The influence of laser parameters in welding aluminum alloys was studied in order to reduce hot cracking. The extension of cracks at the welding surface was used as a cracking susceptibility (CS) index. It has been shown that the CS changes with changing welding velocity for binary Al-Cu alloys. In general, the CS index increased until a maximum velocity and then dropped to zero, generating a typical lambda-curve. This curve is due to two different mechanisms: 1) the refinement of porosities with increasing velocity and 2) the changes in the liquid fraction due to decreasing microsegregation with increasing velocities.
weld cracking; cracking susceptibility; aluminum alloys