ABSTRACT
Stoichiometric hydroxyapatite is a bioreabsorbable material and has been used for bone repair and shot blasting of titanium implants. However, the stoichiometric hydroxyapatite is not stable above 1130 oC to 1200 oC, limiting the heat treatment performed on the biomaterial to increase the mechanical strength of the granules obtained from the synthesis process at room temperature. Therefore, the aim of this work was the elaboration of calcium phosphate with Ca/P molar ratio of 1.7. With this Ca/P molar ratio, the formation of stable hydroxyapatite is possible up to approximately 1360 oC, according to the CaO-P2O5 equilibrium diagram. Calcium phosphate was prepared by the wet method of synthesis using calcium carbonate and phosphoric acid as raw materials. The material obtained from the synthesis consists of agglomerated particles with a size between 20 nm and 70 nm, while the size of the agglomerates varied from a few microns to approximately 200 µm. The results of the thermal analysis and X-ray diffraction showed that the hydroxyapatite is stable between 750 oC and 1350 oC. The heat treatment performed at 1300 oC confirmed that there is no transformation of hydroxyapatite into tricalcium phosphate above 1130 oC to 1200 oC as it happens for stoichiometric hydroxyapatite. In the heat treatment carried out at 1300 oC for 1 hour, hydroxyapatite was obtained with 67 % of porosity whereas in the treatment of 4 hours at the same temperature the porosity was 17 %. Hydroxyapatite with high porosity has applications in bone repair whereas the more compact hydroxyapatite can be used in the blasting of titanium implants. These applications are discussed in the work.
Keywords
calcium phosphate; hydroxyapatite; bone repair; blasting titanium implants
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail