnate the phosphate into the cellulose matrix	3.0	60	64	59
Immobilized Zea mays biomass	for immobilization procedure, Na-alginate (2%, m/v) was dissolved in hot water (60 ºC) and 1 g of corn cob powder was added and homogenized by agitation and extruded into 0.1 M CaCl2 solution	2.0	240	56	60
Modified groundnuthull	after appropriate washing and drying steps, portions of the groundnut hull were then modified with pyromellitic dianhydride (PMDA)	2.0	60	> 95	61
Biosorbent frommango leaves	the leave dust was washed with deionized water and the soluble colored components were then removed by washing repeatedly with hot deionized water (70 ºC ). Then, was then dried at 70 ºC for 24 h	2.0	120	91	62
Biosorbent from peppermint leaves	drying at room temperature away from sunlight, ground and then sieved to appropriate particle size	2.0	180	95	63
Almond green hull waste material	the sorbent was washed thoroughly several times with deionized water and was dried at room temperature for some daysthen, the dried sample was powdered and sieved	2.0	60	> 99	64
Mixed biosorbent (Pseudomonas stutzeri and acid treated Banyan tree bark)	the materials were rinsed, air-dried, ground into fine particles and then sulfuric acid was added in the ratio 1:2 and left undisturbed for 24 hthe materials were then heated up to 80 ºC for 30 min	2.0	45	95	12
Water caltrop shell	the material was rinsed with distilled water and was dried at 48 ºC in hot air oven for 48 hthen, the dried shells were ground to powder and sieved to obtain particles of different sizes	2.0	60	90	65
Biosorbent from yellow mombin seeds	after washing and drying steps in the sun, the material was dried in a stove with air circulation for 24 h and ground in a 2-mm opening knife mill	2.0	120	98	this study

Conclusions

The adsorbent BMC was obtained by a simple methodology using biomass of yellow mombin seeds from agro-industrial residues and it is efficient in the removal of hexavalent chromium in the aqueous medium. The material presented vibrational modes characteristic of functional groups –OH, -COOH and –NH₂, responsible for the electrostatic attraction of negative species when in acidic pH. BMC also showed values for PZC and suspended pH around 6.50. Such characteristics led to a 98% removal of the hexavalent chromium present in the solution. The studied system was kinetically modeled through the pseudo-first-order, pseudo-second order, and Elovich models. The kinetic data were better suited to the Elovich model used to describe the adsorption process on heterogeneous surfaces. The equilibrium data were adjusted to the Langmuir, Freundlich and Redlich-Peterson models and the results showed that the three models are relevant to describe the equilibrium established between Cr^VI adsorbed ions and Cr^VI ions remaining in solution. Rapid removal of adsorbate and reaching equilibrium in a short period of time, in addition to the fact that no physical or chemical treatment has been used, indicate that BMC can be a promising alternative for decontamination of aqueous systems. The outcomes from this research study indicated the solution to two environmental problems. On the one hand, the reuse an agro-industrial waste that would be discarded in the environment and, on the other hand, the production of a low-cost and eco-friendly adsorbent.

Supplementary Information

Supplementary information is available free of charge at http://jbcs.sbq.org.br as PDF file.

Acknowledgments

This study was financed in part by the Coordenação de Aperfeiçoamento de Pessoal de Nível Superior-Brasil (CAPES), finance code 001. The authors also acknowledge the financial support of the Conselho Nacional de Desenvolvimento Científico e Tecnológico (311419/2018-6) and the Financiadora de Estudos e Projetos (FINEP).

