This study aimed to obtain a bifunctional fabric from the point of view of hydrophilicity/hydrophobicity for biomedical applications. To achieve this, both sides of a fabric of polylactic acid (PLA) were subjected to a plasma treatment. While in a side the oxygen was introduced to the other side, simultaneously, was added methane. The plasma treatment was performed at 100 W, 1.8 mbar, during 30 minutes. By Scanning Electron Microscopy (SEM) morphological analysis, it became evident that the fabric side facing the oxygen inlet showed micropittings, while the reverse side had smooth surfaces. Analysis by X-Ray photoelectron spectroscopy (XPS) revealed an increase in the amount of oxygen in the surface of the PLA on both sides of the fabric. The surface function was characterized by measurements of water absorption rate, where it was determined that one fabric side was more hydrophilic than the other side. The results indicated achievement of a bifunctional fabric through orientation of working gases during a plasma treatment.
Key-words:
Plasma treatment; PLA; hydrophilicity; bifunctionality