Ceramic foams were produced from a sludge generated in the aluminum anodizing process by using an industrial polyurethane foam (replication method) with open cell sizes of 10 ± 5 ppi (porosity = 97%) which were impregnated with suspensions containing 50-61 wt.% alumina, 1 wt.% citric acid, 6 wt.% bentonite and fired at 1600 ºC for 2 h. The aluminum anodizing sludge shows a high alumina content (87.5 wt.%) and a low particle size (~1.7 mm) after calcination and milling. The obtained filters show porosity of approximately 70%, filtration capability (mass water flow) of 1.7 kg/s and mechanical strength under compression of 2.40 MPa.
wastes; alumina; ceramic foams