Thermodynamic calculations of the Fe-Cr-N System in the region of the Gas Phase Equilibria have been compared with experimental results of maximum nitrogen absorption during nitriding of two Martensitic Stainless Steels (a 6 mm thick sheet of AISI 410S steel and green powder compacts of AISI 434L steel) under N2 atmospheres. The calculations have been performed combining the Fe-Cr-N System description contained in the SGTE Solid Solution Database and the gas phase for the N System contained in the SGTE Substances Database. Results show a rather good agreement for total nitrogen absorption in the steel and nitrogen solubility in austenite in the range of temperatures between 1273 K and 1473 K and in the range of pressures between 0.1 and 0.36 MPa. Calculations show that an appropriate choice of heat treatment parameters can lead to optimal nitrogen absorption in the alloy. It was observed in the calculations that an increased pressure stabilizes CrN at expenses of Cr2N - type nitrides.
nitrogen absorption; high temperature nitriding; martensitic stainless steels