Cracking susceptibility of aluminum alloys during laser weldingThe influence of laser parameters in welding aluminum alloys was studied in order to reduce hot cracking. The extension of cracks at the welding surface was used as a cracking susceptibility (CS) index. It has been shown that the CS changes with changing welding velocity for binary Al-Cu alloys. In general, the CS index increased until a maximum velocity and then dropped to zero, generating a typical lambda-curve. This curve is due to two different mechanisms: 1) the refinement of porosities with increasing velocity and 2) the changes in the liquid fraction due to decreasing microsegregation with increasing velocities.
weld cracking; cracking susceptibility; aluminum alloys