ABSTRACT
Objectives:
The objective was to evaluate the longevity of ceramic restorative materials in the manufacture of endocrown restorations, through an in vitro study on surface roughness and mechanical strength.
Methods:
Three restorative materials were evaluated and assigned to experimental groups (n=10 disc specimens): Leucite Reinforced Ceramic, Lithium Disilicate and Nanoceramic Resin. These restorative materials were evaluated for surface before and after aging (n=02 specimens) under a stereomicroscope. The specimens were submitted to the average surface roughness test (Ra) (n=10) in a contact roughness meter before and after aging. As well as the biaxial flexural strength test (n=10), after aging, up to a test speed of 0.5 mm/min. Aging was carried out in a thermocycler, with 5,000 cycles with baths of 5 °C ± 1 ° and 55 °C ± 1 °. Fragments after fracture were observed under a stereomicroscope. The data obtained were tabulated and analyzed using the Minitab statistical program.
Results:
The surfaces of the specimens do not show changes between the restorative materials and also in relation to aging. For the roughness data, the restorative material factors (p=0.867) and aging (p=0.321) were not statistically significant. The DIS group presented the highest values of fracture resistance (p=0.000), in relation to the LEU and REN groups, which were statistically similar. The same statistical pattern was identified for post-fracture fragment data (p=0.030).
Conclusions:
The aging factors and restorative material do not interfere with the surface roughness performance. However, the mechanical performance and number of fragments after fracture is affected by the restorative material.
Indexing terms
Ceramics; Computer-aided design; Flexural strength