ABSTRACT
The 304L austenitic stainless steel is susceptible to deformation induced martensitic transformation. This phase transformation depends on the temperature as well as on the mode, rate and level of deformation. In this work the phases and residual stresses of a 304L TRIP steel where martensitic transformation was induced by cold rolling were investigated by X-ray diffraction XRD. The analyses were performed for different sample thicknesses. The results showed that the phase composition and the residual stresses are strongly dependent on sample thickness. All samples showed a compressive residual stress.
Keywords