Austenitic-ferritic stainless steels containing 0.2% and 0.5% niobium were evaluated with respect to the microstructures, microhardness, pitting potential resistance, electrochemical impedance and wearing tests. Niobium is an alphagenic element and has a great influence on phase transformation of duplex stainless steels. In the present investigation, the samples were annealed at 1050 ºC and aged at 850 ºC to promote the formation of sigma phase. The pitting potential resistance and electrochemical impedance were evaluated in 3.5 % sodium chloride solution. The wear coefficients were calculated by micro-wear tests conducted using a fixed ball machine and aluminum oxide as abrasive. The results show that the niobium content lead to increase on Laves phase formation. This phase, in association with the sigma phase, causes a significant increase in the hardness and wear resistance with a decrease on corrosion resistance of the austenitic-ferritic stainless steels.
duplex stainless steel containing niobium; sigma phase; Laves phase; wear coefficient; pitting potential; charge transfer resistance