References

• ¹
  Burakov, A. E.; Galunin, E. V.; Burakova, I. V.; Kucherova, A. E.; Agarwal, S.; Tkachev, A. G.; Gupta, V. K.; Ecotoxicol. Environ. Saf. 2018, 148, 702.
• ²
  Saravanan, A.; Kumar, P. S.; Carolin, C. F.; Sivanesan, S.; J. Hazard., Toxic Radioact. Waste 2017, 21, 04017004.
• ³
  de Rossi, A.; Rigon, M. R.; Zaparoli, M.; Braido, R. D.; Colla, L. M.; Dotto, G. L.; Piccin, J. S.; Environ. Sci. Pollut. Res. 2018, 25, 19179.
• ⁴
  Saravanan, A.; Kumar, P. S.; Yaswanthraj, M.; Part. Sci. Technol. 2018, 36, 934.
• ⁵
  Carolin, C. F.; Kumar, P. S.; Saravanan, A.; Joshiba, G. J.; Naushad, M.; J. Environ. Chem. Eng. 2017, 5, 2782.
• ⁶
  Yaashikaa, P. R.; Kumar, P. S.; Varjani, S. J.; Saravanan, A.; Environ. Sci. Pollut. Res . 2019, 292, 122030.
• ⁷
  Blázquez, G.; Hernáinz, F.; Calero, M.; Martín-Lara, M. A.; Tenorio, G.; Chem. Eng. J. 2009, 148, 473.
• ⁸
  Bulut, Y.; Baysal, Z.; J. Environ. Manage. 2006, 78, 107.
• ⁹
  Javadian, H.; Ahmadi, M.; Ghiasvand, M.; Kahrizi, S.; Katal, R.; J. Taiwan Inst. Chem. Eng. 2013, 44, 977.
• ¹⁰
  Saha, R.; Mukherjee, K.; Saha, I.; Ghosh, A.; Ghosh, S. K.; Saha, B.; Res. Chem. Intermed. 2013, 39, 2245.
• ¹¹
  Wang, X. S.; Li, Z. Z.; Sun, C.; J. Hazard. Mater. 2008, 153, 1176.
• ¹²
  Yaashikaa, P.; Kumar, P. S.; Babu, V. M.; Durga, R. K.; Manivasagan, V.; Saranya, K.; Saravanan, A.; J. Mol. Liq. 2019, 276, 362.
• ¹³
  Nguyen, T. A.; Ngo, H. H.; Guo, W. S.; Zhang, J.; Liang, S.; Yue, Q. Y.; Li, Q.; Nguyen, T. V.; Bioresour. Technol. 2013, 148, 574.
• ¹⁴
  Dakiky, M.; Khamis, M.; Manassra, A.; Mer’eb, M.; Adv. Environ. Res. 2002, 6, 533.
• ¹⁵
  Sharma, D. C.; Forster, C. F.; Bioresour. Technol . 1995, 52, 261.
• ¹⁶
  Zhang, L.; Niu, W.; Sun, J.; Zhou, Q.; Chemosphere 2020, 248, 126102.
• ¹⁷
  Barakat, M. A.; Arabian J. Chem 2011, 4, 361.
• ¹⁸
  Chand, R.; Narimura, K.; Kawakita, H.; Ohto, K.; Watari, T.; Inoue, K.; J. Hazard. Mater . 2009, 163, 245.
• ¹⁹
  Demiral, H.; Demiral, İ.; Tümsek, F.; Karabacakoğlu, B.; Chem. Eng. J . 2008, 144, 188.
• ²⁰
  Dubey, S. P.; Gopal, K.; J. Hazard. Mater . 2007, 145, 465.
• ²¹
  Sun, Y.; Yue, Q.; Gao, B.; Gao, Y.; Li, Q.; Wang, Y.; Chem. Eng. J . 2013, 217, 240.
• ²²
  Varga, M.; Takács, M.; Záray, G.; Varga, I.; Microchem. J. 2013, 107, 25.
• ²³
  Sud, D.; Mahajan, G.; Kaur, M. P.; Bioresour. Technol . 2008, 99, 6017.
• ²⁴
  Bajpai, A.; Rajpoot, M.; J. Sci. Ind. Res. 1999, 58, 844.
• ²⁵
  Farooq, U.; Kozinski, J. A.; Khan, M. A.; Athar, M.; Bioresour. Technol . 2010, 101, 5043.
• ²⁶
  Liu, Z.; Zhou, X.; Chen, X.; Dai, C.; Zhang, J.; Zhang, Y.; J. Environ. Sci. 2013, 25, 2384.
• ²⁷
  Foo, K. Y.; Hameed, B. H.; Chem. Eng. J . 2010, 156, 2.
• ²⁸
  Castro, A. M.; Pereira Jr., N.; Quim. Nova 2010, 33, 181.
• ²⁹
  Gupta, V.; Carrott, P.; Singh, R.; Chaudhary, M.; Kushwaha, S.; Bioresour. Technol . 2016, 216, 1066.
• ³⁰
  Gupta, V. K.; Nayak, A.; Agarwal, S.; Gupta, V. K.; Nayak, A.; Agarwal, S.; Environ. Eng. Res. 2015, 20, 1.
• ³¹
  Hu, Z.; Srinivasan, M. P.; Microporous Mesoporous Mater 1999, 27, 11.
• ³²
  Lua, A. C.; Guo, J.; Colloids Surf., A 2001, 179, 151.
• ³³
  Tsai, W. T.; Chang, C. Y.; Lin, M. C.; Chien, S. F.; Sun, H. F.; Hsieh, M. F.; Chemosphere 2001, 45, 51.
• ³⁴
  Bligh, E. G.; Dyer, W. J.; Can. J. Biochem. Physiol. 1959, 37, 911.
• ³⁵
  Lutz, I. A.; Normas Analíticas: Métodos Físico-Químicos para Análise de Alimentos; Instituto Adolfo Lutz: São Paulo, 2004.
