Introduction:
The Y-TZP zirconia used for prosthetic infrastructure, in some clinical situations, can be exposed to the oral environment. In these situations, a polished surface without changes is extremely important.
Objective:
The aim of this study was to evaluate the mean roughness (Ra) and Vickers hardness of Y-TZP zirconia (Lava™) after simulating ten years of brushing.
Material and method:
Thirty-six Y-TZP bar-shaped specimens (20mm X 4mm X 1.2mm) were divided into three groups: storage in distilled water (DW, n=12, control); brushing with distilled water (BDW, n=12) and brushing with distilled water and fluoride toothpaste (BFT, n=12). Brushing was performed using a brushing machine with a soft-bristled toothbrush, simulating 10 years of brushing (878.400 cycles, 100gf). The mean roughness (Ra in μm) and Vickers hardness (VHN) of all specimens were measured twice: before and after the experimental treatment, in profilometer and microhardness tester (500gf, 30 seconds), respectively. Data were analyzed using the two-way ANOVA test (α = 0.05).
Result:
The interaction between groups was not significant for roughness (p = 0.701) nor for hardness (p = 0.928). The final averages for Ra (μm) were equal to: DW - 0.63; BDW - 0.64; and, BFT - 0.68. The final averages for Vickers hardness (VHN) were: DW - 1301.16; BDW - 1316.60; and, BFT - 1299.58.
Conclusion:
It was concluded that the brushing with distilled or fluoridated toothpaste was not able to change the roughness and hardness of Y-TZP zirconia used in this study.
Hardness; toothbrushing; ceramics