• ³⁶
  https://amrel.bioe.uic.edu/NSFREU2004/Reports2004/Jaime%20Robles_Final%20Report.pdf, accessed in September 2020.
  » https://amrel.bioe.uic.edu/NSFREU2004/Reports2004/Jaime%20Robles_Final%20Report.pdf
• ³⁷
  JIS K 1474: Test Methods for Activated Carbon, Japanese Standards Association: Tokyo, 1992.
• ³⁸
  Wang, Y.; Wang, X. J.; Liu, M.; Wang, X.; Wu, Z.; Yang, L. Z.; Xia, S. Q.; Zhao, J. F.; Ind. Crops Prod. 2012, 39, 81.
• ³⁹
  Alves, M. A. P. M. S.; Silva, S. C.; Silva, S. Y. S.; Pereira Jr., J. B.; Marinho, P. S. B.; Dantas, K. G. F.; da Mota, S. A. P.; Amaral, J. C.; da Silva, M. F. G. F.; Oliveira, M. N.; J. Braz. Chem. Soc. 2020, 31, 574.
• ⁴⁰
  Ho, Y.-S.; J. Hazard. Mater 2006, 136, 681.
• ⁴¹
  Mohammadi, S. Z.; Karimi, M. A.; Afzali, D.; Mansouri, F.; Desalination 2010, 262, 86.
• ⁴²
  Sen Gupta, S.; Bhattacharyya, K. G.; Adv. Colloid Interface Sci. 2011, 162, 39.
• ⁴³
  Karri, R. R.; Jayakumar, N. S.; Sahu, J. N.; J. Mol. Liq . 2017, 231, 249.
• ⁴⁴
  Popescu, C.-M.; Popescu, M.-C.; Singurel, G.; Vasile, C.; Argyropoulos, D.; Willför, S.; Appl. Spectrosc. 2007, 61, 1168.
• ⁴⁵
  Zhang, S.; Ji, Y.; Ao, F.; Wang, Y.; Zhao, J.; Chen, S.; J. Braz. Chem. Soc . 2018, 29, 1487.
• ⁴⁶
  Coates, J. In Encyclopedia of Analytical Chemistry; John Wiley & Sons: Chichester, 2006, DOI: 10.1002/9780470027318.a5606.
  » https://doi.org/10.1002/9780470027318.a5606
• ⁴⁷
  Barbosa, L. C. A.; Espectroscopia no Infravermelho: na Caracterização de Compostos Orgânicos; UFV: Viçosa, 2007.
• ⁴⁸
  Kang, O. L.; Ramli, N.; Said, M.; Ahmad, M.; Yasir, S. M.; Ariff, A.; J. Environ. Sci 2011, 23, 918.
• ⁴⁹
  Pakade, V. E.; Ntuli, T. D.; Ofomaja, A. E.; Appl. Water Sci 2017, 7, 3015.
• ⁵⁰
  Tyagi, U.; Khandegar, V.; J. Hazard., Toxic Radioact. Waste 2018, 22, 04018014.
• ⁵¹
  Vendruscolo, F.; Ferreira, G. L. R.; Antoniosi Filho, N. R.; Int. Biodeterior. Biodegrad 2017, 119, 87.
• ⁵²
  Mahmoud, M. E.; J. Environ. Manage 2015, 147, 264.
• ⁵³
  Pehlivan, E.; Kahraman, H. T.; Food Chem. 2012, 133, 1478.
• ⁵⁴
  Qiu, H.; Lv, L.; Pan, B.-c.; Zhang, Q.-j.; Zhang, W.-m.; Zhang, Q.-x.; J. Zhejiang Univ., Sci., A 2009, 10, 716.
• ⁵⁵
  Figueiredo-Sganderla, J. A.; Prodanov, C. C.; Daroit, D.; Braz. J. Biol. 2010, 70, 1231.
• ⁵⁶
  Wang, Y.; Yang, Q.; Chen, J.; Yang, J.; Zhang, Y.; Chen, Y.; Li, X.; Du, W.; Liang, A.; Ho, S.-H.; Chang, J.-S.; J. Hazard. Mater . 2020, 395, 122658.
• ⁵⁷
  Yuvaraja, G.; Krishnaiah, N.; Subbaiah, M. V.; Krishnaiah, A.; Colloids Surf., B 2014, 114, 75.
• ⁵⁸
  Enniya, I.; Rghioui, L.; Jourani, A.; Sustainable Chem. Pharm. 2018, 7, 9.
• ⁵⁹
  Dehghani, M. H.; Sanaei, D.; Ali, I.; Bhatnagar, A.; J. Mol. Liq . 2016, 215, 671.
• ⁶⁰
  Manzoor, Q.; Sajid, A.; Hussain, T.; Iqbal, M.; Abbas, M.; Nisar, J.; J. Mater. Res. Technol. 2019, 8, 75.
• ⁶¹
  Owalude, S. O.; Tella, A. C.; Beni-Suef Univ. J. Basic Appl. Sci. 2016, 5, 377.
• ⁶²
  Saha, R.; Saha, B.; Desalin. Water Treat. 2014, 52, 1928.
• ⁶³
  Najim, T. S.; Farhan, S. A.; Dadoosh, R. M.; Desalin. Water Treat . 2014, 52, 4810.
• ⁶⁴
  Nasseh, N.; Taghavi, L.; Barikbin, B.; Harifi-Mood, A. R.; J. Water Reuse Desalin 2017, 7, 449.
• ⁶⁵
  Kumar, S.; Narayanasamy, S.; Venkatesh, R. P.; Sep. Sci. Technol. 2019, 54, 2783.

Publication Dates

• Publication in this collection
  01 Feb 2021
• Date of issue
  Feb 2021

History

• Received
  3 June 2020
• Accepted
  30 Sept 2020